Deadmore, D. L.

Publications and source records attributed to Deadmore, D. L..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1987

Effect of alloy composition on the sodium-sulfate induced hot corrosion attack of cast nickel-base superalloys at 900 C

The effects of Cr, Al, Ti, Mo, Ta, Nb, and W content on the hot corrosion of Ni-base alloys were examined experimentally. The superalloys were tested for 300 1-hr cycles at 900 C in a Mach 0.3 burner rig flame containing 0.5 ppmw sodium. The data reveal that the best corrosion resistance is obtained when the Cr content is greater than 12 percent; however, good resistance is detected in some alloys with Cr content less than 10 percent provided that the Al content is less than 2.5 wt pct and the Ti content is less than 4 wt pct. It is observed that the influence of W, Ta, Mo, and Nb content on resistance is dependent on Al and Ti contents. The derivation of an equation for estimating hot corrosion attack as a function of alloy composition using multiple linear regression analysis is described. The applicability of the equation is tested using various data sets of alloys. It is noted that the equation can be used to explain the effects of alloy composition on attack rates.

Stearns, C. A.↗
NASA NTRS1986

Digital Control of Durability-Testing Burner Rigs

Report describes hardware and software that implement hybrid digital control of two Jet A-1 fueled, mach-0.3 burners from startup to completion of preset number of hot-corrosion/flame-durability cycle tests of materials at 1,652 degree F (900 degree C). Surface temperatures controlled more precisely than before.

Deadmore, D. L.↗
NASA NTRS1986

Characterization of the tribological coating composition 77 wt % CaF2 - 23 wt % Li F fused to IN-750 alloy

A coating composed of 77 wt % CaF2 - 23 wt % LiF fused on IN-750 nickel-based alloy was studied using SEM, XRD, EDX, and optical microscopic methods. The surfaces examined were the as-fused coating with no subsequent treatment, the coating after ultrasonic cleaning in water, and the uncoated polished and etched metal. It was found that the coating reacts during fusion with Ti and Nb rich inclusions in the alloy. Numerous small rectangular crystallites of Ca(Ti,Nb) oxide are formed beneath an overlay of fused fluoride composition. These crystallines are stubby and appear to be embedded in the metal substrate surface. It is known from previous studies that this coating-alloy system has good tribological properties in extreme conditions, such as liquid fluorine. It has been concluded from the present study that the short firmly embedded crystalline protuberances contribute to the coating adherence and thereby to enhanced coating wear life.

Deadmore, D. L.↗
NASA NTRS1985

Digital temperature and velocity control of mach 0.3 atmospheric pressure durability testing burner rigs in long time, unattended cyclic testing

Hardware and software were developed to implement the hybrid digital control of two Jet A-1 fueled Mach 0.3 burners from startup to completion of a preset number of hot corrosion flame durability cycle tests of materials at 1652 F. This was accomplished by use of a basic language programmable microcomputer and data aquisition and control unit connected together by the IEEE-488 Bus. The absolute specimen temperature was controlled to + or - 3 F by use of digital adjustment of the fuel flow using a P-I-D (Proportional-Integral-Derivative) control algorithm. The specimen temperature was within + or - 2 F of the set point more than 90 percent of the time. Pressure control was achieved by digital adjustment of the combustion air flow using a proportional control algorithm. The burner pressure was controlled at 1.0 + or - 0.02 psig. Logic schemes were incorporated into the system to protect the test specimen from abnormal test conditions in the event of a hardware of software malfunction.

Deadmore, D. L.↗
NASA NTRS1984

Effects of alloy composition on cyclic flame hot-corrosion attack of cast nickel-base superalloys at 900 deg C

The effects of Cr, Al, Ti, Mo, Ta, Nb, and W content on the hot corrosion of nickel base alloys were investigated. The alloys were tested in a Mach 0.3 flame with 0.5 ppmw sodium at a temperature of 900 C. One nondestructive and three destructive tests were conducted. The best corrosion resistance was achieved when the Cr content was 12 wt %. However, some lower-Cr-content alloys ( 10 wt%) exhibited reasonable resistance provided that the Al content alloys ( 10 wt %) exhibited reasonable resistance provided that the Al content was 2.5 wt % and the Ti content was Aa wt %. The effect of W, Ta, Mo, and Nb contents on the hot-corrosion resistance varied depending on the Al and Ti contents. Several commercial alloy compositions were also tested and the corrosion attack was measured. Predicted attack was calculated for these alloys from derived regression equations and was in reasonable agreement with that experimentally measured. The regression equations were derived from measurements made on alloys in a one-quarter replicate of a 2(7) statistical design alloy composition experiment. These regression equations represent a simple linear model and are only a very preliminary analysis of the data needed to provide insights into the experimental method.

Deadmore, D. L.↗
NASA NTRS1984

In-situ measurements of alloy oxidation/corrosion/erosion using a video camera and proximity sensor with microcomputer control

Two noncontacting and nondestructive, remotely controlled methods of measuring the progress of oxidation/corrosion/erosion of metal alloys, exposed to flame test conditions, are described. The external diameter of a sample under test in a flame was measured by a video camera width measurement system. An eddy current proximity probe system, for measurements outside of the flame, was also developed and tested. The two techniques were applied to the measurement of the oxidation of 304 stainless steel at 910 C using a Mach 0.3 flame. The eddy current probe system yielded a recession rate of 0.41 mils diameter loss per hour and the video system gave 0.27.

Deadmore, D. L.↗
NASA NTRS1984

Application of induction coil measurements to the study of superalloy hot corrosion and oxidation

The assessment of the degree of hot corrosion attack on nickel based alloys is a difficult task, especially when the definition specifies that it must be in terms of metal consumed and even more difficult if the measurement must be nondestructive. The inductance of a solenoid coil responds to changes in volume of fill and composition of metal cores, therefore, it may be used for nondestructive measurement of hot corrosion. The hot corrosion of U700 was studied at 900 C in a Mach 0.3 flame doped with 0.85 wppm of sodium. The change of inductance was found to define the known corrosion behavior and to suggest its use as a tool with predictive capabilities. Sufficient sensitivity exists to detect oxidation of this alloy at 900 C.

Deadmore, D. L.↗
NASA NTRS1983

Silicon-slurry/aluminide coating

A low cost coating protects metallic base system substrates from high temperatures, high gas velocity ovidation, thermal fatigue and hot corrosion and is particularly useful fo protecting vanes and blades in aircraft and land based gas turbine engines. A lacquer slurry comprising cellulose nitrate containing high purity silicon powder is sprayed onto the superalloy substrates. The silicon layer is then aluminized to complete the coating. The Si-Al coating is less costly to produce than advanced aluminides and protects the substrates from oxidation and thermal fatigue for a much longer period of time than the conventional aluminide coatings. While more expensive Pt-Al coatings and physical vapor deposited MCrAlY coatings may last longer or provide equal protection on certain substrates, the Si-Al coating exceeded the performance of both types of coatings on certain superalloys in high gas velocity oxidation and thermal fatigue and increased the resistance of certain superalloys to hot corrosion.

Deadmore, D. L.↗
NASA NTRS1983

Burner rig study of variables involved in hole plugging of air cooled turbine engine vanes

The effects of combustion gas composition, flame temperatures, and cooling air mass flow on the plugging of film cooling holes by a Ca-Fe-P-containing deposit were investigated. The testing was performed on film-cooled vanes exposed to the combustion gases of an atmospheric Mach 0.3 burner rig. The extent of plugging was determined by measurement of the open hole area at the conclusion of the tests as well as continuous monitoring of some of the tests using stop-action photography. In general, as the P content increased, plugging rates also increased. The plugging was reduced by increasing flame temperature and cooling air mass flow rates. At times up to approximately 2 hours little plugging was observed. This apparent incubation period was followed by rapid plugging, reaching in several hours a maximum closure whose value depended on the conditions of the test.

Deadmore, D. L.↗
NASA NTRS1982

Long-term high-velocity oxidation and hot corrosion testing of several NiCrAl and FeCrAl base oxide dispersion strengthened alloys

Several oxide dispersion strengthened (ODS) alloys have been tested for cyclic, long-term, high gas-velocity resistance to oxidation at 1100 C and hot corrosion at 900 C. Both nominally Ni-16Cr-4Al and Fe-20Cr-4.5Al ODS alloys were subjected up to about 2500 cycles, where each cycle consisted of 1 hr in a hot, Mach 0.3 combusted gas stream followed by a 3-min quench in an ambient temperature, Mach 0.3 air blast. For comparison to existing technology, a coated superalloy was simultaneously tested. The ODS iron alloy exhibited clearly superior behavior, surviving 3800 oxidation and 2300 hot corrosion cycles essentially unscathed. While the ODS nickel alloys exhibited adequate oxidation resistance, the long-term hot corrosion resistance could be marginal, since the best life for such alloys under these conditions was only about 1100 cycles. However, the hot corrosion resistance of the ODS Ni-base alloys is excellent in comparison to that of traditional superalloys.

Lowell, C. E.↗
NASA NTRS1982

Method of protecting a surface with a silicon-slurry/aluminide coating

A low cost coating for protecting metallic base system substrates from high temperatures, high gas velocity oxidation, thermal fatigue and hot corrosion is described. The coating is particularly useful for protecting vanes and blades in aircraft and land based gas turbine engines. A lacquer slurry comprising cellulose nitrate containing high purity silicon powder is sprayed onto the superalloy substrates. The silicon layer is then aluminized to complete the coating. The Si-Al coating is less costly to produce than advanced aluminides and protects the substrate from oxidation and thermal fatigue for a much longer period of time than the conventional aluminide coatings. While more expensive Pt-Al coatings and physical vapor deposited MCrAlY coatings may last longer or provide equal protection on certain substrates, the Si-Al coating exceeded the performance of both types of coatings on certain superalloys in high gas velocity oxidation and thermal fatigue. Also, the Si-Al coating increased the resistance of certain superalloys to hot corrosion.

Deadmore, D. L.↗
NASA NTRS1981

High temperature alkali corrosion in high velocity gases

The effects of potential impurities in coal derived liquids such as Na, K, Mg, Ca and Cl on the accelerated corrosion of IN-100, U-700, IN-792 and Mar-M509 were investigated using a Mach 0.3 burner rig for times to 1000 hours in one hour cycles. These impurities were injected in combination as aqueous solutions into the combustor of the burner rig. The experimental matrix utilized was designed statistically. The extent of corrosion was determined by metal recession. The metal recession data were fitted by linear regression to a polynomial expression which allows both interpolation and extrapolation of the data. As anticipated, corrosion increased rapidly with Na and K, and a marked maximum in the temperature response was noted for many conditions. In contrast, corrosion decreased somewhat as the Ca, Mg and Cl contents increased. Extensive corrosion was observed at concentrations of Na and K as low as 0.1 PPM at long times.

Lowell, C. E.↗
NASA NTRS1981

Low cost high temperature, duplex coating for superalloys

Duplex silicon-slurry/aluminide coating substantially improves high temperature resistance to oxidation and corrosion of nickel base alloys. Coating used in critical sections of power systems like turbojet engines extends their operating capabilities.

Young, S. G.↗
NASA NTRS1980

Fouling and the inhibition of salt corrosion

In an attempt to reduce fouling while retaining the beneficial effects of alkaline earth inhibitors on the hot corrosion of superalloys, the use of both additives and the intermittent application of the inhibitors were evaluated. Additions of alkaline earth compounds to combustion gases containing sodium sulfate were shown to inhibit hot corrosion. However, sulfate deposits can lead to turbine fouling in service. For that reason, dual additives and intermittant inhibitor applications were evaluated to reduce such deposit formation. Silicon in conjunction with varium showed some promise. Total deposition was apparently reduced while the inhibition of hot corrosion by barium was unimpaired. The intermittant application of the inhibitor was found to be more effective and controllable.

Deadmore, D. L.↗
NASA NTRS1980

An experimental, low-cost, silicon-aluminide high-temperature coating for superalloys

A duplex silicon-slurry/aluminide coating has been developed and cyclically tested in Mach 1 combustion gases for oxidation and thermal fatigue resistance at 1093 C and Mach 0.3 gases and hot-corrosion resistance at 900 C. The base-metal superalloys were VIA and B-1900. The coated B-1900 specimens were found to perform much better in oxidation than similar specimens coated with aluminides, and almost as well as the more expensive Pt-Al and MCrAlY (where M is Ni and/or Co) coatings deposited by the physical vapor deposition process. The coatings also provided good hot-corrosion protection.

Young, S. G.↗
NASA NTRS1980

Effects of impurities in coal-derived liquids on accelerated hot corrosion of superalloys

A Mach 0.3 burner rig was used to determine the effects of potential coal derived liquid fuel impurity combustion of products on hot corrosion in IN-100, IN-792, IN_738, U-700, Mar M-509, and 304 stainless steel. The impurities, added as aqueous solutions to the combustor, were salts of sodium, potassium, vanadium, molybdenum, tungsten, phosphorus, and lead. Extent of attack was determined by metal consumption and compared to the effects of sodium alone. Vanadium, molybdenum, tungsten, phosphorous, and lead in combination with sodium all resulted in increased attack as compared with sodium alone at some temperatures, apparently due in large part to the extension of the formation of liquid deposits. Varying the sodium-potassium ratio had little effect for ratios less than 1:3 for which reduced, but measurable, attack was observed.

Deadmore, D. L.↗
NASA NTRS1980

Effect of sodium, potassium, magnesium, calcium, and chlorine on the high temperature corrosion of IN-100, U-700, IN-792, and Mar M-509

The effects of potential impurities such as Na, K, Mg, Ca, and Cl, in coal-derived liquid fuels on accelerated corrosion of IN-100, U-700, IN-792, and Mar M-509 were investigated using a Mach 0.3 burner rig for times to 200 hours in one hour cycles. These impurities were injected in combination as aqueous solutions into the combustor. Other variables were time, temperature, and fuel-to-air ratio. The experimental matrix was a central composite fractional fractorial design divided into blocks to allow modification of the design as data was gathered. The extent of corrosion was determined by metal consumption. The time exponent was near 1.0 for the least corrosion resistant alloys, U-700 and IN-100; near 0.8 for the moderately resistant IN-792; and close to Mar M-509, the most corrosion resistant alloy. As anticipated, corrosion rapidly increased with increasing temperature as well as Na and K concentrations, while corrosion decreased somewhat as the Ca concentration increased for all alloys. Mg was beneficial for the Ni-base alloys but had little effect on the Co-base alloy. Surprisingly, the effect of increasing Cl was to decrease the corrosion of all alloys. Little interaction among the dopants was noted.

Lowell, C. E.↗