NASA NTRS1988

Aromatic cyclotriphosphazenes

Four-Aminophenoxy cyclotriphosphazenes are reacted with maleic anhydride to produce maleamic acids which are converted to the maleimides. The maleimides are polymerized. By selection of starting materials (e.g., hexakis amino or trisaminophenoxy trisphenoxy cyclotrisphosphazenes), selection of molar porportions of reactants, use of mixtures of anhydrides and use of dianhydrides as bridging groups a variety of maleimides and polymers are produced. The polymers have high limiting oxygen indices, high char yields and other useful heat and fire resistant properties making them useful as, for example, impregnants of fabrics.

Kamar, Devendra↗

NASA NTRS1988

Stronger Fire-Resistant Epoxies

New curing agent improves mechanical properties and works at lower temperature. Use of aminophenoxycyclotriphosphazene curing agents yields stronger, more heat- and fire-resistant epoxy resins. Used with solvent if necessary for coating fabrics or casting films.

Fohlen, George M.↗

NASA NTRS1987

Process for preparing phthalocyanine polymer from imide containing bisphthalonitrile

Imide-linked bisphthalonitrile compounds are prepared by combining a dicyano aromatic diamine and an organic dianhydride to produce an amic acid linked bisphthalonitrile compound. The amic acid linked bisphthalonitrile compound is dehydrocyclized to produce the imide-linked bisphthalonitrile compounds. The imide-linked bisphthalonitrile compounds may be polymerized to produce a phythalocyanine polymer by heating the imide-linked bisphthalonitrile compound, either alone or in the presence of a metal powder or a metal salt. These compounds are useful in the coating, laminating and molding arts. The polymers are useful in composite matrix resins where increased fire resistance, toughness and resistance to moisture are required, particularly as secondary structures in aircraft and spacecraft.

Achar, Bappalige N.↗

NASA NTRS1987

Fire and heat resistant laminating resins based on maleimido substituted aromatic cyclotriphosphazene polymer

4-Aminophenoxy cyclotriphosphazenes are reacted with maleic anhydride to produce maleamic acids which are converted to the maleimides. The maleimides are polymerized. By selection of starting materials (e.g., hexakis amino or trisaminophenoxy trisphenoxy cyclotriphosphazenes), selection of molar proportions of reactants, use of mixtures of anhydrides and use of dianhydrides as bridging groups a variety of maleimides and polymers are produced. The polymers have high limiting oxygen indices, high char yields and other useful heat and fire resistant properties making them useful as, for example, impregnants of fabrics.

Kumar, Devendra↗

NASA NTRS1977

Aminophenoxycyclotriphosphazene cured epoxy resins and the composites, laminates, adhesives and structures thereof

Aminophenoxy cyclotriphosphazenes such as hexakis (4-aminophenoxy) cyclotriphosphazene and tris (4-aminophenoxy)-tris phenoxy cyclotriphosphazene are used as curing agents for epoxy resins. These 1,2-epoxy resins are selected from di- or polyepoxide containing organic moieties of the formula (CH2-CHO-CH2) m-W-R-W- (CH2CH-CH2O)m where R is diphenyl dimethylmethane, diphenylmethane; W is a nitrogen or oxygen atom; and m is 1 when W is oxygen and 2 when W is nitrogen. The resins are cured thermally in stages at between about 110 to 135 C for between about 1 and 10 min, then at between about 175 to 185 C for between 0.5 to 10 hr and post cured at between about 215 and 235 C for between 0.1 and 2 hr. These resins are useful for making fire resistant elevated temperature stable composites, laminates, molded parts, and adhesives and structures, usually for aircraft secondary structures and for spacecraft construction.

Kumar, Devendra↗