Reviving the rock-salt phases in Ni-rich layered cathodes by mechano-electrochemistry in all-solid-state batteries

The rock-salt phase (RSP) formed on the surface of Ni-rich layered cathodes in liquid-electrolyte lithium-ion batteries is conceived to be electrochemically "dead". Here we show massive RSP forms in the interior of LiNi x Mn y Co (1–x-y) O 2 (NMC) crystals in sulfide based all solid state batteries (ASSBs), but the RSP remains electrochemically active even after long cycles. The RSP and the layered structure constitute a two-phase mixture, a material architecture that is distinctly different from the RSP in liquid electrolytes. The tensioned layered phase affords an effective percolation channel into which lithium is squeezed out of the RSPs by compressive stress, rendering the RSPs electrochemically active. Consequently, the ASSBs with predominant RSP in the NMC cathode deliver remarkable long cycle life of 4000 cycles at high areal capacity of 4.3 mAh/cm 2 . Our study unveils distinct mechano-electrochemistry of RSPs in ASSBs that can be harnessed to enable high energy density and durable ASSBs.

25 ENERGY STORAGE↗

DOE OSTI2021

Degradation by Kinking in Layered Cathode Materials

Layered cathode materials are commonly used in lithium and sodium ion batteries, but they are prone to degradation under electrochemical cycling during battery operation. Here we report a new type of degradation mechanism through the electrochemically induced mechanical buckling and delamination cracking of intercalation layers in a P2 Na 0.7 -Ni 0.3 Mn 0.6 Co 0.1 O 2 (Na-NMC) cathode material. Kinks form in the delaminated layers due to severe local bending, and each kink consists of a vertical array of dislocations, resulting from an easy slip between transition metal oxide layers. In situ mechanical compression experiments directly reveal the kink formation due to strong mechanical anisotropy parallel and perpendicular to the intercalation layers in single-crystal Na-NMC. In situ electrochemical experiments indicate that kinks form during the desodiation process. Our results unveil a new mechanism of electrochemically induced mechanical degradation stemming from weak interlayer bonding in layered cathode materials. In conclusion, this work has broad implications for the mitigation of degradation associated with irreversible interlayer slip in layered cathode materials.

25 ENERGY STORAGE↗