Nb$^{3}$Sn Technology for Low-beta linacs

Nb3Sn is the most advanced potential successor for niobium in superconducting RF accelerator cavities. Nb3Sn has a significantly higher critical temperature (18.3 K) compared to that of niobium (9.2 K). This has a large effect on the BCS surface resistance, and therefore, on the dynamic RF losses at 4.5 K. The higher critical temperature allows two important changes for cavity and cryomodule design. First, the lower BCS losses allow the designer to use a higher frequency, translating to physically smaller cavities and cryomodules. Second, the low dynamic losses allow the use of stand-alone cryocoolers instead of complex helium refrigerators and distribution systems. Fabrication of a prototype 218 MHz cavity, test results, and continuing challenges are discussed.

43 PARTICLE ACCELERATORS↗
DOE OSTI2024

Healing Gradient Degradation in Nb3Sn SRF Cavities Using a Recoating Method

Despite having advantageous superconducting properties, Nb3Sn superconducting radiofrequency (SRF) cavities still have practical challenges compared to Nb SRF cavities due to the brittle nature of Nb3Sn. Performance degradation can occur when a Nb3Sn SRF cavity experiences mechanical stresses such as during handling and tuning of the cavity. In this study, we present a potential treatment for SRF cavities that have experienced stress induced performance degradation that involves a recoating procedure. The degraded cavity is coated with a small amount of Sn using a single step vapor-diffusion methodology. Using this approach we can recover a significant portion of the lost performance of a Nb3Sn SRF cavity.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2024

Niobium-tin as a transformative technology for low-beta linacs

Niobium-tin has been identified as the most promising next-generation superconducting material for accelerator cavities. This is due to the higher critical temperature (Tc = 18 K) of Nb3Sn compared to niobium (TC = 9.2 K), which leads to greatly reduced RF losses in the cavity during 4.5 K operation. This allows two important changes during cavity and cryomodule design. First, the higher Tc leads to negligible BCS losses when operated at 4.5 K, which allows for a higher frequency to be used, translating to significantly smaller cavities and cryomodules. Second, the reduced dissipated power lowers the required cryogenic cooling capacity, meaning that cavities can feasibly be operated on 5-10 W cryocoolers instead of a centralized helium refrigeration plant. These plants and distribution systems are costly and complex, requiring skilled technicians for operation and maintenance. These fundamental changes present an opportunity for a paradigm shift in how low-beta linacs are designed and operated. Fabrication challenges and first coated cavity test results are discussed.

43 PARTICLE ACCELERATORS↗
DOE OSTI2024

First conduction cooled photoinjector status

SRF photoguns become a promising candidate to produce highly stable electrons for UEM/UED applications because of the ultrahigh shot-to-shot stability compared to room temperature RF photoguns. SRF technology was prohibitively expensive for industrial use until two recent advancements: Nb3Sn and conduction cooling. SRF gun can provide a CW operation capability while consuming only 2W of RF power which eliminates the need of an expensive high power RF system and saves a facility footprint. Euclid is developing a continuous wave (CW), 1.5-cell, MeV-scale SRF conduction cooled photogun operating at 1.3 GHz. We aim for generation of the first beam in 2024. In this paper, we present the most up-to-date progress including results of the first cool down of the gun-cavity in the newly developed conduction cooled cryomodule and LLRF system development.

43 PARTICLE ACCELERATORS↗
DOE OSTI2023

Medium Temperature Furnace Baking of Low-beta 650 MHz Five-cell Cavities

Medium Temperature baking of low beta 650 MHz cavities was conducted in a UHV furnace. A systematic study of cavity surface resistance components, residual and BCS, was conducted, including analyzing surface resistance due to trapped magnetic flux. Cavities showed an average 4.5 nano-ohm surface resistance at 17 MV/m under 2 K, which meets PIP-II specifications with a 40% margin. The results provided helpful information for the PIP-II project to optimize the cavity processing recipe for cryomodule application. The results were compared to the 1.3 GHz cavity that received a similar furnace baking.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2023

Latest Development of Electropolishing Optimization for 650 MHz Cavity

Electropolishing (EP) of 1.3 GHz niobium (Nb) superconducting RF cavities is conducted to achieve a desired smooth and contaminant-free surface that yields good RF performance. Achieving a smooth surface of a large-sized elliptical cavity with the standard EP conditions was found to be challenging. This work aimed to conduct a systematic parametric EP study to understand the effects of various EP parameters on the surface of 650 MHz cavities used in PIP-II linac. Parameters optimized in this study provided a smooth surface of the cavities. The electropolished cavities met the baseline requirement of field gradient and qualified for further surface treatment to improve the cavity quality factor.

43 PARTICLE ACCELERATORS↗
DOE OSTI2023

Commissioning of new CVD/ALD Furnace at Fermilab

The new CVD/ALD furnace that we are commissioning at Fermilab will allow us to deposit thin films of superconducting materials on RF cavities on different shapes, 1 cell and 9 cells 1.3GHz and 1 cell and 5 cells 650MHz. This furnace is capable to perform two different types of deposition: chemical vapor deposition and atomic layer deposition. Different materials are under investigation to push accelerating superconducting RF cavities to support higher accelerating fields and to operate with lower power loss. The first tests are focusing on the alternative A15 superconductors as: Nb3Ge, Nd3Ga, Nb3Sn, V3Si. The furnace has two different sources of precursors: 1) chlorine furnace, where we can produce the precursors in-situ, so we can build our own precursors and test how the deposited material is affecting the cavity performance, 2) 6 different bubblers, 3 low temperature bubblers and 3 high temperature bubblers. The deposition chamber is a versatile chamber with two independ ent vacuum volumes, to ensure a higher cleanliness of the deposited material. The furnace is designed to have two different configurations: High temperature, up to 1400 C, and low temperature, up to 400 C.

Grassellino, Laura↗
DOE OSTI2023

First Results from Nanoindentation of Vapor Diffused Nb3Sn Films on Nb

The mechanical vulnerability of the Nb3Sn-coated cavities is identified as one of the significant technical hurdles toward deploying them in practical accelerator applications in the not-so-distant future. It is crucial to characterize the material's mechanical properties in ways to address such vulnerability. Nanoindentation is a widely used technique for measuring the mechanical properties of thin films that involves indenting the film with a small diamond tip and measuring the force-displacement response to calculate the film's elastic modulus, hardness, and other mechanical properties. For the first time, the nanoindentation analysis was performed on multiple vapor-diffused Nb3Sn samples coated at Jefferson Lab and Fermilab coating facilities. This contribution will discuss the first results obtained from the nanoindentation of Nb3Sn-coated Nb samples prepared via the Sn vapor diffusion technique.