Sb doping via drive-in diffusion as an alternative to in-situ doping in VTD

Group-V doping can enhance the efficiency of CdTe photovoltaic devices by increasing the open-circuit voltage (Voc), if long lifetimes can be retained and radiative voltage loss can be avoided. In this preliminary study, ex-situ Sb doping via drive-in diffusion improved grain sizes compared to Sb-free films without CdCl2 treatment. Sb doping did not reduce the carrier lifetime for uniform CdSeTe absorbers. Additionally, the CST-air surface recombination decreased with Sb. No potential fluctuations were observed by PL at this doping level. The [Sb] and carrier concentration for this study are not yet measured so the conclusions drawn are all preliminary

14 SOLAR ENERGY↗
DOE OSTI2024

Quantifying carrier dynamics and PL characterization of antimony-doped CdTe and CdSeTe

Our team has achieved ~20% doping activation of CdSeTe with antimony (Sb), whose shallow acceptor level makes it a viable alternative to As.1,2 Arsenic (As)-doped graded CdSeTe photovoltaics have achieved record efficiencies of 22.3%. Remaining challenges include doping activation of only ~2% in polycrystalline films and radiative voltage losses of ~100 mV. Here we use (transient) terahertz and photoluminescence spectroscopy of CdTe:Sb and CdSeTe:Sb to show sufficiently long bulk lifetimes to enable high-efficiency devices. Early results also indicate dominant bandgap emission in CdSeTe:Sb and a lack of potential fluctuations with Sb-doping that have proven detrimental for As-doped films. While more work is needed, these results show significant promise for Sb doping.

14 SOLAR ENERGY↗
DOE OSTI2024

Optimization of Sb-doped CdSeTe Solar Cells

The effect of high-temperature annealing (HTA) treatments and Cd-excess during the in-situ doping of CdSeTe:Sb is investigated. Optimized treatments eliminate the wurtzite phase from the as-deposited CdSeTe layer, while facilitating Se intermixing and grain size enhancement before CdCl2 treatment. The improved device stack quality results in a VOC improvement of 250 mV. VOC is further improved by tuning the Cd/Sb flux ratio during CdSeTe:Sb deposition. The lowest defect concentration is achieved at Cd/Sb of 1.4:1, which produced the best VOC CdSeTe:Sb cell with VOC = 849mV, despite a decreased carrier concentration due to the harsh CdCl2 treatment.

14 SOLAR ENERGY↗
DOE OSTI2024

Investigation of properties of CdSeTe/Sb and Sb/CdSeTe stacks

The effect of Sb inclusion in CdSeTe thin films was examined. CdSeTe alloys were grown by co-evaporation, either on 5 nm thick electron-beam evaporated Sb layers (Sb/CdSeTe) or coated with Sb post-deposition (CdSeTe/Sb). Sb inclusion improved CdSeTe grain structure, a critical factor for device performance, with average grain size increasing from 0.6 to 1.5 μm. All samples crystallized on annealing to the cubic structure, with a change in film orientation from (111) to random or (220). The presence of Sb in CdSeTe/Sb or Sb/CdSeTe samples, however, had a limited effect on the carrier concentration compared to Sb-free samples. Time resolved photoluminescence showed Sb inclusion increased decay lifetimes, with τ1 = 0.8 ns for and τ2 = 6.9 ns for the Sb/CdSeTe sample.

14 SOLAR ENERGY↗
DOE OSTI2024

Carrier Dynamics and Photoluminescence in Antimony-Doped CdTe and CdSeTe

Arsenic (As)-doped graded Cd(Se,Te) photovoltaics have achieved record efficiency of 22.4%, but further increases in efficiency have been limited by doping activation of only ~1% and radiative voltage losses of ~100 meV. Antimony (Sb) can also act as a p-type dopant of Cd(Se,Te) but has received relatively little attention. We measured carrier dynamics and photoluminescence of Sb-doped CdTe and CdSeTe films grown by vapor-transport deposition, with dopant activation up to ~20% Time resolved terahertz (TRTS) and photoluminescence (TRPL) data were fit by simulating the semiconductor equations, revealing bulk lifetimes of >20 ns in CdTe:Sb and >65 ns in CdSeTe:Sb and surface recombination velocities <1000 cm/s at alumina interfaces. We also qualitatively compare transients and PL spectra of doped and undoped films, with no apparent variation associated with hole concentrations up to 1015 cm-3. Preliminary variable temperature steady state photoluminescence (VT-SSPL) indicates dominant band-gap emission in CdSeTe:Sb and no evidence of potential fluctuations with Sb-doping up to this hole concentration.

14 SOLAR ENERGY↗
DOE OSTI2024

Antimony Chloride Treatments of CdTe-Based Solar Cells

Development of a new SbCl3-based solution treatment for chloride activation of CdTe-based solar cells is described. Activation was confirmed with CdSeTe:Sb devices exhibiting VOC > 550 mV and JSC > 25 mAcm-2. Treatment optimization showed strong effects of annealing time and temperature on cell properties. Material characterization indicated surface conversion of CdSeTe to CdCl2 and Sb2Te3 with SbCl3 treatment. However, no reaction products were formed with treatment under inert conditions, which was coupled with poor device performance. Drying the SbCl3 films at controlled humidity conditions confirmed that exposure to high relative humidity is critical for CdSeTe activation, through hydrolysis of SbCl3. Mechanistic details of SbCl3 speciation during hydrolysis and annealing to activate CdSeTe are discussed.

14 SOLAR ENERGY↗
DOE OSTI2023

Quantifying carrier dynamics and PL characterization of antimony-doped CdTe and CdSeTe

Our team has achieved ~20% doping activation of CdSeTe with antimony (Sb), whose shallow acceptor level makes it a viable alternative to As.1,2 Arsenic (As)-doped graded CdSeTe photovoltaics have achieved record efficiencies of 22.3%. Remaining challenges include doping activation of only ~2% in polycrystalline films and radiative voltage losses of ~100 mV. Here we use (transient) terahertz and photoluminescence spectroscopy of CdTe:Sb and CdSeTe:Sb to show sufficiently long bulk lifetimes to enable high-efficiency devices. Early results also indicate dominant bandgap emission in CdSeTe:Sb and a lack of potential fluctuations with Sb-doping that have proven detrimental for As-doped films. While more work is needed, these results show significant promise for Sb doping.

14 SOLAR ENERGY↗
DOE OSTI2023

Pyrolyzer Assisted Vapor Transport Deposition of Antimony-doped Cadmium Telluride

A new method for in-situ Sb doping of CdTe that uses a modified vapor transport deposition system is described. This modification enables control of the Sb concentration with a pyrolysis stage to enhance the doping efficiency. CdTe:Sb films under different deposition conditions are characterized by SEM, XRD, and CV measurements for determining morphology, crystal structure, and hole concentration. Variations of the Sb dopant heater and pyrolyzer temperatures do not affect the CdTe morphology and crystal structure. However, CV measurements show that a higher dopant heater or pyrolyzer temperature leads to higher hole concentration. In this study, CdTe: Sb films achieve a hole concentration of 1016 cm-3 and 10% doping efficiency when the dopant heater is 600C and the pyrolyzer temperature is 1100C. This demonstrates a path to produce high hole concentration polycrystalline CdTe film with a low concentration of dopant-induced defect.

14 SOLAR ENERGY↗