Modeling Creep Effects within SiC/SiC Turbine Components

Anticipating the implementation of advanced SiC/SiC ceramic composites into the hot section components of future gas turbine engines, the primary objective of this on-going study is to develop physics-based analytical and finite-element modeling tools to predict the effects of constituent creep on SiC/SiC component service life. A second objective is to understand how to possibly select and manipulate constituent materials, processes, and geometries in order to minimize these effects. In initial studies aimed at SiC/SiC components experiencing through-thickness stress gradients, creep models were developed that allowed an understanding of detrimental residual stress effects that can develop globally within the component walls. It was assumed that the SiC/SiC composites behaved as isotropic visco-elastic materials with temperature-dependent creep behavior as experimentally measured in-plane in the fiber direction of advanced thin-walled 2D SiC/SiC panels. The creep models and their key results are discussed assuming state-of-the-art SiC/SiC materials within a simple cylindrical thin-walled tubular structure, which is currently being employed to model creep-related effects for turbine airfoil leading edges subjected to through-thickness thermal stress gradients. Improvements in the creep models are also presented which focus on constituent behavior with more realistic non-linear stress dependencies in order to predict such key creep-related SiC/SiC properties as time-dependent matrix stress, constituent creep and content effects on composite creep rates and rupture times, and stresses on fiber and matrix during and after creep.

DiCarlo, J. A.↗

NASA NTRS2004

SiC/SiC Composites for 1200 C and Above

The successful replacement of metal alloys by ceramic matrix composites (CMC) in high-temperature engine components will require the development of constituent materials and processes that can provide CMC systems with enhanced thermal capability along with the key thermostructural properties required for long-term component service. This chapter presents information concerning processes and properties for five silicon carbide (SiC) fiber-reinforced SiC matrix composite systems recently developed by NASA that can operate under mechanical loading and oxidizing conditions for hundreds of hours at 1204, 1315, and 1427 C, temperatures well above current metal capability. This advanced capability stems in large part from specific NASA-developed processes that significantly improve the creep-rupture and environmental resistance of the SiC fiber as well as the thermal conductivity, creep resistance, and intrinsic thermal stability of the SiC matrices.

DiCarlo, J. A.↗

NASA NTRS2004

Issues on Fabrication and Evaluation of SiC/SiC Tubes With Various Fiber Architectures

SiC/SiC engine components, high-modulus Sylramic-iBN SiC fiber tows were used to form nine different tubular architectural preforms with 13 mm (0.5 in.) inner diameter and lengths of approx. 75 and 230 mm (approx. 3 and approx, 9 in.). The thin-walled preforms were then coated with a BN interphase and densified with a hybrid SiC matrix using nearly the same process steps previously established for slurry-cast melt-infiltrated Sylramic-iBN/BN/SiC flat panels. The as-fabricated CMC tubes were microstructurally evaluated and tested for tensile hoop and flexural behavior, and some of the tubes were also tested in a low-pressure burner rig test with a high thru-thickness thermal gradient. To date, four general tube scale-up issues have been identified: greater CVI deposits on outer wall than inner wall; increased ply thickness and reduced fiber fraction; poor test standards for accurately determining the hoop strength of a small-diameter tube; and poor hoop strength for architectures with seams or ply ends. The underlying mechanisms and possible methods for their minimization are discussed.

Yun, H. M.↗

NASA NTRS2004

Advanced Constituents and Processes for Ceramic Composite Engine Components

The successful replacement of metal alloys by ceramic matrix composites (CMC) in hot-section engine components will depend strongly on optimizing the processes and properties of the CMC microstructural constituents so that they can synergistically provide the total CMC system with improved temperature capability and with the key properties required by the components for long-term structural service. This presentation provides the results of recent activities at NASA aimed at developing advanced silicon carbide (Sic) fiber-reinforced hybrid Sic matrix composite systems that can operate under mechanical loading and oxidizing conditions for hundreds of hours at 2400 and 2600 F, temperatures well above current metal capability. These SiC/SiC composite systems are lightweight (-30% metal density) and, in comparison to monolithic ceramics and carbon fiber-reinforced ceramic composites, are able to reliably retain their structural properties for long times under aggressive engine environments. It is shown that the improved temperature capability of the SiC/SiC systems is related first to the NASA development of the Sylramic-iBN Sic fiber, which displays high thermal stability, creep resistance, rupture resistance, and thermal conductivity, and possesses an in-situ grown BN surface layer for added environmental durability. This fiber is simply derived from Sylramic Sic fiber type that is currently produced at ATK COI Ceramics. Further capability is then derived by using chemical vapor infiltration (CVI) to form the initial portion of the hybrid Sic matrix. Because of its high creep resistance and thermal conductivity, the CVI Sic matrix is a required base constituent for all the high temperature SiC/SiC systems. By subsequently thermo- mechanical-treating the CMC preform, which consists of the S ylramic-iBN fibers and CVI Sic matrix, process-related defects in the matrix are removed, further improving matrix and CMC creep resistance and conductivity.

Yun, H. M.↗

NASA NTRS2004

Thermo-Mechanical Properties of Super Sylramic SiC Fibers

Ceramic matrix composites (CMC) reinforced by Sic fibers, such as SiC/SiC, are targeted for application in hot-section components of advanced engines for aerospace propulsion and for electrical power generation. Two Super Sylramic Sic fiber types recently developed at NASA using the Sylramic fiber from COI Ceramics are candidates fof providing these components with improved thermal capability and improved performance. This paper reports on the state-of-the-art ability of these new fiber types to meet the key fiber requirements of these applications: high strength, high creep-rupture resistance, high environmental resistance, and high thermal conductivity. For example, creep-rupture tests performed at from 1350 to 1500 C under various environments to simulate CMC fabrication and service conditions show creep resistance in air improved -20 and -7 times in comparison to current Sylramic and Sylramic-iBN fiber types, respectively. This in turn resulted in an increase in fiber rupture life by up to two orders of magnitude. TEM and AES microscopic observations are presented to indicate that these improvements can be correlated with the replacement of weak grain boundary phases with stronger phases that hinder grain boundary sliding more effectively. SiC/SiC composite results are also provided to show the advantages of the Super Sylramic fiber types both for CMC fabrication and high temperature application.

Yun, H. M.↗

NASA NTRS2004

Thermo-Mechanical Properties of SiC/SiC Composites with Hybrid CVI-PIP Matrices

For long term structural service, the upper temperature capability for slurry-cast melt infiltrated (MI) SiC/SiC composites is limited to approx. 1315 C because of silicon reaction with the SiC fibers. For applications requiring material temperatures in excess of 1315 C, alternate methods of manufacturing the SiC matrices without silicon are being investigated, such as a hybrid combination of CVI and PIP. In this study, stacked fabric plies of Sylramic i-BN SiC fibers were coated with a CVI BN interface layer followed by a partial CVI SiC matrix. The remaining porosity in the SiC/SiC preforms was then infiltrated with silicon carbide matrix by PIP. Thermo-mechanical property measurements indicate that these composites are stable to 1700 C in inert environments under no load conditions for 100 h and under load conditions to 1450 C in air for 300 h. The advantages, disadvantages, and potential of this composite system for high temperature applications will be discussed.

Bhatt, R. T.↗

NASA NTRS2003

Fabrication And Evaluation Of Sic/Sic Tubes With Various Fiber Architectures

SiC/SiC composites are excellent material candidates for high temperature applications where the performance requirements are high strength, high creep-rupture resistance, high environmental durability, and high thermal conductivity. In the past, the NASA UEET program has demonstrated fabrication of high-performance SiC/SiC flat panels reinforced by Sylramic-iBN SiC fibers. Currently NASA UEET is scaling up this SiC/SiC system by fabrication of more complex shaped components using the same fiber type. This paper reports the effects of various fiber architectures on the processing, mechanical, and durability behavior of small-diameter 0.5" ID SiC/SiC tubes, which are potential sub-elements for leading edges and cooling channels in turbine vanes and blades. Nine different fiber architectures were utilized for construction of seamless tube preforms, from simple 2D jelly-rolling to complex braiding, pin-weaving, filament-winding and 3D orthogonal weaving with approximately 5% fibers in the thru-thickness direction. Using the BN interphase and Sic matrix processing steps established for the flat panels, SiC/SiC tubes were fabricated with wall thicknesses of approximately 60 mils and total fiber fractions of approximately 35%. The "D" split ring tests for hoop tensile properties, micro-structural examinations for relationship between fiber architecture formation and matrix infiltration, and the low-pressure burner rig tests for the high temperature durability under thru-thickness thermal gradient were conducted. The better matrix infiltration and higher hoop strength were achieved using the tri-axial braided and the three-float pin woven SiC/SiC tubes. In general, it needs not only higher hoop direction fibers but also axial direction fibers for the higher hoop strength and the better infiltration, respectively. These results are analyzed to offer general guidelines for selecting fiber pre-form architectures and SiC/SiC processes that maximize tube hoop strength, thru-thickness thermal conductivity, and burner-rig durability under a high thermal gradient.

Yun, H. M.↗

NASA NTRS2002

Progress in SiC/SiC Ceramic Composite Development for Gas Turbine Hot-Section Components under NASA EPM and UEET Programs

The successful application of ceramic matrix composites as hot-section components in advanced gas turbine engines will require the development of constituent materials and processes that can provide the material systems with the key thermostructural properties required for long-term component service. Much initial progress in identifying these materials and processes was made under the former NASA Enabling Propulsion Materials Program using stoichiometric Sylramic (trademark) silicon-carbide (SiC) fibers, 2D (two dimensional)-woven fiber architectures, chemically vapor-infiltrated (CVI) BN fiber coatings (interphases), and SiC-based matrices containing CVI SiC interphase over-coatings, slurry-infiltrated SiC particulate, and melt-infiltrated (MI) silicon. The objective of this paper is to discuss the property benefits of this SiC/SiC composite system for high-temperature engine components and to elaborate on further progress in SiC/SiC development made under the new NASA Ultra Efficient Engine Technology Program. This progress stems from the recent development of advanced constituent materials and manufacturing processes, including specific treatments at NASA that improve the creep, rupture, and environmental resistance of the Sylramic fiber as well as the thermal conductivity and creep resistance of the CVI SiC over-coatings. Also discussed are recent observations concerning the detrimental effects of inadvertent carbon in the fiber-BN interfacial region and the beneficial effects of certain 2D-architectures for thin-walled SiC/SiC panels.

DiCarlo, J. A.↗

NASA NTRS1999

Thermomechanical Characterization of SiC Fiber Tows and Implications for CMC

In order to better understand SiC fiber behavior within CMC microstructures, mechanical tests were performed on multifilament tows consisting of different types of as produced and pretreated fibers. Tensile strengths of tows and single fibers were measured at room temperature for nonstoichiometric Hi-Nicalon and ZMI fibers and for stoichiometric Hi-Nicalon-S, Tyranno SA. and Sylramic fibers. Based on simple bundle theory, measured strengths for as-produced and sized tows were in general agreement with the single fiber results. However, after sizing removal under inert conditions, tow strengths for the coarser grained stoichiometric fibers were typically lower than those predicted from individual fiber data. This effect is attributed to enhanced fiber-fiber mechanical interaction caused by sizing removal from the rough surfaces of these fibers. In support of this, tow strengths remained high for those fiber types with fine grains or excess surface carbon; and, when re-coated with a BN interphase coating, tow strengths for the coarser grained fibers returned to their as-produced values. When the tows were pretreated in air at intermediate temperatures, tow strengths decreased in a manner that could be correlated with the oxidation characteristics of each fiber type as measured by thermogravimetric analysis. The creep and rupture properties of Hi-Nicalon and Sylramic tows were also measured in air and argon from 1200 to 1400 C. Although displaying transient and environmental effects similar to single fibers, the tows crept faster at short times and slower at long times. This resulted in the tow rupture strengths at long time being much greater than the rupture strengths of single fibers. The CMC implications of the tow results are discussed, as well as the benefits and limitations of tow testing.

Yun, H. M.↗

NASA NTRS1999

Comparison of the Tensile, Creep, and Rupture Strength Properties of Stoichiometric SiC Fibers

Tensile strength, creep strength, and rupture strength properties were measured for the following types of polymer-derived stoichiometric SiC fibers: Hi-Nicalon Type S from Nippon Carbon, Tyranno SA from Ube, and Sylramic from Dow Corning. Also included in this study were an earlier version of the SA fiber plus two recent developmental versions of the Sylramic fiber. The tensile strength measurements were made at room temperature on as-received fibers and on fibers after high-temperature inert exposure. The creep-rupture property data were obtained at 1400 deg C in air as well as, argon. Some fiber types showed strong effects of environment on their strength properties. These results are compared and discussed in terms of underlying mechanisms and implications for ceramic composites.

Yun, H. M.↗

NASA NTRS1999

Factors Controlling Stress Rupture of Fiber-Reinforced Ceramic Composites

The successful application of fiber-reinforced ceramic matrix composites (CMC) depends strongly on maximizing material rupture life over a wide range of temperatures and applied stresses. The objective of this paper is to examine the various intrinsic and extrinsic factors that control the high-temperature stress rupture of CMC for stresses below and above those required for cracking of the 0 C plies (Regions I and II, respectively). Using creep-rupture results for a variety of ceramic fibers and rupture data for CMC reinforced by these fibers, it is shown that in those cases where the matrix carries little structural load, CMC rupture conditions can be predicted very well from the fiber behavior measured under the appropriate test environment. As such, one can then examine the intrinsic characteristics of the fibers in order to develop design guidelines for selecting fibers and fiber microstructures in order to maximize CMC rupture life. For those cases where the fiber interfacial coatings are unstable in the test environment, CMC lives are generally worse than those predicted by fiber behavior alone. For those cases where the matrix can support structural load, CMC life can even be greater provided matrix creep behavior is properly controlled. Thus the achievement of long CMC rupture life requires understanding and optimizing the behavior of all constituents in the proper manner.

DiCarlo, J. A.↗

NASA NTRS1998

Annealing Effects on Creep and Rupture of Polycrystalline Alumina-Based Fibers

Continuous-length polycrystalline aluminum-oxide-based fibers are being considered as reinforcements for advanced high-temperature composite materials. For these fine-grained fibers, basic issues arise concerning grain growth and microstructural instability during composite fabrication and the resulting effects on the fiber's thermo-mechanical properties. To examine these issues, commercially available Nextel 610 (alumina) and Altex (alumina-silica) fibers were annealed at 1100 and 1300 C for up to 100 hr in air. Changes in fiber microstructure, fiber tensile creep, stress rupture, and bend stress relaxation (BSR) that occurred with annealing were then determined. BSR tests were also used to compare as-received and annealed fibers to other polycrystalline oxide fibers. Annealing was shown to have a significant effect, particularly on the Altex fiber, and caused it to have increased creep resistance.

Goldsby, J. C.↗

NASA NTRS1997

Creep and Rupture Strength of an Advanced CVD SiC Fiber

In the as-produced condition the room temperature strength (approx. 6 GPa) of Textron Specialty Materials' 50 microns CVD SiC fiber represents the highest value thus far obtained for commercially produced polycrystalline SiC fibers. To understand whether this strength can be maintained after composite processing conditions, high temperature studies were performed on the effects of time, stress, and environment on 1400 deg. C tensile creep strain and stress rupture on as-produced, chemically vapor deposited SiC fibers. Creep strain results were consistent, allowing an evaluation of time and stress effects. Test environment had no influence on creep strain but I hour annealing at 1600 deg. C in argon gas significantly reduced the total creep strain and increased the stress dependence. This is attributed to changes in the free carbon morphology and its distribution within the CVD SiC fiber. For the as-produced and annealed fibers, strength at 1400 deg. C was found to decrease from a fast fracture value of 2 GPa to a 100-hr rupture strength value of 0. 8 GPa. In addition a loss of fast fracture strength from 6 GPa is attributed to thermally induced changes in the outer carbon coating and microstructure. Scatter in rupture times made a definitive analysis of environmental and annealing effects on creep strength difficult.

Goldsby, J. C.↗