Crystallographic ordering of Al and Sn in α-Ti

Increasing attention is being paid to α (2) Ti 3 (Al,Sn) precipitation from the α phase of titanium alloys owing to its effect on slip band formation, localisation and the implications for fatigue performance in jet engine titanium. However, the early stages of α 2 precipitation have historically been difficult to observe by electron microscopy, neutron diffraction or atom probe analysis. Here, small angle X-ray scattering is used to reexamine the phase boundary in binary Ti-Al and Ti-Sn alloys with around 500 ppmw O. It is found that the phase boundaries in the literature are approximately correct, at 6.2 wt.% Al and 16.9 wt.% Sn, and that this favours the use of Al as a solid solution strengthener over Sn for ambient temperature applications. However, once O content and phase partitioning in α + β alloys are taken into account, this implies that Al eq limits for future alloy design of critical rotating parts should be lowered substantially.

36 MATERIALS SCIENCE↗
DOE OSTI2022

The influence of alloying on slip intermittency and the implications for dwell fatigue in titanium

Dwell fatigue, the reduction in fatigue life experienced by titanium alloys due to holds at stresses as low as 60% of yield, has been implicated in several uncontained jet engine failures. Dislocation slip has long been observed to be an intermittent, scale-bridging phenomenon, similar to that seen in earthquakes but at the nanoscale, leading to the speculation that large stress bursts might promote the initial opening of a crack. Here we observe such stress bursts at the scale of individual grains in situ, using high energy X-ray diffraction microscopy in Ti–7Al–O alloys. This shows that the detrimental effect of precipitation of ordered Ti 3 Al is to increase the magnitude of rare pri $\langle$a$\rangle$ and bas $\langle$a$\rangle$ slip bursts associated with slip localisation. By contrast, the addition of trace O interstitials is beneficial, reducing the magnitude of slip bursts and promoting a higher frequency of smaller events. This is further evidence that the formation of long paths for easy basal plane slip localisation should be avoided when engineering titanium alloys against dwell fatigue.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Mechanisms of Ti 3 Al precipitation in hcp α -Ti

Here, nucleation and growth of Ti3Al α( 2 ) ordered domains in alpha-Ti-Al-X alloys were characterised using a combination of transmission electron microscopy, atom probe tomography and small angle X-ray scattering. Model alloys based on Ti-7Al (wt.%) and containing O, V and Mo were aged at 550 °C for times up to 120d and the resulting precipitate dispersions were observed at intermediate points. Precipitates grew to around 30nm in size, with a volume fraction of 6-10% depending on tertiary solutes. Interstitial O was found to increase the equilibrium volume fraction of α 2 , while V and Mo showed relatively little influence. Addition of any of the solutes in this study, but most prominently Mo, was found to increase nucleation density and decrease precipitate size and possibly coarsening rate. Coarsening can be described by the Lifshitz-Slyozov-Wagner model, suggesting a matrix diffusion-controlled coarsening mechanism (rather than control by interfacial coherency). Solutionising temperature was found to affect nucleation number density with an activation energy of E f = 1.5 +/- 0.4 eV, supporting the hypothesis that vacancy concentration affects α 2 nucleation. The observation that all solutes increase nucleation number density is also consistent with a vacancy-controlled nucleation mechanism.