Engineering topics

Dawicke, D. S.

Publications and source records attributed to Dawicke, D. S..

34 records · Page 2

NASA NTRS1993

A fracture criterion for widespread cracking in thin-sheet aluminum alloys

An elastic-plastic finite-element analysis was used with a critical crack-tip-opening angle (CTOA) fracture criterion to model stable crack growth in thin-sheet 2024-T3 aluminum alloy panels with single and multiple-site damage (MSD) cracks. Comparisons were made between critical angles determined from the analyses and those measured with photographic methods. Calculated load against crack extension and load against crack-tip displacement on single crack specimens agreed well with test data even for large-scale plastic deformations. The analyses were also able to predict the stable tearing behavior of large lead cracks in the presence of stably tearing MSD cracks. Small MSD cracks significantly reduced the residual strength for large lead cracks.

Newman, J. C., Jr.↗

NASA NTRS1992

Analysis and prediction of Multiple-Site Damage (MSD) fatigue crack growth

A technique was developed to calculate the stress intensity factor for multiple interacting cracks. The analysis was verified through comparison with accepted methods of calculating stress intensity factors. The technique was incorporated into a fatigue crack growth prediction model and used to predict the fatigue crack growth life for multiple-site damage (MSD). The analysis was verified through comparison with experiments conducted on uniaxially loaded flat panels with multiple cracks. Configuration with nearly equal and unequal crack distribution were examined. The fatigue crack growth predictions agreed within 20 percent of the experimental lives for all crack configurations considered.

Dawicke, D. S.↗

NASA NTRS1992

Finite-element analyses and fracture simulation in thin-sheet aluminum alloy

A two-dimensional, elastic-plastic finite-element analysis was used with a critical crack-tip-opening angle (CTOA) fracture criterion to model stable crack growth in thin-sheet 2024-T3 aluminum alloy under monotonic loading after precracking at different cyclic stress levels. Tests were conducted on three types of specimens: middle-crack, three-hole-crack and blunt-notch tensile specimens. An experiment technique was developed to measure CTOA during crack growth initiation and stable tearing using a high-resolution video camera and recorder. Crack front shapes were also measured during initiation and stable tearing using a fatigue marker-load technique. Three-dimensional elastic-plastic finite-element analyses of these crack shapes for stationary cracks were conducted to study the crack-front opening displacements. Predicted load against crack extension on middle-crack tension specimens agreed well with test results even for large-scale plastic deformations. The analyses were able to predict the effects of specimen size and precracking stress history on stable tearing. Predicted load against load-line displacements agreed well with test results up to maximum load bu the analyses tended to overpredict displacements as crack grew beyond the maximum load under displacement-controlled conditions. During the initiation phase, the measured CTOA values were high but decreased and remained nearly constant after a small amount of stable tearing. The constant value of CTOA agree well with the calculated value from the finite-element analysis. The larger CTOA values measured at the sheet surface during the initiation phase may be associated with the crack tunneling observed in the tests. Three-dimensional analyses for nonstraight crack fronts predicted much higher displacements near the free surface than in the interior.

Newman, J. C., Jr.↗

NASA NTRS1992

An inverse method for the calculation of through-thickness fatigue crack closure behavior

An inverse technique was used to calculate through-thickness fatigue crack closure behavior. The through-thickness variation in crack opening stress-intensity factor was calculated by considering the variation in the three-dimensional stress-intensity factor, the variation in crack growth rate along the crack front, and a relationship between the crack growth rate and effective stress-intensity factor range (da/dN-Delta-K(eff)). The three-dimensional stress-intensity factor variation was obtained from an elastic finite element analysis of specific crack-front profiles observed experimentally. The variation in crack growth rate along the crack front was obtained experimentally from comparison of observed crack front changes. The da/dN-Delta-K(eff) relationship was estimated from high stress ratio, constant load amplitude, and fatigue crack growth tests. The through-thickness crack opening stress-intensity factor results agreed with crack opening measurements obtained from fatigue striations, near-tip strain gages, and remote strain and displacement gages.

Dawicke, D. S.↗

NASA NTRS1991

An evaluation of the pressure proof test concept for 2024-T3 aluminium alloy sheet

The concept of pressure proof testing of fuselage structures with fatigue cracks to insure structural integrity was evaluated from a fracture mechanics viewpoint. A generic analytical and experimental investigation was conducted on uniaxially loaded flat panels with crack configurations and stress levels typical of longitudinal lap splice joints in commercial transport aircraft fuselages. The results revealed that the remaining fatigue life after a proof cycle was longer than that without the proof cycle because of crack growth retardation due to increased crack closure. However, based on a crack length that is slightly less than the critical value at the maximum proof stress, the minimum assured life or proof test interval must be no more than 550 pressure cycles for a 1.33 proof factor and 1530 pressure cycles for a 1.5 proof factor to prevent in-flight failures.

Dawicke, D. S.↗

NASA NTRS1990

An evaluation of the pressure proof test concept for thin sheet 2024-T3

The concept of pressure proof testing of fuselage structures with fatigue cracks to insure structural integrity was evaluated from a fracture mechanics viewpoint. A generic analytical and experimental investigation was conducted on uniaxially loaded flat panels with crack configurations and stress levels typical of longitudinal lap-splice joints in commercial transport aircraft fuselage. The results revealed that the remaining fatigue life after a proof test was longer than that without the proof test because of crack growth retardation due to increased crack closure. However, based on a crack length that is slightly less than the critical value at the maximum proof test stress, the minimum assured life or proof test interval must be no more than 550 pressure cycles for a 1.33 proof factor and 1530 pressure cycles for a 1.5 proof factor to prevent in-flight failures.

Dawicke, D. S.↗

NASA NTRS1990

An evaluation of the pressure proof test concept for thin sheet 2024-T3

The concept of pressure proof testing of fuselage structures with fatigue cracks to insure structural integrity was evaluated from a fracture mechanics viewpoint. A generic analytical and experimental investigation was conducted on uniaxially loaded flat panels with crack configurations and stress levels typical of longitudinal lap splice joints in commercial transport aircraft fuselages. The results revealed that the remaining fatigue life after a proof test was longer than that without the proof test because of crack growth retardation due to increased crack closure. However, based on a crack length that is slightly less than the critical value at the maximum proof test stress, the minimum assured life or proof test interval must be no more than 550 pressure cycles for a 1.33 proof factor and 1530 pressure cycles for a 1.5 proof factor to prevent in-flight failures.

Dawicke, D. S.↗

NASA NTRS1990

Through-the-thickness fatigue crack closure behavior in an aluminum alloy

The variation in fatigue crack closure behavior across the thickness of aluminum alloy specimens was investigated. The specimen geometries examined were the middle crack tension M(T) and compact tension C(T). The fatigue crack closure behavior was determined using remote displacement and strain gages, near tip strain gages, and fatigue striations. A hybrid experimental/numerical method was also used to infer the crack opening loads. The results indicate a variation in crack opening load, of 0.2 in the specimen interior to 0.4 to 0.5 at the surface.

Dawicke, D. S.↗

NASA NTRS1990

Three-dimensional crack closure behavior

A crack closure measurement technique involving fatigue striations was used to produce a three-dimensional crack opening load profile for 2024-T351 aluminum alloy. The crack opening load profile, determined through the specimen thickness, was compared with crack opening load measurements made with strain gages and displacement gages. The results of this study indicate that a significant three-dimensional variation in crack closure behavior occurs in the alloy examined. An understanding of this phehomenon is important in understanding crack growth behavior, predicting crack shape changes, and interpreting 'standard' crack closure measurement techniques.

Dawicke, D. S.↗

NASA NTRS1990

Through-the-thickness fatigue crack closure behavior in an aluminum alloy

Dawicke, D. S.↗

NASA NTRS1990

Proof test and fatigue crack growth modeling on 2024-T3 aluminum alloy

Pressure proof testing of aircraft fuselage structures has been suggested as a means of screening critical crack sizes and of extending their useful life. The objective of this paper is to study the proof-test concept and to model the crack-growth process on a ductile material. Simulated proof and operational fatigue life tests have been conducted on cracked panels made of 2024-T3 aluminum alloy sheet material. A fatigue crack-closure model was modified to simulate the proof test and operational fatigue cycling. Using crack-growth rate and resistance-curve data, the model was able to predict crack growth during and after the proof load. These tests and analyses indicate that the proof test increases fatigue life; but the beneficial life, after a 1.33 or 1.5 proof, was less than a few hundred cycles.

Newman, J. C., Jr.↗

NASA NTRS1989

Prediction of fatigue-crack growth in a high-strength aluminum alloy under variable-amplitude loading

The present paper is concerned with the application of an analytical crack-closure model to study crack growth under various load histories. The model was based on a concept like the Dugdale model, but modified to leave plastically deformed material in the wake of the advancing crack tip. The thickness effect was accounted for by using a 'constraint' factor on tensile yielding at the crack tip. The model was used to correlate crack-growth rates under constant-amplitude loading, and to predict crack growth under variable-amplitude loading on a high-strength aluminum alloy (7475-T7351) sheet material. The experimental data was obtained from Zhang et al. Predicted crack-growth lives agreed well with experimental data. For ten crack-growth tests subjected to various variable-amplitude load histories, the ratio of predicted-to-experimental lives ranged from 0.54 to 1.19. The mean value of predicted-to-experimental lives was 0.95 with a standard error of 0.2 for a constraint factor of 1.9.

Newman, J. C., Jr.↗

NASA NTRS1989

Prediction of fatigue-crack growth in a high-strength aluminum alloy under variable-amplitude loading

The present paper is concerned with the application of an analytical crack-closure model to study crack growth under various load histories. The model was based on a crack-tip plasticity concept like the Dugdale model, but modified to leave plastically deformed material in the wake of the advancing crack tip. The effect of material thickness on plasticity was accounted for by using a constraint factor on tensile yielding at the crack tip. The model was used to correlate crack-growth rates under constant-amplitude loading, and to predict crack growth under variable-amplitude loading on a high-strength aluminum alloy (7475-T7351) sheet material. The experimental data were obtained from Zhang et al. Predicted crack-growth lives agreed well with experimental data. For ten crack-growth tests subjected to various variable-amplitude load histories, the ratio of predicted-to-experimental lives ranged from 0.54 to 1.19. The mean value of the ratio of predicted-to-experimental lives was 0.95 and the standard error was 0.2 using a constraint factor of 1.9 in the model. Crack-opening stresses calculated from the model were significantly different from those determined by Zhang et al. using a striation-based experimental method.

Newman, J. C., Jr.↗

NASA NTRS1983

A total life prediction model for stress concentration sites

Fatigue crack growth tests were performed on center crack panels and radial crack hole samples. The data were reduced and correlated with the elastic parameter K taking into account finite width and corner crack corrections. The anomalous behavior normally associated with short cracks was not observed. Total life estimates for notches were made by coupling an initiation life estimate with a propagation life estimate.

Hartman, G. A.↗

NASA NTRS1983

A total life prediction model for stress concentration sites

Fatigue crack growth tests were performed on center crack panels and radial crack hole samples. The data were reduced and correlated with the elastic parameter-K taking into account finite width and corner crack corrections. The anomalous behavior normally associated with short cracks was not observed. Total life estimates for notches were made by coupling an initiation life estimate with a propagation life estimate.

Hartman, G. A.↗

NASA NTRS1982

A preliminary study of crack initiation and growth at stress concentration sites

Crack initiation and propagation models for notches are examined. The Dowling crack initiation model and the E1 Haddad et al. crack propagation model were chosen for additional study. Existing data was used to make a preliminary evaluation of the crack propagation model. The results indicate that for the crack sizes in the test, the elastic parameter K gave good correlation for the crack growth rate data. Additional testing, directed specifically toward the problem of small cracks initiating and propagating from notches is necessary to make a full evaluation of these initiation and propagation models.

Dawicke, D. S.↗