Electrochemical study of aluminum corrosion in boiling high-purity water includes an equation relating current and electrochemical potential derived on the basis of a physical model of the corrosion process. The work involved an examination of the cathodic polarization behavior of 1100 aluminum during aqueous oxidation.
Report describes a technique for reducing the corrosion rate of aluminum by adding colloidal substances in a closed-loop system. Experimental work shows that the addition of graphite and colloidal hydrated aluminum oxide significantly reduces the corrosion rate in flowing high-temperature water.
Study provides insight into the oxidation mechanism of zirconium by combining electrical measurements with oxidation data. The measurement of electrical potential across growing scale on zirconium and the determination of conventional weight-change oxidation data were carried out at 550, 700, and 800 degrees C.
Corrosion of 1100 aluminum in oxygen-saturated water at 70 degrees C under experimental conditions was studied, emphasizing effects of exposure interruption, the number of specimens, and the refreshment rate. A logarithmic equation was derived to express the corrosion rate.
Corrosion effects of aluminum-copper and aluminum-nickel couples in oxygenated distilled water, and aluminum alloys in oxygenated copper sulfate solution were studied. One of each of the couples had a water tight seal, and showed no substantial corrosion, and of the unsealed couples, only the aluminum-copper developed corrosion.