Hydrogen transport in iron and steel
The permeabilities of protium, deuterium, and tritium in foil specimens of Marz grade iron, 4130 steel, Armco iron, HP-9-4-20, and T-1 steels were studied at hydrogen pressures between 0.02 and 0.5 MPa over the temperature range 260-700 K. The permeability was measured by a pressure-rise method, deuterium counting with a detector, and radioactivity counting. Good agreement is found between the measurement techniques used. It is shown that the permeabilities of protium, deuterium, and tritium in iron and T-1 steel at temperatures as low as 260 K are in good agreement with the equation proposed by Gonzalez (1967). However, the permeabilities of HP-9-4-20 and 4130 steel to hydrogen are typically lower than predicted. The isotope effect on hydrogen permeability of HP-9-4-20, 4130 and T-1 steels, and high-purity iron can be estimated by an inverse square root of mass correction.