NASA NTRS2013

Lap Shear Testing of Candidate Radiator Panel Adhesives

During testing of a subscale radiator section used to develop manufacturing techniques for a full-scale radiator panel, the adhesive bonds between the titanium heat pipes and the aluminum face sheets failed during installation and operation. Analysis revealed that the thermal expansion mismatch between the two metals resulted in relatively large shear stresses being developed even when operating the radiator at moderate temperatures. Lap shear testing of the adhesive used in the original joints demonstrated that the two-part epoxy adhesive fell far short of the strength required. A literature review resulted in several candidate adhesives being selected for lap shear joint testing at room temperature and 398 K, the nominal radiator operating temperature. The results showed that two-part epoxies cured at room and elevated temperatures generally did not perform well. Epoxy film adhesives cured at elevated temperatures, on the other hand, did very well with most being sufficiently strong to cause yielding in the titanium sheet used for the joints. The use of an epoxy primer generally improved the strength of the joint. Based upon these results, a new adhesive was selected for the second subscale radiator section.

Ellis, David↗

NASA NTRS2006

Comparison of AMZIRC and GRCop-84

The mechanical properties of two copper alloys with high thermal conductivity, GRCop-84 and AMZIRC, were compared. These are competing alloys in high temperature, high heat flux applications such as rocket nozzles. The GRCop-84 data presented was taken from previous work. The results of new tensile, creep, and compression tests on AMZIRC are presented. Tests were done on as-received hard drawn material, and on material that had been subjected to a heat treatment designed to simulate a brazing operation at 935 C. As-received AMZIRC was found to have excellent properties at temperatures below 550 C, with room temperature yield and ultimate tensile strengths of about 500 MPa, and ductile failures. By comparison, GRCop-84 s room temperature tensile yield and ultimate strengths are about 200 and 380 MPa respectively. However, the simulated brazing heat treatment substantially decreased the mechanical properties of AMZIRC; and the strength of as-received AMZIRC dropped precipitously as test temperatures exceeded 500 C. The properties of GRCop-84 were not significantly affected by the 935 C heat treatment. As a result, there appear to be advantages to GRCop- 84 over AMZIRC if use or processing temperatures of greater than 500 C are expected. Tensile creep tests were done at 500 and 650 C. At these temperatures, the creep properties of GRCop-84 were superior to AMZIRC s. At equivalent rupture life and stress, GRCop-84 was found to have a 150 C temperature advantage over AMZIRC; for equivalent rupture life and temperature GRCop-84 was two times stronger.

de Groh, Henry C. III↗

NASA NTRS2006

Comparison of the Fatigue Behavior of Copper Alloys

This presentation is about the development of advanced copper alloys with high thermal conductivity, good creep strength, and adequate fatigue strength for rocket engine applications. It also focuses on the commercial availability of the advanced alloy-GRCop-84 developed at NASA-GRC. The presentation's conclusions are that GRCop-84 has equivalent or better isothermal fatigue lives compared to other commercially available copper alloys, that GRCop-84 can be fabricated in various forms with minimal change in the fatigue lives, that it is equivalent in sothermal, fatigue to AMZIRC at moderate temperatures, and that Narloy-Z is equivalent in fatigue capabilities to GRCop-84 at 400C and below.

Lerch, Brad↗

NASA NTRS2006

Fabrication of GRCop-84 Rocket Thrust Chambers

GRCop-84, a copper alloy, Cu-8 at% Cr-4 at% Nb developed at NASA Glenn Research Center for regenerative1y cooled rocket engine liners has excellent combinations of elevated temperature strength, creep resistance, thermal conductivity and low cycle fatigue. GRCop-84 is produced from pre-alloyed atomized powder and has been fabricated into plate, sheet and tube forms as well as near net shapes. Fabrication processes to produce demonstration rocket combustion chambers will be presented and includes powder production, extruding, rolling, forming, friction stir welding, and metal spinning. GRCop-84 has excellent workability and can be readily fabricated into complex components using conventional powder and wrought metallurgy processes. Rolling was examined in detail for process sensitivity at various levels of total reduction, rolling speed and rolling temperature representing extremes of commercial processing conditions. Results indicate that process conditions can range over reasonable levels without any negative impact to properties.

Loewenthal, William↗

NASA NTRS2004

Microstructural Evaluation of KM4 and SR3 Samples Subjected to Various Heat Treatments

The gamma-gamma microstructures of two advanced powder metallurgy disk alloys, KM4 and SR3, were quantified after a series of heat treatments using transmission electron microscopy and image analysis. Relationships between the heat treatments and the resulting gamma distributions were evaluated. Statistical correlations between the gamma distributions and the reported tensile strengths, creep resistances, and dwell crack growth resistances were separately assessed for each alloy. To avoid the effects of grain size related mechanisms, the grain size of the samples used in the correlations for each alloy were limited to narrow ranges of about 1.5 in ASTM grain size number. In both alloys, yield and tensile strength increased with increasing fraction of medium sized gamma. The strength increased as the size of the medium gamma decreased and the size of the fine gamma increased. Time to 0.2 percent creep in SR3 increased with increasing medium gamma volume fraction, and decreasing fine gamma sizes. However, 0.2 percent creep time was not clearly correlated with the gamma microstructures of KM4 specimens, apparently due to effects of stabilization heat treatments which greatly suppress creep resistance. Dwell fatigue crack growth rate decreased with increasing medium gamma volume fraction, indicating more medium gamma is beneficial. The crack growth rate also decreased with decreasing gamma size, indicating finer gamma is better.

Ellis, David↗

NASA NTRS2000

GRCop-84 Development for Combustion Chamber Liners

The development, test, and thermophysical & mechanical properties of a GRCop-84 alloy for combustion chamber liners is discussed. Topics discussed include: History of GRCop-84 development, GRCop-84 thermal expansion, thermal conductivity of GRCop-84, yield strength of GRCop-84, GRCop-84 creep lives, GrCop-84 low cycle fatigue (LCF) lives, and hot fire testing of GRCop-84 spool pieces.

Ellis, David↗

NASA NTRS1999

Robust Low Cost Aerospike/RLV Combustion Chamber by Advanced Vacuum Plasma Process

Next-generation, regeneratively cooled rocket engines will require materials that can withstand high temperatures while retaining high thermal conductivity. At the same time, fabrication techniques must be cost efficient so that engine components can be manufactured within the constraints of a shrinking NASA budget. In recent years, combustion chambers of equivalent size to the Aerospike chamber have been fabricated at NASA-Marshall Space Flight Center (MSFC) using innovative, relatively low-cost, vacuum-plasma-spray (VPS) techniques. Typically, such combustion chambers are made of the copper alloy NARloy-Z. However, current research and development conducted by NASA-Lewis Research Center (LeRC) has identified a Cu-8Cr-4Nb alloy which possesses excellent high-temperature strength, creep resistance, and low cycle fatigue behavior combined with exceptional thermal stability. In fact, researchers at NASA-LeRC have demonstrated that powder metallurgy (P/M) Cu-8Cr-4Nb exhibits better mechanical properties at 1,200 F than NARloy-Z does at 1,000 F. The objective of this program was to develop and demonstrate the technology to fabricate high-performance, robust, inexpensive combustion chambers for advanced propulsion systems (such as Lockheed-Martin's VentureStar and NASA's Reusable Launch Vehicle, RLV) using the low-cost, VPS process to deposit Cu-8Cr-4Nb with mechanical properties that match or exceed those of P/M Cu-8Cr-4Nb. In addition, oxidation resistant and thermal barrier coatings can be incorporated as an integral part of the hot wall of the liner during the VPS process. Tensile properties of Cu-8Cr-4Nb material produced by VPS are reviewed and compared to material produced previously by extrusion. VPS formed combustion chamber liners have also been prepared and will be reported on following scheduled hot firing tests at NASA-Lewis.

Holmes, Richard↗

NASA NTRS1997

Microstructure and Mechanical Properties of Vacuum Plasma Sprayed Cu-8Cr-4Nb

This paper compares the tensile properties of Cu-8Cr-4Nb material produced by VPS to material previously produced by extrusion. The microstructure of the VPS material is also presented. The combustion chamber liner of rocket motors represents an extreme materials application. The liner hot wall is exposed to a 2760 C (5000 F) flame while the cold side is exposed to cryogenic hydrogen liquid. Materials for use in the combustion chamber liner require a combination of high temperature strength, creep resistance, and low cycle fatigue resistance along with high thermal conductivity. The hot side is also subject to localized cycles between reducing and oxidizing environments that degrade the liner by a process called blanching. A new Cu-8 at.% Cr-4 at% Nb (Cu-8Cr-4Nb) alloy has been developed at NASA Lewis Research Center as a replacement for the currently used alloy, NARloy-z (Cu-3 wt.% Ag-0.5 wt.% Zr). The alloy is strengthened by a fine dispersion of Cr2Nb particles. The alloy has better mechanical properties than NARloy-Z while retaining most of the thermal conductivity of pure copper. The alloy has been successfully consolidated by extrusion and hot isostatic pressing (HIPing). However, vacuum plasma spraying (VPS) offers several advantages over prior consolidation methods. VPS can produce a near net shape piece with the profile of the liner. In addition, oxidation resistant and thermal barrier coatings can be incorporated as an integral part of the liner hot wall during the VPS deposition. The low oxygen VPS Cu-8Cr-4Nb exhibits a higher strength than Cu-8Cr-4Nb produced by extrusion at elevated temperatures and a comparable strength at room temperature. Moduli and ductility were not significantly different. However, the ability to produce parts to near-net shape and maintain the good elevated temperature tensile properties of the extruded Cu-8Cr-4Nb makes VPS an attractive processing method for fabricating rocket engine combustion liners.

Holmes, Richard↗