DOE OSTI2022

Perovskite grain wrapping by converting interfaces and grain boundaries into robust and water-insoluble low-dimensional perovskites

Stabilizing perovskite solar cells requires consideration of all defective sites in the devices. Substantial efforts have been devoted to interfaces, while stabilization of grain boundaries received less attention. Here, we report on a molecule tributyl(methyl)phosphonium iodide (TPI), which can convert perovskite into a wide bandgap one-dimensional (1D) perovskite that is mechanically robust and water insoluble. Mixing TPI with perovskite precursor results in a wrapping of perovskite grains with both grain surfaces and grain boundaries converted into several nanometer-thick 1D perovskites during the grain formation process as observed by direct mapping. The grain wrapping passivates the grain boundaries, enhances their resistance to moisture, and reduces the iodine released during light soaking. The perovskite films with wrapped grains are more stable under heat and light. The best device with wrapped grains maintained 92.2% of its highest efficiency after light soaking under 1-sun illumination for 1900 hours at 55°C open-circuit condition.

14 SOLAR ENERGY↗
DOE OSTI2022

Carbazole-Based Hole Transport Polymer for Methylammonium-Free Tin-Lead Perovskite Solar Cells with Enhanced Efficiency and Stability

As the most commonly used hole transport material (HTM) in tin-lead (Sn-Pb) perovskite solar cells (PSCs), poly(3,4-ethylenedioxythiophene) polystyrenesulfonate (PEDOT:PSS) limits the power conversion efficiency (PCE) and stability of the PSCs due to its acidic characteristics. Herein, an easily synthesized polymer HTM poly[(phenyl)imino[9-(2-ethylhexyl)carbazole]-2,7-diyl] (CzAn) with a shallow highest occupied molecular orbital (HOMO) level of -4.95 eV is used in a p-i-n structure, methylammonium-free, Sn-Pb PSC to replace PEDOT:PSS. Upon optimization using doping and surface engineering, high quality Sn-Pb PSCs could be successfully fabricated, boosting the PCE to 22.6% (stabilized PCE of 21.3%) compared with 21.2% for PEDOT:PSS. The perovskite films prepared on the modified CzAn HTM possess improved crystallinity, reduced trap-state density, and larger carrier mobility resulting in PSCs with greatly improved stability.

carrier mobility↗
DOE OSTI2022

Efficient monolithic all-perovskite tandem solar modules with small cell-to-module derate

All-perovskite tandem solar modules are promising to reduce the cost of photovoltaic systems with their high efficiency and solution fabrication, but their sensitivity to air still imposes a great challenge. Here a hot gas-assisted blading method is developed to accelerate the perovskite solidification, forming compact and thick narrow bandgap (NBG) perovskite films. Adding a reduction agent into NBG films followed by a short period of air exposure and a post-fabrication storage surprisingly increases carrier recombination lifetime and enables laser scribing in ambient conditions without obvious loss of device performance. This combination suppresses tin and iodide oxidation and forms a thin SnO 2 layer on the NBG film surface. Monolithic all-perovskite tandem solar modules showed a champion efficiency of 21.6% with a 14.3 cm 2 aperture area, corresponding to an active area efficiency of 23.0%. Lastly, the very small cell-to-module derate of 6.5% demonstrates the advantage of a tandem monolithic structure for solar modules.

14 SOLAR ENERGY↗
DOE OSTI2021

Stabilizing perovskite-substrate interfaces for high-performance perovskite modules

The interfaces of perovskite solar cells (PSCs) are important in determining their efficiency and stability, but the morphology and stability of imbedded perovskite-substrate interfaces have received less attention than have top interfaces. We found that dimethyl sulfoxide (DMSO), which is a liquid additive broadly applied to enhance perovskite film morphology, was trapped during film formation and led to voids at perovskite-substrate interfaces that accelerated the film degradation under illumination. Partial replacement of DMSO with solid-state carbohydrazide reduces interfacial voids. A maximum stabilized power conversion efficiency (PCE) of 23.6% was realized for blade-coated p-type/intrinsic/n-type (p-i-n) structure PSCs with no efficiency loss after 550-hour operational stability tests at 60°C. The perovskite mini-modules showed certified PCEs of 19.3 and 19.2%, with aperture areas of 18.1 and 50.0 square centimeters, respectively.

Chen, Shangshang↗
DOE OSTI2021

Highly Efficient Pure‐Blue Light‐Emitting Diodes Based on Rubidium and Chlorine Alloyed Metal Halide Perovskite

Abstract Perovskite light‐emitting diodes (PeLEDs) are promising candidates for display and solid‐state lighting, due to their tunable colors, high conversion efficiencies, and low cost. However, the performance of blue PeLEDs is far inferior to that of the near‐infrared, red, and green counterparts. Here, the fabrication of pure‐blue PeLEDs with an emission peak at 475 nm, a peak external quantum efficiency of 10.1%, and a maximum luminance of 14 000 cd m −2 is demonstrated by tailoring the compositions of perovskites. The pure‐blue electroluminescence is achieved by simultaneous addition of rubidium and chlorine ions into CsPbBr 3 and incorporation of phenylethylammonium chloride forms quasi‐2D hybrid perovskites. The combination of these composition engineering results in blueshifted emissions without reducing the quantum yield. The judicious alloying is shown to be critical to result in the better morphology with suppressed current leakage and enhanced light outcoupling.

Yang, Yang↗