DiGregorio, Anthony | Engineering Papers

NASA NTRS2002

Micro-Cracking Detection in Laminated Composites

Porosity and fatigue cracking are two critical factors that affect the performance and safety of cryogenic fuel tanks and feedlines made from unlined laminated or weaved carbon/epoxy materials. This paper presents the experiments to induce fatigue cracking of laminated composites through thermal cycling as well as the feasibility of using Thermography and Ultrasound Spectroscopy technology (UT) to detect and measure such micro-cracking. Carbon/epoxy laminated composite panels were built and cut into strips. These specimens were partially submerged in liquid nitrogen while subjected to various loads on a test machine. Edges of some specimens were polished and etched to determine the degree of micro-cracking. The rest of specimens were then examined with Thermography and Ultrasound Spectroscopy NDE systems to investigate the feasibility of finding such micro-cracking in the laminated composites. Thermography is utilized to determine changes in thermal diffusivity. The degree of cracking may reduce the apparent thermal diffusivity and therefore change the thermal response on the surface. Thermography testing was conducted on a group of specimens where it is desired to have some correlation between the predetermined stress and the thermography data. Ultrasound Spectroscopy was used to determine peak changes between the pre-stressed and stressed samples. Data from the inspections were analyzed and the results are presented in this paper.

Chu, Tsuchin↗

NASA NTRS1999

The Effect of Penetration Depth on Thermal Contrast of NDT by Thermography

Nondestructive evaluation by Thermography (TNDE) is generally classified into two categories, the passive approach and the active approach. The passive approach is usually performed by measuring the natural temperature difference between the ambient and the material or structure to be tested. The active approach, on the other hand, requires the application of an external energy source to stimulate the material for inspection. A laser, a heater, a hot air blower, a high power thermal pulse, mechanical, or electromagnetic energy may provide the energy sources. For the external heating method to inspect materials for defects and imperfection at ambient temperature, a very short burst of heat can be introduced to one of the surfaces or slow heating of the side opposite to the side being observed. Due to the interruption of the heat flow through the defects, the thermal images will reveal the defective area by contrasting against the surrounding good materials. This technique is called transient Thermography, pulse video Thermography, or thermal wave imaging. As an empirical rule, the radius of the smallest defect should be at least one to two times larger than its depth under the surface. Thermography is being used to inspect void, debond, impact damage, and porosity in composite materials. It has been shown that most of the defects and imperfection can be detected. However, the current method of inspection using thermographic technique is more of an art than a practical scientific and engineering approach. The success rate of determining the defect location and defect type is largely depend on the experience of the person who operates thermography system and performs the inspection. The operator has to try different type of heat source, different duration of its application time, as well as experimenting with the thermal image acquisition time and interval during the inspection process. Further-more, the complexity of the lay-up and structure of composites makes it more difficult to determine the optimal operating condition for revealing the defects. In order to develop an optimal thermography inspection procedure, we must understand the thermal behavior inside the material subjected to transient heat in order to interpret the thermal images correctly. Fabrication of finite element models of characteristic defects in composite materials subjected to transient heat will enable the development of appropriate procedure for thermography inspection. Design of phantom defects could be modeled and behavior characterized prior to physically building these test parts. Since production of phantom test parts can be very time consuming and laborious, it is important to design good representative defects.

Chu, Tsuchin Philip↗