Engineering topics
Publications and source records attributed to Davis, G. D..
Report describes tests conducted to assess use of bondable stainless surface (BOSS) coating materials to protect steel cases of solid-fuel rocket motors against corrosion and to provide surface microstructure and chemistry suitable for bonding to insulating material. Eliminates need to cover cases with grease to prevent corrosion and degreasing immediately prior to use.
Plasma-sprayed Bondable Stainless Surface (BOSS) coatings are being developed under the Solid Propulsion Integrity Program's (SPIP) Bondlines Package. These coatings are designed as a steel case preparation treatment prior to insulation lay-up. Other uses include the exterior of steel cases and bonding surfaces of nozzle components. They provide excellent bondability - rubber insulation and epoxy bonds fail cohesively within the polymer - for both fresh surfaces and surfaces having undergone natural and accelerated environmental aging. They have passed the MSFC requirements for protection of inland and sea coast environment. Because BOSS coatings are inherently corrosion resistant, they do not require preservation by greases or oils. The reduction/elimination of greases and oils, known bondline degraders, can increase SRM reliability, decrease costs by reducing the number of process steps, and decrease environmental pollution by reducing the amount of methyl chloroform used for degreasing and thus reduce release of the ozone-depleting chemical in accordance with the Clean Air Act and the Montreal Protocol. The coatings can potential extend the life of RSRM case segments and nozzle components by eliminating erosion due to multiple grit blasting during each use cycle and corrosion damage during marine recovery. Concurrent work for the Air Force show that other BOSS coatings give excellent bondline strength and durability for high-performance structures of aluminum and titanium.
An investigation is conducted of the mechanisms by which nitrilotris methylene phosphonic acid (NTMP) and related compounds are adsorbed onto oxidized aluminum surfaces to inhibit hydration and increase the durability of adhesive bonds formed with inhibitor-treated panels. P - O - Al bonds are identified as the basis of adsorption, and it is found that water initially adsorbed onto the etched aluminum surfaces is displaced by the NTMP. The hydration of the NTMP-treated surfaces occurs in three stages, namely the reverisble physisorption of water, the slow dissolution of NTMP followed by rapid hydration of the freshly exposed Al2O3 to AlOOH and further hydration of the surface to Al(OH)3. Five properties of an ideal inhibitor are identified.
An Ultrareliable, Fault-Tolerant, Control-System (UFTCS) concept is described using a systems design philosophy which allows development of system structures containing virtually no common elements. Common elements limit achievable system reliability and can cause catastrophic loss of fault-tolerant system function. The UFTCS concept provides the means for removing common system elements by permitting the elements of the system to operate as independent, uncoupled entities. Multiple versions of the application program are run on dissimilar hardware. Fault tolerance is achieved through the use of static redundancy management.