NASA NTRS2005

Conductive Composites Made Less Expensively

The use of electrically conductive composite structures for electrostatic dissipation, electromagnetic interference shielding, and ground return planes could save between 30 and 90 percent of the mass of the structure, in comparison to aluminum. One strategy that has been shown to make conducting composites effectively uses intercalated graphite fiber as the reinforcement. Intercalation--the insertion of guest atoms or molecules between the graphene planes--can lower the electrical resistivity of graphite fibers by as much as a factor of 10, without sacrificing mechanical or thermal properties.

Gaier, James R.↗

NASA NTRS2005

The Effects of Lunar Dust on EVA Systems During the Apollo Missions

Mission documents from the six Apollo missions that landed on the lunar surface have been studied in order to catalog the effects of lunar dust on Extra-Vehicular Activity (EVA) systems, primarily the Apollo surface space suit. It was found that the effects could be sorted into nine categories: vision obscuration, false instrument readings, dust coating and contamination, loss of traction, clogging of mechanisms, abrasion, thermal control problems, seal failures, and inhalation and irritation. Although simple dust mitigation measures were sufficient to mitigate some of the problems (i.e., loss of traction) it was found that these measures were ineffective to mitigate many of the more serious problems (i.e., clogging, abrasion, diminished heat rejection). The severity of the dust problems were consistently underestimated by ground tests, indicating a need to develop better simulation facilities and procedures.

Gaier, James R.↗

NASA NTRS2005

Effect of Architecture on the Resistivity of Carbon Fiber Polymer Composites

The electrical resistivity of carbon fiber laminar composites can be tailored by weave direction, fiber composition, resin composition, applied pressure, and fiber fraction. Although the weave direction was only found to be important in the case of high aspect ratio composites, the other factors were found to influence the resistivity generally. Most intriguing, the resistivity of composites with lamina of different fiber compositions follows a parallel resistor model. This opens the door for higher performance, lower cost composites to be fabricated from these mixed fiber composites.

Gaier, James R.↗

NASA NTRS2004

Ultra High Voltage Propellant Isolators and Insulators for JIMO Ion Thrusters

Within NASA's Project Prometheus, high specific impulse ion thrusters for electric propulsion of spacecraft for the proposed Jupiter Icy Moon Orbiter (JIMO) mission to three of Jupiter's moons: Callisto, Ganymede and Europa will require high voltage operation to meet mission propulsion. The anticipated approx.6,500 volt net ion energy will require electrical insulation and propellant isolation which must exceed that used successfully by the NASA Solar Electric Propulsion Technology Readiness (NSTAR) Deep Space 1 mission thruster by a factor of approx.6. Xenon propellant isolator prototypes that operate at near one atmosphere and prototypes that operate at low pressures (<100 Torr) have been designed and are being tested for suitability to the JIMO mission requirements. Propellant isolators must be durable to Paschen breakdown, sputter contamination, high temperature, and high voltage while operating for factors longer duration than for the Deep Space 1 Mission. Insulators used to mount the thrusters as well as those needed to support the ion optics have also been designed and are under evaluation. Isolator and insulator concepts, design issues, design guidelines, fabrication considerations and performance issues are presented. The objective of the investigation was to identify candidate isolators and insulators that are sufficiently robust to perform durably and reliably during the proposed JIMO mission.

Banks, Bruce A.↗

NASA NTRS2004

Resistivity of Carbon-Carbon Composites Halved

Carbon-carbon composites have become the material of choice for applications requiring strength and stiffness at very high temperatures (above 2000 C). These composites comprise carbon or graphite fibers embedded in a carbonized or graphitized matrix. In some applications, such as shielding sensitive electronics in very high temperature environments, the performance of these materials would be improved by lowering their electrical resistivity. One method to lower the resistivity of the composites is to lower the resistivity of the graphite fibers, and a proven method to accomplish that is intercalation. Intercalation is the insertion of guest atoms or molecules into a host lattice. In this study the host fibers were highly graphitic pitch-based graphite fibers, or vapor-grown carbon fibers (VGCF), and the intercalate was bromine. Intercalation compounds of graphite are generally thought of as being only metastable, but it has been shown that the residual bromine graphite fiber intercalation compound is remarkably stable, resisting decomposition even at temperatures at least as high as 1000 C. The focus of this work was to fabricate composite preforms, determine whether the fibers they were made from were still intercalated with bromine after processing, and determine the effect on composite resistivity. It was not expected that the resistivity would be lowered as dramatically as with graphite polymer composites because the matrix itself would be much more conductive, but it was hoped that the gains would be substantial enough to warrant its use in high-performance applications. In a collaborative effort supporting a Space Act Agreement between the NASA Glenn Research Center and Applied Sciences, Inc. (Cedarville, OH), laminar preforms were fabricated with pristine and bromine-intercalated pitch-based fibers (P100 and P100-Br) and VGCF (Pyro I and Pyro I-Br). The green preforms were carbonized at 1000 C and then heat treated to 3000 C. To determine whether the fibers in the samples were still intercalated after composite fabrication, they were subjected to X-ray diffraction. The composites containing intercalated graphite fibers showed much higher background scatter than that of pristine fibers, indicating the presence of bromine in the samples. More importantly, faint features indicative of intercalation were visible in the diffraction pattern, showing that the fibers were still intercalated.

Gaier, James R.↗

NASA NTRS2002

Physical and Thermal Properties Evaluated of Teflon FEP Retrieved From the Hubble Space Telescope During Three Servicing Missions

Mechanical properties of aluminized Teflon fluorinated ethylene propylene (FEP) thermal control materials on the Hubble Space Telescope (HST) exposed to low Earth orbit for up to 9.7 years have significantly degraded, with extensive cracking occurring on orbit. The NASA Glenn Research Center and the NASA Goddard Space Flight Center have collaborated on analyzing the physical and thermal properties of aluminized FEP (FEP-Al, DuPont) materials retrieved in December 1999 during HST's third servicing mission (SM3A). Comparisons have been made to properties of FEP-Al retrieved during the first and second HST servicing missions, SM1 and SM2, in order to determine degradation processes for FEP on HST.

Dever, Joyce A.↗

NASA NTRS2002

High-Temperature Intercalated Graphite Fiber Conductors Fabricated

Composites of intercalated graphite fibers show promise to significantly reduce the weight of electromagnetic interference shielding in spacecraft and aircraft. Bromine intercalated pitch-based fibers have been among the most heavily studied systems because of their attractive electrical and thermal conductivities and their stability over a wide range of environmental conditions. Previous studies found that the resistivity of bromineintercalated graphite fibers began to increase when the fibers were exposed to temperatures in excess of about 200 C in air for long periods of time. If the temperature was as high as 450 C, the resistivity increased dramatically within a few hours. It remained unclear, however, whether the increase was due to deintercalation of the bromine or to air oxidation of the fibers. Studies were initially directed toward determining the temperature at which bromine would deintercalate from the fibers, and perhaps become a hazard to both personnel and equipment. So the mass of bromine-intercalated graphite fibers was carefully monitored as it was heated in an inert atmosphere, since the fibers are known to oxidize at a lower temperature than they deintercalate. What was found was that the fibers, which are about 18-wt% bromine, did not lose any appreciable mass even at temperatures approaching 1000 C. X-ray diffraction studies showed that there were also no changes in the overall structure of the compound. Resistivity measurements indicated that there is some slight degradation in the electronic structure, in that the resistivity increased by a few percent. Overall, the results show that these materials may be suitable for applications at temperatures at least this high, provided oxygen is excluded. This may enable their use in carbon-ceramic, and perhaps even carbon-carbon composites.

Gaier, James R.↗

NASA NTRS2002

The Electrical and Thermal Conductivity of Woven Pristine and Intercalated Graphite Fiber-Polymer Composites

A series of woven fabric laminar composite plates and narrow strips were fabricated from a variety of pitch-based pristine and bromine intercalated graphite fibers in an attempt to determine the influence of the weave on the electrical and thermal conduction. It was found generally that these materials can be treated as if they are homogeneous plates. The rule of mixtures describes the resistivity of the composite fairly well if it is realized that only the component of the fibers normal to the equipotential surface will conduct current. When the composite is narrow with respect to the fiber weave, however, there is a marked angular dependence of the resistance which was well modeled by assuming that the current follows only along the fibers (and not across them in a transverse direction), and that the contact resistance among the fibers in the composite is negligible. The thermal conductivity of composites made from less conductive fibers more closely followed the rule of mixtures than that of the high conductivity fibers, though this is thought to be an artifact of the measurement technique. Electrical and thermal anisotropy could be induced in a particular region of the structure by weaving together high and low conductivity fibers in different directions, though this must be done throughout all of the layers of the structure as interlaminar conduction precludes having only the top layer carry the anisotropy. The anisotropy in the thermal conductivity is considerably less than either that predicted by the rule of mixtures or the electrical resistivity.

Gaier, James R.↗

NASA NTRS2000

Insights Developed Into the Damage Mechanism of Teflon FEP Thermal Control Material on the Hubble Space Telescope

Metalized Teflon FEP (DuPont; fluorinated ethylene propylene) thermal control material on the Hubble Space Telescope (HST) has been found to degrade in the space environment. Teflon FEP thermal control blankets retrieved during the first servicing mission were found to be embrittled on solar-facing surfaces and to contain microscopic cracks (the FEP surface is exposed to the space environment). During the second servicing mission, astronauts noticed that the FEP outer layer of the multilayer insulation blanketing covering the telescope was cracked in many locations. Large cracks were observed on the light shield, forward shell, and equipment bays. A tightly curled piece of cracked FEP from the light shield was retrieved during the second mission. This piece was severely embrittled, as witnessed by ground testing. A Failure Review Board was organized by NASA Goddard Space Flight Center to determine the mechanism causing the multilayer insulation degradation. This board included members of the Electro-Physics Branch of the NASA Glenn Research Center at Lewis Field. Density measurements of the retrieved materials obtained under the review board's investigations indicated that FEP from the first servicing mission was essentially unchanged from pristine FEP but that the second servicing mission FEP had increased in density in comparison to pristine FEP (ref. 1). The results were consistent with crystallinity measurements taken using x-ray diffraction and with results from solid-state nuclear magnetic resonance tests (see the table and ref. 1). Because the second servicing mission FEP was embrittled and its density and crystallinity had increased in comparison to pristine FEP, board researchers expected that the first servicing mission FEP, which was also embrittled, would also have increased in crystallinity and density, but it did not. Because the retrieved second servicing mission material curled while in space, it experienced a higher temperature extreme during thermal cycling (estimated at 200 C) than the first servicing mission material (estimated at 50 C). Therefore, Glenn initiated and conducted an investigation of the effects of heating pristine FEP and FEP that had been exposed on the Hubble Space Telescope. Samples of pristine and first and second servicing mission FEP were heated to 200 C and evaluated for changes in density and morphology. We hoped that the results would help explain why FEP degrades in the Hubble Space Telescope space environment.

deGroh, Kim K.↗

NASA NTRS1999

Effects of Heating on Teflon(Registered Trademark) FEP Thermal Control Material from the Hubble Space Telescope

Metallized Teflon(Registered Trademark) FEP (fluorinated ethylene propylene) thermal control material on the Hubble Space Telescope (HST) is degrading in the space environment. Teflon(Registered Trademark) FEP thermal control blankets (space-facing FEP) retrieved during the first servicing mission (SM1) were found to be embrittled on solar facing surfaces and contained microscopic cracks. During the second servicing mission (SM2) astronauts noticed that the FEP outer layer of the multi-layer insulation (MLI) covering the telescope was cracked in many locations around the telescope. Large cracks were observed on the light shield, forward shell and equipment bays. A tightly curled piece of cracked FEP from the light shield was retrieved during SM2 and was severely embrittled, as witnessed by ground testing. A Failure Review Board (FRB) was organized to determine the mechanism causing the MLI degradation. Density, x-ray crystallinity and solid state nuclear magnetic resonance (NMR) analyses of FEP retrieved during SM1 were inconsistent with results of FEP retrieved during SM2. Because the retrieved SM2 material curled while in space, it experienced a higher temperature extreme during thermal cycling, estimated at 200 C, than the SM1 material, estimated at 50 C. An investigation on the effects of heating pristine and FEP exposed on HST was therefore conducted. Samples of pristine. SM1, and SM2 FEP were heated to 200 C and evaluated for changes in density and morphology. Elevated temperature exposure was found to have a major impact on the density of the retrieved materials. Characterization of polymer morphology of as-received and heated FEP samples by NMR provided results that were consistent with the density results. These findings have provided insight to the damage mechanisms of FEP in the space environment.

deGroh, Kim↗

NASA NTRS1999

New Materials for EMI Shielding

Graphite fibers intercalated with bromine or similar mixed halogen compounds have substantially lower resistivity than their pristine counterparts, and thus should exhibit higher shielding effectiveness against electromagnetic interference. The mechanical and thermal properties are nearly unaffected, and the shielding of high energy x-rays and gamma rays is substantially increased. Characterization of the resistivity of the composite materials is subtle, but it is clear that the composite resistivity is substantially lowered. Shielding effectiveness calculations utilizing a simple rule of mixtures model yields results that are consistent with available data on these materials.

Gaier, James R.↗

NASA NTRS1999

Highly Conducting Graphite Epoxy Composite Demonstrated

Weight savings as high as 80 percent could be achieved if graphite polymer composites could replace aluminum in structures such as electromagnetic interference shielding covers and grounding planes. This could result in significant cost savings, especially for the mobile electronics found in spacecraft, aircraft, automobiles, and hand-held consumer electronics. However, such composites had not yet been fabricated with conductivity sufficient to enable these applications. To address this lack, a partnership of the NASA Lewis Research Center, Manchester College, and Applied Sciences, Inc., fabricated nonmetallic composites with unprecedented electrical conductivity. For these composites, heat-treated, vapor-grown graphite fibers were selected which have a resistivity of about 80 mW-cm, more than 20 times more conductive than typical carbon fibers. These fibers were then intercalated with iodine bromide (IBr). Intercalation is the insertion of guest atoms or molecules between the carbon planes of the graphite fibers. Since the carbon planes are not highly distorted in the process, intercalation has little effect on mechanical and thermal properties. Intercalation does, however, lower the carbon fiber resistivity to less than 10 mW-cm, which is comparable to that of metal fibers. Scaleup of the reaction was required since the initial intercalation experiments would be carried out on 20-mg quantities of fibers, and tens of grams of intercalated fibers would be needed to fabricate even small demonstration composites. The reaction was first optimized through a time and temperature study that yielded fibers with a resistivity of 8.7 2 mW-cm when exposed to IBr vapor at 114 C for 24 hours. Stability studies indicated that the intercalated fibers rapidly lost their conductivity when exposed to temperatures as low as 40 C in air. They were not, however, susceptible to degradation by water vapor in the manner of most graphite intercalation compounds. The 1000-fold scaleup experiments concluded that 114 C was near the optimum temperature, but that the intercalation time needed to be lengthened by a factor of 3.

Gaier, James R.↗

NASA NTRS1999

Synchrotron Vacuum Ultraviolet Light and Soft X-Ray Radiation Effects on Aluminized Teflon FEP Investigated

Since the Hubble Space Telescope (HST) was deployed in low Earth orbit in April 1990, two servicing missions have been conducted to upgrade its scientific capabilities. Minor cracking of second-surface metalized Teflon FEP (DuPont; fluorinated ethylene propylene) surfaces from multilayer insulation (MLI) was first observed upon close examination of samples with high solar exposure retrieved during the first servicing mission, which was conducted 3.6 years after deployment. During the second HST servicing mission, 6.8 years after deployment, astronaut observations and photographic documentation revealed significant cracks in the Teflon FEP layer of the MLI on both the solar- and anti-solar-facing surfaces of the telescope. NASA Goddard Space Flight Center directed the efforts of the Hubble Space Telescope MLI Failure Review Board, whose goals included identifying the low-Earth-orbit environmental constituent(s) responsible for the cracking and embrittling of Teflon FEP which was observed during the second servicing mission. The NASA Lewis Research Center provided significant support to this effort. Because soft x-ray radiation from solar flares had been considered as a possible cause for the degradation of the mechanical properties of Teflon FEP (ref. 1), the effects of soft xray radiation and vacuum ultraviolet light on Teflon FEP were investigated. In this Lewisled effort, samples of Teflon FEP with a 100-nm layer of vapor-deposited aluminum (VDA) on the backside were exposed to synchrotron radiation of various vacuum ultraviolet and soft x-ray wavelengths between 18 nm (69 eV) and 0.65 nm (1900 eV). Synchrotron radiation exposures were conducted using the National Synchrotron Light Source at Brookhaven National Laboratory. Samples of FEP/VDA were exposed with the FEP surface facing the synchrotron beam. Doses and fluences were compared with those estimated for the 20-yr Hubble Space Telescope mission.

Dever, Joyce A.↗

NASA NTRS1999

Effect of X-Rays on the Mechanical Properties of Aluminized FEP Teflon(trademark)

Pieces of the multilayer insulation (MLI) that is integral to the thermal control of the Hubble Space Telescope (HST) have been returned by two servicing missions after 3.6 and 6.8 years in orbit. They reveal that the outer layer, which is made from 5 mil (0.13 mm) thick aluminized fluorinated ethylenepropylene (FEP) Teflon. has become severely embrittled. Although possible agents of this embrittlement include electromagnetic radiation across the entire solar spectrum, trapped particle radiation, atomic oxygen, and thermal cycling, intensive investigations have not yielded unambiguous causes. Previous studies utilizing monoenergetic photons in the 69-1900 eV range did not cause significant embrittlement, even at much higher doses than were experienced by the HST MLI. Neither did x-rays in the 3 to 10 keV range generated in a modified electron bean evaporator. An antidotal aluminized FEP sample that was exposed to an intensive dose from unfiltered Mo x-ray radiation from a rotating anode generator, however, did show the requisite embrittlement. Thus, a study was undertaken to determine the effects of x-ray exposure on the embrittlement of aluminized FEP in hopes that it might elucidate the HST MLI degradation mechanism. Tensile specimens of aluminized 5 mil thick FEP were exposed to a constant fluence of unfiltered x-ray radiation from a Mo target whose maximum energy ranged from 20-60 kV. Other samples were annealed, thermally cycled (100x) between 77-333 K, or cycled and irradiated. Tensile tests and density measurements were then performed on the samples. Only the samples which had been irradiated had the drastically reduced elongation-to-break, characteristic of the HST samples. Thermal cycling may accelerate the embrittlement, but the effect was near the scatter in the measurements. Annealing and thermal cycling had no apparent effect. Only the samples which had been irradiated and annealed showed significant density increases, likely implicating polymer chain scission and annealing.

Gaier, James R.↗

NASA NTRS1998

Synchrontron VUV and Soft X-Ray Radiation Effects on Aluminized Teflon FEP

Surfaces of the aluminized Teflon FEP multi-layer thermal insulation on the Hubble Space Telescope (HST) were found to be cracked and curled in some areas at the time of the second servicing, mission in February 1997, 6.8 years after HST was deployed in low Earth orbit (LEO). As part of a test program to assess environmental conditions which would produce embrittlement sufficient to cause cracking of Teflon on HST, samples of Teflon FEP with a backside layer of vapor deposited aluminum were exposed to vacuum ultraviolet (VUV) and soft x-ray radiation of various energies using facilities at the National Synchrotron Light Source. Brookhaven National Laboratory. Samples were exposed to synchrotron radiation of narrow energy bands centered on energies between 69 eV and 1900 eV. Samples were analyzed for ultimate tensile strength and elongation. Results will be compared to those of aluminized Teflon FEP retrieved from HST after 3.6 years and 6.8 years on orbit and will he referenced to estimated HST mission doses of VUV and soft x-ray radiation.

Dever, Joyce A.↗

NASA NTRS1998

Fabrication and Resistivity of IBr Intercalated Vapor-Grown Carbon Fiber Composites

Composites using vapor-crown carbon fibers (VGCF), the most conductive of the carbon fiber types, are attractive for applications where low density, high strength, and at least moderate conductivity are required, such as electromagnetic interference shielding covers for spacecraft. The conductivity can be enhanced another order of magnitude by intercalation of the VGCF. If a high Z intercalate is used, the protection of components from ionizing radiation can be enhanced also. Thus, the intercalation of VGCF with IBr is reported. Since composite testing is required to verify properties, the intercalation reaction optimization, stability of the intercalation compound, scale-up of the intercalation reaction, composite fabrication, and resistivity of the resulting composites is also reported. The optimum conditions for low resistivity and uniformity for the scaled up reaction (20-30 g of product) were 114 C for at least 72 hr, yielding a fiber with a resistivity of 8.7+/-2 micro-Omega-cm. The thermal stability of these fibers was poor, with degradation occurring at temperatures as low as 40 C in air, though they were insensitive to water vapor. Composite resistivity was 20-30 micro-Omega-cm, as measured by contactless conductivity measurements, about a factor of five higher than would be expected from a simple rule of mixtures. The addition of 1.0 percent Br2, intercalated microfibers increased the resistivity of the composites by more than 20 percent.

Gaier, James R.↗

NASA NTRS1998

Effect of X-Rays on the Mechanical Properties of Aluminized FEP Teflon(R)

Pieces of the multilayer insulation (MLI) that is integral to the thermal control of the Hubble Space Telescope (HST) have been returned by two servicing missions after 3.6 and 6.8 years in orbit. They reveal that the outer layer, which is made from 5 mil (0.13 mm)thick aluminized fluorinated ethylene propylene(FEP) Teflon(R), has become severely embrittled. Although possible agents of this embrittlement include electromagnetic radiation across the entire solar spectrum, trapped particle radiation, atomic oxygen, and thermal cycling, intensive investigations have not yielded unambiguous causes. Previous studies utilizing monoenergetic photons in the 69-1900 eV range did not cause significant embrittlement, even at much higher doses than were experienced by the HST MLI. Neither did x-rays in the 3 to 10 keV range generated in a modified electron beam evaporator. An antidotal aluminized FEP sample that was exposed to an intensive dose from unfiltered Mo x-ray radiation from a rotating anode generator, however, did show the requisite embrittlement. Thus, a study was undertaken to determine the effects of x-ray exposure on the embrittlement of aluminized FEP in hopes that it might elucidate the HST MLI degradation mechanism. Tensile specimens of aluminized 5 mil thick FEP were exposed to a constant fluence of unfiltered x-ray radiation from a Mo target whose maximum energy ranged from 20-60 kV. Other samples were annealed, thermally cycled (100x) between 77-333 K, or cycled and irradiated. Tensile tests and density measurements were then performed on the samples. Only the samples which had been irradiated had the drastically reduced elongation-to-break, characteristic of the HST samples. Thermal cycling may accelerate the embrittlement, but the effect was near the scatter in the measurements. Annealing and thermal cycling had no apparent effect. Only the samples which had been irradiated and annealed showed significant density increases, likely implicating polymer chain scission and annealing.

Gaier, James R.↗

NASA NTRS1997

New Electromagnetic Interference Shielding Material Demonstrated

A demonstration electromagnetic interference (EMI) shielding cover that has a potential mass savings in excess of 80 percent over conventional aluminum has been fabricated and tested. It was the culmination of a 3-yr effort involving Hughes Space and Communications (Los Angeles), Applied Sciences, Inc. (Cedarville, Ohio), and the NASA Lewis Research Center. The cover was fabricated from a composite of polycyanate ester resin and graphite fibers that had been chemically modified by intercalation to enhance their electrical conductivity.

Gaier, James R.↗