Analyses of Elemental Partitioning in Advanced Nickel-Base Superalloy Single Crystals

Aircraft propulsion engines for the High Speed Civil Transport which may be developed early in the 21st century will require significantly different durability requirements than those which currently power civil aircraft. The durability will be more difficult to achieve because it is expected that the new aircraft engines will have to operate at near maximum power for more than half of each flight compared to 5 to 10 percent for typical current aircraft. To meet this requirement, a team of NASA, Pratt & Whitney Aircraft, and General Electric personnel have been formed to develop an appropriate alloy for the mission. This report summarizes the work performed by a part of that team up to the retirement of one of its members, R.L. Dreshfield. The prime purpose of the report is to assemble the data obtained in a single document so that it may be more accessible to those who may wish to pursue it at a later date.

Dreshfield, Robert L.↗

NASA NTRS1994

Copper Alloy For High-Temperature Uses

Alloy of Cu/8Cr/4Nb (numbers indicate parts by atom percent) improved over older high-temperature copper-based alloys in that it offers enhanced high temperature strength, resistance to creep, and ductility while retaining most of thermal conductivity of pure copper; in addition, alloy does not become embrittled upon exposure to hydrogen at temperatures as high as 705 degrees C. Designed for use in presence of high heat fluxes and active cooling; for example, in heat exchangers in advanced aircraft and spacecraft engines, and other high-temperature applications in which there is need for such material. High conductivity and hardness of alloy exploited in welding electrodes and in high-voltage and high-current switches and other applications in which wear poses design problem.

Dreshfield, Robert L.↗

NASA NTRS1993

NDE of PWA 1480 single crystal turbine blade material

Cantilever bending fatigue specimens were examined by fluorescent liquid penetrant and radioactive gas penetrant (Krypton) non-destructive evaluation (NDE) methods and tested. Specimens with cast, ground, or polished surface were evaluated to study the effect of surface condition on NDE and fatigue crack initiation. Fractographic and metallurgical analyses were performed to determine the nature of crack precursors. Preliminary results show that fatigue strength was lower for specimens with cast surfaces than for specimens with machined surfaces. The liquid penetrant and gas penetrant techniques both provided indications of a large population of defects on the cast surfaces. On ground or polished specimen surfaces, the gas penetrant appeared to estimate the actual number of voids more accurately than the liquid penetrant.

Klima, Stanley J.↗

NASA NTRS1993

NDE of PWA 1480 single crystal turbine blade material

Cantilever bending fatigue specimens were examined by fluorescent liquid penetrant and radioactive gas penetrant (Krypton) Nondestructive Evaluation (NDE) methods and tested. Specimens with cast, ground, or polished surfaces were evaluated to study the effect of surface condition on NDE and fatigue crack initiation. Fractographic and metallurgical analyses were performed to determine the nature of crack precursors. Preliminary results show that fatigue strength was lower for specimens with cast surfaces than for specimens with machined surfaces. The liquid penetrant and gas penetrant techniques both provided indications of a large population of defects on the cast surfaces. On ground or polished specimen surfaces, the gas penetrant appeared to estimate the actual number of voids more accurately than the liquid penetrant.

Klima, Stanley J.↗

NASA NTRS1992

Post-test examination of a pool boiler receiver

A subscale pool boiler test apparatus to evaluate boiling stability developed a leak after being operated with boiling NaK for 791.4 hr at temperatures from 700 to 750 C. The boiler was constructed using Inconel 625 with a type 304L stainless steel wick for the boiler and type 316 stainless steel for the condenser. The boiler assembly was metallurgically evaluated to determine the cause of the leak and to assess the effects of the NaK on the materials. It was found that the leak was caused by insufficient (about 30 pct.) joint penetration in a butt joint. There was no general corrosion of the construction materials, but the room temperature ductility of the Inconel 625 was only about 6.5 pct. A crack in the heat affected zone of the Inconel 625 near the Inconel 625 to type 316 stainless steel butt joint was probably caused by excessive heat input. The crack was observed to have a zone depleted of iron at the crack surface and porosity below that zone. The mechanism of the iron depletion was not conclusively determined.

Dreshfield, Robert L.↗

NASA NTRS1991

The effect of porosity and gamma-gamma' eutectic content on the low cycle fatigue behavior of hydrogen-charged PWA-1480

Single crystal superalloys such as PWA 1480 are considered for turbopump blades in the main engines of the space shuttle. As fatigue resistance in a hydrogen environment is a key issue in this application, a study of the effect of porosity and gamma-gamma' eutectic content on the fatigue life of a hydrogen-charged PWA 1480 was performed. Porosity and eutectic were linked to fatigue initiation, and therefore reduction of either of both may be one means to improve fatigue life of PWA 1480 when hydrogen is present.

Gayda, John↗

NASA NTRS1988

Materials technology assessment for a 1050 K Stirling space engine design

An assessment of materials technology and proposed materials selection was made for the 1050 K (superalloy) Stirling Space Engine design. The objectives of this assessment were to evaluate previously proposed materials selections, evaluate the current state-of-the-art materials, propose potential alternate materials selections and identify research and development efforts needed to provide materials that can meet the stringent system requirements. This assessment generally reaffirmed the choices made by the contractor. However, in many cases alternative choices were described and suggestions for needed materials and fabrication research and development were made.

Scheuermann, Coulson M.↗

NASA NTRS1987

Defects in nickel-base superalloys

The presence of substantial amounts of the sigma phase in Ni-base superalloys can drastically reduce the alloy's stress rupture life. No predictive system exists which is entirely successful in anticipating the formation of sigma, mu, and similar phases in new and substantially different alloys. Freckles are defects due to the segregation of elements in quantities that can lead to phase precipitation, and are caused by gravity-driven fluid motion that yields microsegregation in the ingots typically used in the fabrication of structures based on these alloys. Also noted are the effects of porosity and grain boundaries on superalloy mechanical properties.

Dreshfield, Robert L.↗

NASA NTRS1987

Observations of directional gamma prime coarsening during engine operation

Two alloys with negative mismatch parameters, NASAIR 100 and a modified NASAIR 100 called Alloy 3 were run as turbine blades in an experimental ground based Garret TFE731 engine for up to 200 hr. The directional coarsening of gamma prime (rafting) that developed during engine testing was analyzed and compared to previous research from laboratory tests. The blades were found to be rafted normal to the centrifugal stress axis over much of the span, but near the surfaces, the blades were found to be rafted parallel to the centrifugal stress axis for certain cycles. Representative photomicrographs of the blades and the effects of stress and temperature on raft formation are shown.

Draper, Susan L.↗

NASA NTRS1986

Understanding single-crystal superalloys

The unique properties of single crystals are considered. The anisotropic properties of single crystals, and the relation between crystal orientation and the fatigue life and slip systems of the crystals are examined. The effect of raft formation on the creep-rupture life of the crystals is studied. Proposed research on the properties of and new applications for single crystals is discussed.