NASA NTRS1992

Melting of the Abrikosov flux lattice in anisotropic superconductors

It has been proposed that the Abrikosov flux lattice in high-Tc superconductors is melted over a significant fraction of the phase diagram. A thermodynamic argument is provided which establishes that the angular dependence of the melting temperature is controlled by the superconducting mass anisotropy. Using a low-frequency torsional-oscillator technique, this relationship has been tested in untwinned single-crystal YBa2Cu3O(7-delta). The results offer decisive support for the melting proposal.

Beck, R. G.↗
NASA NTRS1992

Glass-Derived Superconductive Ceramic

Critical superconducting-transition temperature of 107.2 K observed in specimen made by annealing glass of composition Bi1.5Pb0.5Sr2Ca2Cu3Ox for 243 h at 840 degrees C. PbO found to lower melting temperature and viscosity of glass, possibly by acting as fluxing agent. Suggested partial substitution of lead into bismuth oxide planes of crystalline phase having Tc of 110 K stabilizes this phase and facilitates formation of it.

Bansal, Narottam P.↗
NASA NTRS1991

Experimental evidence for flux-lattice melting

A low-frequency torsional oscillator has been used to search for flux-lattice melting in an untwinned single crystal of YBa2Cu3O(7-delta). The damping of the oscillator was measured as a function of temperature, for applied magnetic fields in the range H = 0.1-2.3 T. A remarkably sharp damping peak has been located. It is suggested that the temperature of the peak corresponds to the melting point of the Abrikosov flux lattice.

Farrell, D. E.↗
NASA NTRS1990

Experimental evidence of a dimensional crossover in Y1Ba2Cu3O(7-delta)

High-resolution torque-magnetometry data have been obtained on an untwinned single crystal of Y1Ba2Cu3O(7-delta) in the temperature range 63-88 K (Tc = 90.5 K). At T = 80 K and above, the data are fitted extremely well with the accepted three-dimensional phenomenological theory, but below this temperature an anomalous torque develops when the magnetic field lies close to the Cu-O planes. The qualitative and quantitative features of these results provide strong evidence that breakdown of the three-dimensional description below 80 K is associated with a crossover to two-dimensional superconducting behavior.

Farrell, D. E.↗
NASA NTRS1989

Glass-derived superconducting ceramics with zero resistance at 107 K in the Bi(1.5)Pb(0.5)Sr2Ca2Cu3O(x) system

A melt of composition Bi(1.5)Pb(0.5)Sr2Ca2Cu3O(x) was fast quenched to form a glass. This was subsequently air annealed and the influence of annealing time and temperature on the formation of various crystalline phases was investigated. X-ray powder diffraction indicate that none of the resulting samples were single phase. However, for an annealing temperature of 840 C, the volume fraction of the high Tc phase (isostructural with Bi2Sr2Ca2Cu3O10) increased with annealing time. A specimen annealed at this temperature for 243 h followed by slow cooling showed a sharp transition and Tc (R = 0) = 107.2 K.

Bansal, Narottam P.↗
NASA NTRS1989

Screen-Printed YBa2Cu3O7-x Films On Alumina

Superconducting films made in relatively simple process. Thick films of YBa2Cu3O7-x superconductor deposited on highly-polished alumina substrates by screen printing. In addition to simplicity, screen-printing technique offers advantage that patterns for electronic and microwave circuits and devices printed directly, without additional etching steps.

Bansal, Narottam P.↗
NASA NTRS1989

Synthesis and characterization of high-Tc superconductors in the Tl-Ca-Ba-Cu-O system

Both Tl2Ca2Ba2Cu3O10 and TlCa3BaCu3O8.5 are investigated for superconductivity as a function of the sintering temperature, time, atmosphere, and quench rate in an effort to synthesize the high-Tc superconducting phase in the thallium system. The samples are characterized by electrical resistivity measurements, X-ray diffraction, and scanning electron microscopy. Samples of starting composition Tl2Ca2Ba2Cu3O10 fired in air at 860-900 C and rapidly quenched show a Tc of 96-107 K. In contrast, specimens of starting composition TlCa3BaCu3O8.5 when baked at 900 C and slowly cooled in oxygen superconduct at 116 K and above and consist of Tl2Ca2Ba2Cu3O(10+x) as the dominant phase. The results also show that, in contrast to the case of YBa2Cu3O(7-x), doping with a small concentration of fluorine sharpens the resistive transition and produces a large Tc increase in thallium-based superconductors.

Bansal, Narottam P.↗
NASA NTRS1989

Critical currents of aligned grains of Tl-Ba-Ca-Cu-O compounds

A study of irreversibility in the magnetization curves of Tl2Ba2Ca2Cu3O10 and Tl2Ba2Ca1Cu2O8 was undertaken to determine the intragranular critical currents and the effects of flux-creep in grain-aligned samples of these materials. For fields of greater than 0.3 T, and H parallel to c axis, the critical supercurrent falls approximately exponentially with both magnetic field and temperature. Flux-creep is found to be linear in the logarithm of time at low fields over a wide temperature range.

Fang, M. M.↗
NASA NTRS1989

Free energy surfaces in the superconducting mixed state

The free energy surface for Tl2Ba2Ca2Cu3O1O has been measured as a function of temperature and magnetic field to determine the fundamental thermodynamic properties of the mixed state. The change in free energy, G(H)-G(O), is found to be linear in temperature over a wide range indicating that the specific heat is independent of field.

Finnemore, D. K.↗
NASA NTRS1988

Doping directed at the oxygen sites in Y1Ba2Cu3O(7-delta) - The effect of sulfur, fluorine, and chlorine

The effect of three dopants directed at the oxygen sites in Y1Ba2Cu3O(7-delta) have been investigated: sulfur, fluorine, and chlorine. Single-phase material has been obtained up to a (nominal) replacement of about 1 percent of the oxygen. Although the lattice parameters are unchanged, all dopants raise Tc (very slightly), sharpen the resistive transition, reduce the normal state resistivity, and very substantially increase the (magnetically determined) fraction of the material that is superconducting. All of these results differ qualitatively from those obtained with dopants directed at other locations in the 123 structure, and it is suggested that small additions of sulfur, fluorine, or chlorine may help to stabilize the ideal 123 stoichiometry.

Bansal, N. P.↗
NASA NTRS1988

High Tc screen-printed YBa2Cu3O(7-x) films - Effect of the substrate material

Thick films of YBa2Cu3O(7-x) have been deposited on highly polished alumina, magnesia spinel, nickel aluminum titanate (Ni-Al-Ti), and barium tetratitanate (Ba-Ti) substrates by the screen printing technique. Properties of the films were found to be highly sensitive to the choice of the substrate material. The film on Ba-Ti turned green after firing, due to a reaction with the substrate and were insulating. A film on Ni-Al-Ti had a Tc (onset) of about 95 K and lost 90 percent of its resistance by about 75 K. However, even at 4 K it was not fully superconducting, possibly due to a reaction between the film and the substrate and interdiffusion of the reaction products. The film on alumina had Tc (onset) of about 96 K, Tc (zero) of about 66 K, and Delta Tc of about 10 K. The best film was obtained on spinel and had Tc (onset) of about 94 K, zero resistance at 81 K, and a transition width of about 7 K.

Bansal, Narottam P.↗
NASA NTRS1988

Effect of fluoride doping on the transition temperature of YBa2Cu3O(6.5+delta)

The effects of F content on the Tc of superconducting YBa2Cu3F(x)O(6.5+delta-0.5x) (x = 0.0165-1.65) prepared by the solid-state reaction method (Bandsahl and Sandkuhl, 1988) are investigated experimentally. The results are presented in tables and graphs and characterized. Tc is found to increase steadily from 90.8 to 93.4 K as x is increased from 0.0165 to 0.066, but to decrease as x is further increased (Tc = 90.3 K at x = 1.65). The structure of the samples with x = 0.066 or lower is found to be single-phase perovskite.

Bansal, Narottam P.↗
NASA NTRS1988

Synthesis and characterization of high-T(sub c) screen-printed Y-Ba-Cu-O films on alumina

Thick films of YBa2Cu3O(sub 7-x) have been deposited on highly polished alumina substrates by the screen printing technique. To optimize the post-printing heat treatment, the films were baked at various temperatures for different lengths of time and oxygen-annealed at a lower temperature. The resulting films were characterized by electrical resistivity measurements, x-ray diffraction, and optical and scanning electron microscopy. Properties of the films were found to be highly sensitive to the post-printing thermal treatment. Films baked for 15 min at 1000 C in oxygen were hard, adherent, near single phase, and superconducting with T(sub c)(onset) approx 96 K, T(sub c)(zero) approx 66 K and Delta T sub c (10 to 90 percent) approx 10 K.

Bansal, Narottam P.↗
NASA NTRS1988

Synthesis and characterization of high-T(c) screen-printed Y-Ba-Cu-O films on alumina

Thick films of YBa2Cu3O(sub 7-x) have been deposited on highly polished alumina substrates by the screen printing technique. To optimize the post-printing heat treatment, the films were baked at various temperatures for different lengths of time and oxygen-annealed at a lower temperature. The resulting films were characterized by electrical resistivity measurements, X-ray diffraction, and optical and scanning electron microscopy. Properties of the films were found to be highly sensitive to the post-printing thermal treatment. Films baked for 15 min at 1000 C in oxygen were hard, adherent, near single phase, and superconducting with T(sub c) (onset) approx 96 KK, T(sub c) (zero) approx 66 K and Delta T sub c (10 to 90 percent) approx 10 K.

Bansal, Narottam P.↗
NASA NTRS1987

Weak-field magnetization of superconducting Y1Ba2Cu3O(x) - Relationship to microstructure

The granular magnetization model of Finnemore et al. (1987) has been tested on a well-characterized sample of Y1Ba2Cu3Ox. The temperature dependence of the magnetic susceptibility is in excellent agreement with the model. In addition, the grain size deduced from the magnetization data (1-2 microns) is in reasonable agreement with direct scanning-electron-microscopy measurements of the microstructure.

Farrell, D. E.↗