NASA NTRS1987

Design Criteria for Controlling Stress Corrosion Cracking

This document sets forth the criteria to be used in the selection of materials for space vehicles and associated equipment and facilities so that failure resulting from stress corrosion will be prevented. The requirements established herein apply to all metallic components proposed for use in space vehicles and other flight hardware, ground support equipment, and facilities for testing. These requirements are applicable not only to items designed and fabricated by MSFC (Marshall Space Flight Center) and its prime contractors, but also to items supplied to the prime contractor by subcontractors and vendors.

Franklin, D. B.↗
NASA NTRS1981

Corrosion fatigue of Inconel 718 and Incoloy 903

Corrosion fatigue tests were conducted on Inconel 718 and Incoloy 903 in distilled water, 500 ppm NaCl, and 3.5% NaCl. Results were compared to the endurance limit in air. For Inconel 718, the corrosion fatigue strength (CFS) IN 3.5% NaCl WAS 328 MPa or 75 percent of the endurance limit. For Incoloy 903, the CFS ranged from 234 MPa in distilled water (68 percent of the endurance limit) to 103 MPa in 3.5% NaCl (30 percent of the endurance limit). Results indicate that, for components which have limited fatigue life, an evaluation of the combined effects of fatigue and the corrosive atmosphere must be considered in projecting useful lifetimes.

Franklin, D. B.↗
NASA NTRS1977

Evaluation and control of environmental corrosion for aluminum and steel alloys

Corrosion protection systems for aerospace application and the effects of surface treatments and methods of controlling stress corrosion are evaluated. Chromate pigmented systems were found to be most effective for aluminum alloys; zinc-rich coatings gave the greatest protection to steel alloys. Various steel and aluminum alloys are rated for stress corrosion resistance.