The back contact is a key component for further developments of CdSeTe solar cells. In this contribution, we investigate several materials and designs that could help the development of highly-reflective, ohmic back contacts for conventional (3.45 um) and thin (800 nm) CdSeTe solar cells. We also explore numerically, nanostructured metal back contacts for light-trapping in ultrathin (200 nm) CdTe solar cells.
In this project, we attempted to make CdTe homojunctions using single crystal p-type doped substrates and closed-space sublimation epitaxy (CSSE) n-type doped films. The project included modeling which determined the ideal thickness for the n-type layer as being <200 nm. Boules of high concentration indium-doped CdTe and CdSe 0.4 Te 0.6 (CST) were grown using modified vertical Bridgman (MVB) methods. Similarly, iodine-doped CdTe crystals were grown for the first time. Washington State University (WSU) stock phosphorus-doped CdTe was used as the p-type substrate layer. The crystals were characterized by Hall effect and time-resolved photoluminescence (TRPL, for electrical properties), photoluminescence microscopy (for uniformity), X-ray diffraction (for crystal structure), and glow discharge mass spectrometry (GDMS, for dopant and impurity concentration). CdTe:I crystals were also characterized by visible and infrared transmission measurements, and various Cd or Te heat treatments were performed to assess changes in optical and electrical properties. The grown n-type materials – CdTe:In, CdSe0.4Te0.6:In, and CdTe:I – were provided to the National Renewable Energy Laboratory (NREL) for growth of CSSE thick films for characterization by two photon TRPL (for carrier lifetime), electron back-scatter diffraction (EBSD, to assess epitaxy), and Hall effect. Several measurements of secondary ion mass spectroscopy (SIMS) were performed. Nearly 100% of the indium from the crystal was incorporated into the measured thick films, while only ~2-22% of the iodine from the crystal was incorporated. The net result of the diffusion issue is that homojunction devices created using CSSE have a buried homojunction, as indicated by the near infrared peak in the external quantum efficiency (EQE). Various parameterization of front and back contacts suggested that the poor device performance was primarily a result of this buried junction and not due to other effects. There may also be an issue with the CSSE film lifetime in addition to the dopant profile.