DOE OSTI2022

Structure–Transport Properties Governing the Interplay in Humidity-Dependent Mixed Ionic and Electronic Conduction of Conjugated Polyelectrolytes

Polymeric mixed ionic-electronic conductors (MIECs) are of broad interest in the field of energy storage and conversion, opto-electronics, and bioelectronics. A class of polymeric MIECs are conjugated polyelectrolytes (CPEs), which possess a p-conjugated backbone imparting electronic transport characteristics along with side chains comprised of a pendant ionic group to allow for ionic transport. Here, our study focuses on the humidity-dependent structure-transport properties of poly[3-(potassium-n-alkanoate) thiophene-2,5-diyl] (P3KnT) CPEs with varied side-chain lengths of n = 4, 5, 6, and 7. UV-Vis spectroscopy along with electronic paramagnetic resonance (EPR) spectroscopy reveal the infiltration of water leads to a hydrated, self-doped state that allows for electronic transport. The resulting humidity-dependent ionic conductivity (σ i ) of the thin films shows a monotonic increase with relative humidity (RH) while electronic conductivity (σ e ) follows a nonmonotonic profile. The values of σ e continue to rise with increasing RH reaching a local maximum after which σ e begins to decrease. P3KnTs with higher n values demonstrate greater resiliency to increasing RH before suffering decrease in σ e . This drop in σ e is attributed to two factors. First, disruption of the locally-ordered π-stacked domains observed through in situ humidity-dependent grazing incidence wide angle X-ray scattering (GIWAXS) experiments can account for some of the decrease in σ e . A second and more dominant factor is attributed to the swelling of the amorphous domains where electronic transport pathways connecting ordered domains are impeded. P3K7T is most resilient to swelling (based on ellipsometry and water uptake measurements) where sufficient hydration allows for high σ i (1.0 × 10 -1 S/cm at 95% RH) while not substantially disrupting σ e (1.7 × 10 -2 S/cm at 85% RH and 8.0 × 10 -3 S/cm at 95% RH). Overall, our study highlights the complexity of balancing electronic and ionic transport in hydrated CPEs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Correlating conductivity and Seebeck coefficient to doping within crystalline and amorphous domains in poly(3-(methoxyethoxyethoxy)thiophene)

Molecular doping of conjugated polymers (CPs) plays a vital role in optimizing organic electronic and energy applications. For the case of organic thermoelectrics, it is commonly believed that doping CPs with a strong dopant could result in higher conductivity (σ) and thus better power factor (PF). Herein, by investigating thermoelectric performance of a polar side-chain bearing CP, poly(3- (methoxyethoxyethoxy)thiophene) (P3MEET), vapor doped with fluorinatedderivative of tetracyanoquinodimethane FnTCNQ (n = 1, 2, 4), we show that using strong dopants can in fact have detrimental effects on the thermoelectric performance of CPs. Despite possessing higher electron affinity, doping P3MEET with F4TCNQ only results in a σ (27.0 S/cm) comparable to samples doped with other two weaker dopants F2TCNQ and F1TCNQ (26.4 and 20.1 S/cm). Interestingly, F4TCNQ-doped samples display a marked reduction in the Seebeck coefficient (α) compared to F1TCNQ- and F2TCNQ-doped samples from 42 to 13 μV/ K, leading to an undesirable suppression of the PF. Additionally, structural characterizations coupled with Kang-Snyder modeling of the α–σ relation show that the reduction of α in F4TCNQ-doped P3MEET samples originates from the generation of low mobility carrier within P3MEET's amorphous domain. Our results demonstrate that factors such as dopant distribution and doping efficiency within the crystalline and amorphous domains of CPs should play a crucial role in advancing rational design for organic thermoelectrics.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Ionic Dopant-Induced Ordering Enhances the Thermoelectric Properties of a Polythiophene-Based Block Copolymer

Conjugated polymer-based block copolymers (CP-BCPs) are an unexplored class of materials for organic thermoelectrics. In this study, the authors report on the electronic conductivity (σ) and Seebeck coefficient (α) of a newly synthesized CP-BCP, poly(3-hexylthiophene)-block-poly (oligo-oxyethylene methacrylate) (P3HT-b-POEM), upon solution co-processing with lithium bis(trifluoromethanesulfonyl)imide (LiTFSI), and subsequently vapor-doping with a molecular dopant, 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ). It is found that the addition of the hydrophilic block POEM greatly enhances the processability of P3HT, enabling homogeneous solution-mixing with LiTFSI. Notably, interactions between P3HT-b-POEM with ionic species significantly improve molecular order and unexpectedly cause electrical oxidizing doping of P3HT block both in solution and solid-states, a phenomenon that has not been previously observed in Li-salt containing P3HT. Vapor doping of P3HT-b-POEM-LiTFSI thin films with F4TCNQ further enhances σ and yields a thermoelectric power factor PF = α 2 σ of 13.0 μW m -1 K -2 , which is more than 20 times higher than salt-free P3HT-b-POEM sample. Through modeling thermoelectric behaviors of P3HT-b-POEM with the Kang-Snyder transport model, the improvement in PF is attributed to higher electronic charge mobility originating from the enhanced molecular ordering of P3HT. The results demonstrate that solution co-processing CP-BCPs with a salt is a powerful method to control structure and performance of organic thermoelectric materials.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Side chain engineering control of mixed conduction in oligoethylene glycol-substituted polythiophenes

A major limitation for polymeric mixed ionic/electronic conductors (MIECs) is the trade-off between ionic and electronic conductivity; changes made that improve one typically hinder the other. In order to address this fundamental problem, this work provides insight into ways that we could improve one type of conduction without hindering the other. Here, we investigated a common oligoethylene glycol side chain polymer by adjusting the oxygen atom content and position, providing structural insights for materials that better balanced the two conduction pathways. The investigated polymer series showed the prototypical conflict between ionic and electronic conduction for oxygen atom content, with increasing oxygen atom content increasing ionic conductivity, but decreasing electronic conductivity; however, by increasing the oxygen atom distance from the polymer backbone, both ionic and electronic conductivity could be improved. Following these rules, we show that poly(3-(methoxyethoxybutyl)thiophene), when blended with lithium bistrifluoromethanesulfonimide (LiTFSI), matches the ionic conductivity of a comparable MIEC [poly(3-(methoxyethoxyethoxymethyl)thiophene)], while simultaneously showing higher electronic conductivity, highlighting the potential of this design strategy. We also provide strategies for tuning the MIEC performance to fit a desired application, depending on if electronic, ionic, or balanced conduction is most important. These results have implications beyond just polythiophene-based MIECs, as these strategies for balancing backbone crystallization and coordinating group interconnectivity apply for all semicrystalline conjugated polymers.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Complex Relationship between Side-Chain Polarity, Conductivity, and Thermal Stability in Molecularly Doped Conjugated Polymers

Molecularly doped conjugated polymers with polar side chains are an emerging class of conducting materials exhibiting enhanced and thermally stable conductivity. In this work, we study the electronic conductivity (σ) and the corresponding thermal stability of two polythiophene derivatives comprising oligoethylene glycol side chains: one having oxygen attached to the thiophene ring (poly(3-(methoxyethoxyethoxy)thiophene) (P3MEET)) and the other having a methylene spacer between the oxygen and the thiophene ring (poly(3-(methoxyethoxyethoxymethyl)thiophene) (P3MEEMT)). Thin films were vapor-doped with fluorinated derivatives of tetracyanoquinodimethane (FnTCNQ, n = 4, 2, 1) to determine the role of dopant strength (electron affinity) in maximum achievable σ. Specifically, when vapor doping with F 4 TCNQ, P3MEET achieved a substantially higher σ of 37.1 ± 10.1 S/cm compared to a σ of 0.82 ± 0.06 S/cm for P3MEEMT. Structural characterization using a combination of X-ray and optical spectroscopy reveals that the higher degree of conformational order of polymer chains in the amorphous domain upon doping with F 4 TCNQ in P3MEET is a major contributing factor for the higher σ of P3MEET. Additionally, vapor-doped P3MEET exhibited superior thermal stability compared to P3MEEMT, highlighting that the presence of polar side chains alone does not ensure higher thermal stability. Molecular dynamics simulations indicate that the dopant–side-chain nonbond energy is lower in the P3MEET:F 4 TCNQ mixture, suggesting more favorable dopant–side-chain interaction, which is a factor in improving the thermal stability of a polymer/dopant pair. Our results reveal that additional factors such as polymer ionization energy and side-chain–dopant interaction should be taken into account for the design of thermally stable, highly conductive polymers.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Charge carrier transport in thin conjugated polymer films: influence of morphology and polymer/substrate interactions

The performance of conjugated polymer (CP)-based electronic devices relies on optimal charge carrier mobilities, which are determined by monomeric architecture, degree of polymerization, chain conformation, and the nano- and mesoscale morphologies. With regard to the latter, we discuss two effects that have received limited attention in the literature, yet important for device performance optimization: (1) the role of morphological disorder and of CP/substrate interactions on the in-plane and out-of-plane carrier transport in CPs; (2) the impact of morphological disorder on charge transfer at the CP/substrate interface. The emergence of film thickness-dependent carrier mobilities, varying over two orders of magnitude within a length scale of 200 nm, and band-bending phenomena, extending tens of nanometers within the CP, are associated with these effects. These findings suggest areas for further research in order to enable widespread applications of next-generation CP-based devices.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Intrinsic Ion Transport Properties of Block Copolymer Electrolytes

Knowledge of intrinsic properties is of central importance for materials design and assessing suitability for specific applications. Self-assembling block copolymer electrolytes (BCEs) are of great interest for applications in solid-state energy storage devices. A fundamental understanding of ion transport properties, however, is hindered by the difficulty in deconvoluting extrinsic factors, such as defects, from intrinsic factors, such as the presence of interfaces between the domains. Here, we quantify the intrinsic ion transport properties of a model BCE system consisting of poly(styrene-block-ethylene oxide) (SEO) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) salt using a generalizable strategy of depositing thin films on interdigitated electrodes and self-assembling fully connected parallel lamellar structures throughout the films. Comparison between conductivity in homopolymer poly(ethylene oxide) (PEO)-LiTFSI electrolytes and the analogous conducting material in SEO over a range of salt concentrations (r, molar ratio of lithium ion to ethylene oxide repeat units) and temperatures reveals that between 20% and 50% of the PEO in SEO is inactive. Using mean-field theory calculations of the domain structure and monomer concentration profiles at domain interfaces-both of which vary substantially with salt concentration-the fraction of inactive PEO in the SEO, as derived from conductivity measurements, can be quantitatively reconciled with the fraction of PEO that is mixed with greater than a few volume percent of polystyrene. Despite the detrimental interfacial effects for ion transport in BCEs, the intrinsic conductivity of the SEO studied here (ca. 10 -3 S/cm at 90 degrees C, r = 0.085) is an order of magnitude higher than reported values from bulk samples of similar molecular weight SEO (ca. 10 -4 S/cm at 90 degrees C, r = 0.085). Finally, this work provides motivation and methods for pursuing improved BCE chemical design, interfacial engineering, and processing.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Leveraging Sequential Doping of Semiconducting Polymers to Enable Functionally Graded Materials for Organic Thermoelectrics

With the ability to modulate electronic properties through molecular doping coupled with ease in processability, semiconducting polymers are at the forefront in enabling organic thermoelectric devices for thermal energy management. In contrast to uniform thermoelectric material properties, an alternative route focuses on functionally graded materials (FGMs) where one spatially controls and optimizes transport properties across the length of a thermoelectric material. While primarily studied in the context of inorganic materials, the concept of FGMs for organic thermoelectrics has not been explored. Herein, we introduce how molecular doping of semiconducting polymers enables spatial compositional control of thin-film FGMs. Specifically, we utilize sequential vapor doping of poly[2,5-bis(3-tetradecylthiophen-2-yl) thieno [3,2-b]thiophene] (PBTTT) with the small molecule acceptor 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ) to fabricate the simplest form of FGMs – double- segmented thin films. The two thin-film segments are of equal length (7.5 mm), but each set to different doping levels. Our study focuses on understanding the thermoelectric properties (Seebeck coefficient, α, and electronic conductivity, σ) and structural properties (through X-ray scattering, UV-vis-NIR spectroscopy, and Raman spectroscopy) within and across the two segments. We observe the presence of a small diffuse interfacial region of 0.5 – 1 mm between the two segments where the doping level and transport properties vary continuously. Despite the diffuse interface, the measured effective Seebeck coefficient (αeff) across the two segments is simply the average of α within each segment. Importantly, this experimental result is consistent with reported mathematical models describing αeff in graded thermoelectric materials. Finally, our results demonstrate the facile fabrication and characterization of functionally graded organic thermoelectric materials, providing guidelines for further development on more complex FGMs.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Thermal Stability of π-Conjugated n -Ethylene-Glycol-Terminated Quaterthiophene Oligomers: A Computational and Experimental Study

This work represents a joint computational and experimental study on a series of $\textit{n}$-ethylene glycol (PEO$\textit{n}$)-terminated quaterthiophene (4T) oligomers for 1 < $\textit{n}$ < 10 to elucidate their self-assembly behavior into a smectic-like lamellar phase. This study builds on an earlier study for $\textit{n}$ = 4 that showed that our model predictions were consistent with experimental data on the melting behavior and structure of the lamellar phase, with the latter consisting of crystal-like 4T domains and liquid-like PEO4 domains. The present study aims to understand how the length of the terminal PEO$\textit{n}$ chains modulates the disordering temperature of the lamellar phase and hence the relative stability of the ordered structure. In this work, a simplified bilayer model, where the 4T domains are not explicitly described, is put forward to efficiently estimate the disordering effect of the PEO domains with increasing n; this method is first validated by correctly predicting that layers of alkyl (PE)-capped 4T oligomers (for 1 < $\textit{n}$ < 10) stay ordered at room temperature. Both 4T-domain implicit and explicit model simulations reveal that the order-disorder temperature decreases with the length of the PEO capping chains, as the associated increase in conformational entropy drives a tendency toward disorder that overtakes the cohesive energy, keeping the ordered packing of the 4T domains.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗