Engineering topics
Publications and source records attributed to Fabes, B. D..
Experiments are described in which monolithic glasses, short fibers, and glass ceramics were prepared by melt processing of simulated lunar regolith. The melt was formed by direct solar as well as resistive heating and was processed using a range of techniques. The processes used in making the three types of lunar ceramics are described together with physical properties of these ceramics and their potential uses.
The goal of this project is to produce useful ceramics materials from lunar resources using the by products of lunar oxygen production processes. Emphasis is being placed on both fabrication of a variety of melt-processed ceramics, and on understanding the mechanical properties of these materials. Previously, glass-ceramics were formed by casting large glass monoliths and heating these to grow small crystallites. The strengths of the resulting glass-ceramics were found to vary with the inverse square root of the crystal grain size. The highest strengths (greater than 300 MPa) were obtained with the smallest crystal sizes (less than 10 microns). During the past year, the kinetics of crystallization in simulated lunar regolith were examined in an effort to optimize the microstructure and, hence, mechanical properties of glass ceramics. The use of solar energy for melt-processing of regolith was examined, and strong (greater than 630 MPa) glass fibers were successfully produced by melt-spinning in a solar furnace. A study of the mechanical properties of simulated lunar glasses was completed during the past year. As on Earth, the presence of moisture was found to weaken simulated lunar glasses, although the effects of surface flaws was shown to outweigh the effect of atmospheric moisture on the strength of lunar glasses. The effect of atmospheric moisture on the toughness was also studied. As expected, toughness was found to increase only marginally in an anhydrous atmosphere. Finally, our efforts to involve undergraduates in the research lab fluorished this past year. Four undergraduates worked on various aspects of these projects; and two of them were co-authors on papers which we published.
The goal is to fabricate useful ceramic materials from the by-products of lunar oxygen production processes. Specifically, the crystal nucleation and growth kinetics of ilmenite-extracted lunar regolith were studied in order to produce glass-ceramics with optimal mechanical, thermal, and abrasion resistant properties. In the initial year of the program, construction and calibration of a high temperature viscometer, used for determining the viscosity of simulated lunar glasses was finished. A series of lunar simulants were also prepared, and the viscosity of each was determined over a range of temperatures. It was found that an increase in the concentration of Fe2O3 decreases the viscosity of the glass. While this may be helpful in processing the glass, Fe2O3 concentrations greater than approximately 10 wt percent resulted in uncontrolled crystallization during viscosity measurements. Impurities (such as Na2O, MnO, and K2O) in the regolith appeared to decrease the viscosity of the parent glass. These effects, as well as those of TiO2 and SiO2 on the processability of the glass, however, remain to be quantified.
Refractories - materials which are able to withstand extremely high temperatures - are sure to be an important part of any processing facility or human outpost which is built on Mars. Containers for processing lunar oxygen will need high temperature components. Fabrication of structural material from lunar resources need both containment vessels to hold high temperature melts and molds in which to form the final shapes. Certainly, it would be desirable to fabricate such vessels and molds on the Moon, rather than carrying them up from the Earth. At first glance, this might appear to be a trivial task, since the Moon's surface consists of a variety of refractory compositions. To turn the regolith into a useful fire brick or mold, however, will require water or other binders and additives which are likely to be in extremely short supply on the Moon. The steps needed to make fire bricks and molds for lunar-derived structural materials are examined, pointing out the critical steps and resources which will be needed. While these processes and applications may seem somewhat mundane, it is emphasized that it is precisely these rudimentary processes which must be mastered before discussing making aerobrakes, and other fancier refractories from lunar resources.