Controlling microstructure and B2 ordering kinetics in Fe–Al system through additive manufacturing

Multi-material fabrication between steel and aluminum is challenging because of the formation of several intermetallic phases. Embrittling B2 ordered intermetallics form in the steel rich side and are stable till about 60% of Al dilution in steel. In this work by using multi-length scale characterization coupled with integrated computational process and thermokinetic modeling, we show that the ordered B2 intermetallics in the steel rich side of the Fe–Al system forms via a nucleation and growth mechanism. The extent of B2 ordered intermetallics can be controlled by modifying the directed energy deposition-additive manufacturing (DED-AM) process parameters. Our findings lay the foundation for enabling fabrication of crack-free functionally graded compositions between the two alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Reduction kinetics of hematite powder using argon/hydrogen plasma with prospects for near net shaping of sustainable iron

Direct reduction of iron ore using hydrogen plasma is being explored as a potential solution to decarbonize the iron and steel sector. The current state-of-the-art demonstrated reduction of hematite pellets via hydrogen plasma using Ar + 10% H 2 but had slow reduction kinetics, requiring 30 minutes of plasma exposure for complete reduction. Here we show that using hematite in a powder form, easily obtainable from beneficiated ore, results in 10× faster kinetics using plasma generated from Ar + 2% H 2 shielding gas compared to the current state-of-the art. Additionally, the increased kinetics using powders and a dilute hydrogen concentration can enable the use of advanced manufacturing techniques like blown powder directed energy deposition using a plasma tungsten arc welding torch to manufacture near net shape components directly from the ore concentrates. This ore to part approach will also reduce the emissions associated with downstream processes like rolling, forging, and machining, thereby further aiding in the sectorial decarbonization efforts.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Additively Manufacturing Nitinol Shape Memory Alloys for Advanced Actuator Designs

The objective of this research was to understand the role of feedstock production in the phase transformation behavior of additively manufactured Ni-Ti alloys for advanced actuator design. Industrial adoption of additively manufactured Ni-Ti alloys depends on the ability to produce repeatable phase transformation behavior, quantified here by the austenite to martensite transformation on heating. Small variations in the alloy composition may have a significant effect on the temperature at which this transformation occurs. This project showed that the powder characteristics play an important role in determining this behavior. Increases in the surface area per unit volume of the powder, either as a function of size distribution or morphology, have the effect of reducing the Ti content in the alloy through the formation of Ti-rich oxides on the powder surface, which has the effect of depressing the transformation temperature. Preferential Ni vaporization during additive manufacturing can partially offset this effect. To achieve repeatable results, it is important to understand the effect of powder oxidation, and to control the powder characteristics.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Heterogeneous phase transformation pathways in additively manufactured Al-Ce-Mn alloys

Heat treatment of additively manufactured Al-Ce based multicomponent alloys leads to complex microstructure evolution. In this research, the ability to extend the phase transformation theories involving nucleation of a product phase from a heterogeneous multi-phase microstructure typical to that of additively manufactured samples is explored. The Al-10Ce-8Mn (wt%) was used as a model alloy system. Under additive manufacturing conditions different solidification microstructures were obtained due to spatial and temporal variations of thermal gradients (G) and liquid-solid interface velocities (R) within a given melt pool. Near the melt pool boundary (high G and low R, referred as MPB region), initially, Al 20 Mn 2 Ce forms from the liquid followed by a eutectic of FCC Al and Al 11 Ce 3 . In the melt pool interiors (low G and high R referred as ES region) a eutectic structure between FCC Al and Al 20 Mn 2 Ce is observed. During subsequent heat treatments, the MPB and ES regions transform into different sets of microstructures. In the MPB region, a fine globular microstructure containing FCC Al, Al 11 Ce 3 , Al 6 Mn, and Al 12 Mn results from the decomposition of Al 20 Mn 2 Ce. In the ES region a faceted Al 51 Mn 7 Ce 4 plate phase results from the decomposition of Al 20 Mn 2 Ce. The formation of the Al 51 Mn 7 Ce 4 phase within the eutectic microstructure at the boundaries of FCC Al and Al 20 Mn 2 Ce has not been reported in the literature. Further, these two distinct phase transformation pathways are rationalized based on the role of driving force on the nucleation of (Al 6 Mn) and/or metastable intermetallic (Al 51 Mn 7 Ce 4 ) phases at the interface of aluminum (FCC) and the non-equilibrium intermetallic (Al 20 Mn 2 Ce) phases.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Role of scan strategies and heat treatment on grain structure evolution in Fe-Si soft magnetic alloys made by laser-powder bed fusion

A major goal in printing soft magnetic Fe-Si steels using additive manufacturing is to take advantage of the potential for complex geometric designs and site-specific grain control. One major step in the processing of these alloys is understanding how processing parameters might impact how the as-built microstructure responds to annealing (i.e. the annealing response). The impact of scan strategy on the annealing response for thin wall geometries is specifically explored. Two scan strategies were explored for a thin wall geometry that produced a strongly columnar grain structure and equiaxed grain structure. Additionally, samples from both scan strategies annealed at 1200 °C showed a marked difference in annealing response with the more equiaxed sample seeing full recrystallization and grain growth, while the more columnar grain structure saw little change in microstructure. After analysis through characterization techniques and thermal-mechanical simulations Differences in internal energy within the grains were ruled out because calculated GND density values were similar for both samples. The formation of secondary particles was ruled out as a contributing factor due to the type of oxide formations and their size. It was concluded that the contributing factor to the difference in the annealing response were a difference in the resulting grain size and the density of high angle grain boundaries. These two differences were largely attributed to differences in the thermal gradient conditions due to grains preferentially growing in the direction of the steepest thermal gradient.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Residual stresses and microstructure within Allvac 718Plus laser powder bed fusion bars

The residual stresses within Allvac 718Plus bars built using LBPF with different laser powers, speeds and table displacements were measured using diffraction and mechanical methods and modelled with the baseplate attached and then removed. The residual stress profiles within the bars from the top surface down through the bulk were all quite similar, becoming less tensile due to a strain hardening mechanism. Table displacement has the greatest impact on residual stress, decreasing with increasing displacement/powder layer thickness. There was good agreement amongst the modeling and measurements. The microstructures were examined and varied slightly with energy density with higher densities having larger grains and enhanced post solidification diffusion. We found energy density had minimal impact on the residuals stresses within the parameters to produce dense material.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Quantitative texture analysis using the NOMAD time-of-flight neutron diffractometer

Strategies for efficient and reliable texture measurements have been explored using the Nanoscale Ordered Materials Diffractometer (NOMAD) at the Spallation Neutron Source located at Oak Ridge National Laboratory (ORNL). To test these strategies, the texture of an Al alloy was also investigated using another neutron diffraction instrument, a constant-wavelength neutron diffractometer (NRSF2) located at the High Flux Isotope Reactor, also at ORNL. Reasonable agreement was found across the two experimental methods, but differences in overall texture strength and the symmetry of some components were noted, depending on the data reduction and analysis method selected. Finally, on the basis of these results, potential improvements are identified which would enhance the texture measurement capability on NOMAD.

47 OTHER INSTRUMENTATION↗