NASA NTRS1982

Benchmark notch test for life prediction

The laser Interferometric Strain Displacement Gage (ISDG) was used to measure local strains in notched Inconel 718 test bars subjected to six different load histories at 649 C (1200 F) and including effects of tensile and compressive hold periods. The measurements were compared to simplified Neuber notch analysis predictions of notch root stress and strain. The actual strains incurred at the root of a discontinuity in cyclically loaded test samples subjected to inelastic deformation at high temperature where creep deformations readily occur were determined. The steady state cyclic, stress-strain response at the root of the discontinuity was analyzed. Flat, double notched uniaxially loaded fatigue specimens manufactured from the nickel base, superalloy Inconel 718 were used. The ISDG was used to obtain cycle by cycle recordings of notch root strain during continuous and hold time cycling at 649 C. Comparisons to Neuber and finite element model analyses were made. The results obtained provide a benchmark data set in high technology design where notch fatigue life is the predominant component service life limitation.

Domas, P. A.↗

NASA NTRS1982

Benchmark notch test for life prediction

Aircraft gas turbine engine components are subjected to severe stress, temperature, and environmental conditions. Economic and reliabilty demands have prompted inordinate effort in development of analytic methods to predict stresses and strains in aircraft engines. There remains, however, the need to check or verify these analytical methodologies against actual experimental data measurements. The laser interferometric strain displacement gage was recognized as having the potential to accomplish this task and was employed in this program. The actual strains incurred at the root of a discontinuity in cyclically loaded test samples subjected to inelastic deformation at high temperature where creep deformation readily occur were measured. The steady-state, cyclic stress-strain response at the root of the discontinuity in the tested samples was analyzed for comparison with the measured results. A comprehensive set of local notch root strain measurements for a variety of load patterns in an Inconel 718 notch specimen at 649 C (1200 F) was obtained and documented using the laser interferometric strain displacement gage.

Domas, P. A.↗

NASA NTRS1978

Redundant disc

A rotatable disc is described that consists of parallel plates tightly joined together for rotation about a hub. Each plate is provided with several angularly projecting spaced lands. The lands of each plate are interposed in alternating relationship between the lands of the next adjacent plate. In this manner, circumferential displacement of adjacent sectors in any one plate is prevented in the event that a crack develops. Each plate is redundantly sized so that, in event of structural failure of one plate, the remaining plates support a proportionate share of the load of the failed plate. The plates are prevented from separating laterally through the inclusion of generally radially extending splines which are inserted to interlock cooperating, circumferentially adjacent lands.

Barack, W. N.↗

NASA NTRS1976

An improved turbine disk design to increase reliability of aircraft jet engines

An analytical study was performed on a novel disk design to replace the existing high-pressure turbine, stage 1 disk on the CF6-50 turbofan engine. Preliminary studies were conducted on seven candidate disk design concepts. An integral multidisk design with bore entry of the turbine blade cooling air was selected as the improved disk design. This disk has the unique feature of being redundant such that if one portion of the disk would fail, the remaining portion would prevent the release of large disk fragments from the turbine system. Low cycle fatigue lives, initial defect propagation lives, burst speed, and the kinetic energies of probable disk fragment configurations were calculated, and comparisons were made with the existing disk, both in its current material, IN 718, and with the substitution of an advanced alloy, Rene 95. The design for redundancy approach which necessitated the addition of approximately 44.5 kg (98 lb) to the design disk substantially improved the life of the disk. The life to crack initiation was increased from 30,000 cycles to more than 100,000 cycles. The cycles to failure from initial defect propagation were increased from 380 cycles to 1564 cycles. Burst speed was increased from 126 percent overspeed to 149 percent overspeed. Additionally, the maximum fragment energies associated with a failure were decreased by an order of magnitude.