Cation Migration and LSCF/SDC Decomposition Related to Long-Term Operation Mode as Revealed by Electron Microscopy

This study utilized energy dispersive spectroscopy (EDS) in a scanning electron microscope (SEM) and a scanning transmission electron microscope (STEM) in order to track cation migration and related particle decomposition for air electrode components of solid oxide cells. The influence of a Sm-doped ceria (SDC) barrier layers was assessed for three operation modes (fuel cell, electrolysis, reversible) over long time periods (1000-1500 hours). Composition profiles across air electrode/electrolyte interfaces indicated negligible accumulation of La/Sr cations to the yttria-stabilized zirconia (YSZ) electrolyte during operation. Instead, air electrode particles composed of SDC and/or La-Sr-Co-Fe-oxides (LSCF) exhibited decomposition by Sr evaporation and Sm migration to LSCF particle edges.

Picard, Yoosuf↗
DOE OSTI2022

Multiphysics modeling of SOFC performance degradation caused by interface delamination and active layer cracking

In solid oxide device operation, delamination and cracking cause more catastrophic damage to cell life than other degradation mechanisms, leading to more rapid cell failure. The electrochemical performance degradation caused by electrode/electrolyte interface delamination and active layer cracking were investigated through in-house developed three-dimensional multiphysics simulations. Here the multiphysics simulations, fully calibrated against experimental datasets for button cells in a previous study, were extended to quantitatively investigate the effects of electrode/electrolyte interface delamination and active layer cracking. The simulated polarization curves and impedance behavior with various levels of delamination and cracking provided insights of the performance degradation. Furthermore, the local current distributions within the cell were analyzed for three different operating modes: constant voltage, constant current, and constant power. Finally, a practical strategy was proposed to mitigate the performance degradation in the realistic cell operations, extending overall cell lifetime.

08 HYDROGEN↗