High Purity and Reduced Defects Hard Carbon Synthesis for Sodium-Ion Batteries
Hard carbon (HC) is the state-of-the-art anode material for sodium-ion batteries; however, the high-temperature carbonization of precursors (>1100 °C) often introduces inorganic impurities, an issue that remains largely underexplored. Here, we report a simple synthesis strategy for producing high purity HC by carbonizing a cellulose-derived precursor at 1400 °C under a slightly reducing Ar–H2 atmosphere on a graphite substrate, thereby eliminating the aluminum contamination observed during conventional carbonization on an alumina substrate under Ar. In addition, the modified synthetic condition reduces surface defects and the concentration of oxygen-containing functional groups, thereby altering the interphase formation on the HC surface. At a current density of 20 mA g−1, the impurity-rich HC exhibited an initial coulombic efficiency (ICE) of 74.1% and a reversible capacity of 248.8 mAh g−1. In sharp contrast, the high purity HC delivered a significantly improved ICE of 90.1% and a reversible capacity of 345.1 mAh g−1. These results underscore the critical importance of impurity and defect control during HC synthesis and highlight the clear electrochemical advantages of high purity HC with reduced defects for sodium-ion battery anodes.