NASA NTRS1990

Containerless processing of fluoride glass

Ground-based experiments on glass formation, crystallization, surface tension, vaporization, and chemical durability of a zirconium-barium-lanthanum (ZBL) fluoride glass are summarized. In a container large, columnar grains grew out from the container-glass interface during cooling. The main crystalline phase was alpha BaZrF6. A ZBL glass sphere was levitated acoustically during Shuttle flight STS-11. The glass was melted and then cooled while being levitated (containerless). Crystallization in the recovered sample was very fine and mainly beta BaZr2F10, showing the influence of the container on the nucleation and microstructure of crystallization in the glass. Glass formation should be easier for a containerless glass than in a container.

Doremus, Robert H.↗

NASA NTRS1988

Crystallization of BaF2-ZnF2-YbF3-ThF4 glass

The phases and the rates of crystallization in a Ba-Zn-Yb-Th fluoride glass were studied using differential scanning calorimetry, XRD, and observational and chemical SEM analyses. The crystallizing phases that were identified included a BaYbTh fluoride, ZnF2, and YbF3. The BaYbTh fluoride crystallized first at about 450 C, and ZnF2, which was excluded from this phase, crystallized at its surfaces. At higher temperatures, the BaYbTh fluoride phase decomposed partially to BaThF6 and YbF3 phases.

Garcia, Roberto↗

NASA NTRS1988

Noncontact temperature measurement in glass and other transparent materials

The relationship between the optical properties of glass and temperature measurements in it by radiation pyrometry are described. Equations for the calculation of emissivity are presented and the transmittance, surface reflection and absorption characteristics of glass are defined. Recommendations are given regarding the selection of pyrometer wavelength sensitivity and the use of a blackbody radiator.

Doremus, Robert H.↗

NASA NTRS1986

Annealing of electron damage in mid-IR transmitting fluoride glass

Damage in ZrF4-BaF2-LaF3 glass induced by high-energy electrons was studied by ESR and optical spectroscopy. An optical absorption band at 314 nm in the irradiated glass annealed rapidly above about 50 C, probably by a second-order reaction at room temperature; the ESR lines annealed very slowly at room temperature.

Bansal, Narottam P.↗

NASA NTRS1984

Crystallization of fluorozirconate glasses

The crystallization of a number of glasses of the fluorozirconate family has been studied (using powder X-ray diffraction and DSC) as a function of time and temperature of heating. The main crystalline phases were beta BaZrF6 and beta BaZr2F10. Stable and metastble transformations to the low-temperature alpha phases were also investigated. The size of crystallites in fully devitrified glasses was calculated (from line broadening of the X-ray diffraction peaks) to be about 60 nm.

Bansal, Narottam P.↗

NASA NTRS1983

Surface crystallization of a fluoride glass

Growth of crystals on the surface of a Zr-Ba-La fluoride glass was observed by optical and scanning electron microscopy. Small, dark crystal nucleated rapidly and grew to a size of about 10 microns; then they stopped growing, and wrinkled regions emerged, covering the entire crystal surface.

Bansal, Narottam P.↗