DOE OSTI2024

Intern Poster

Digital Image Correlation (DIC) is an optical technique that combines image registration and tracking methods for accurate two-dimensional and three-dimensional changes in images. DIC software can be used to track the contour, deformation, and strain of a sample. In the Advanced Test Reactor (ATR) at INL (Idaho National Laboratory) there exists a small working window of samples that can become irradiated. Hundreds of graphite disks called piggybacks have undergone this irradiation as part of the Advanced Reactor Technologies (ART) program. After irradiation, it is desirable to understand the change in tensile strength as a function of dose. Due to the limited space in the ATR, typical dog bone tensile tests reduce the number of graphite samples from hundreds to tens. However, there does exist an ASTM standard, D8289, which uses disc compression of graphite to estimate the tensile strength of the specimen with the Brazilian Disk test fixture. While only used as an estimate, which is typically off by a third, it is the purpose of this study to identify how to amend D8289 to remove the word "estimate" with the help of DIC.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Graphite Oxidation Activities

Graphite Oxidation Activities to include introduction, rate determination, strength after oxidation, penetration depth analysis, strategic partnership projects, and summary and continuing work.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Baseline Characterization Database Verification Report ? NBG-17 Billet V104

The purpose of this report is to present data collected in the Baseline Graphite Characterization Program, which is directly tasked with supporting the Idaho National Laboratory’s (INL’s) research and development efforts on the Advanced Reactor Technologies (ART) Program. This program populates a comprehensive database that reflects the baseline properties of nuclear-grade graphite regarding individual grade, billet, and position within individual billets. The physical- and mechanical-property information being collected will be transferred to the Nuclear Data Management and Analysis System (NDMAS), and that database will help populate the handbook of property data available to member nations of the Generation-IV International Forum. Transfer of these data from the applicable technical lead to the dissemination databases available to other end users requires a full review of the test procedures and data-collection efforts through an analysis of the multiple summary spreadsheets and values being collected. This report represents the analysis for NBG-17 Billet V104 and facilitates release of associated data to the NDMAS custodians. Millions of raw data points have been collected during testing and quantification analyses for these billets. The summary scalar property values and supplementary traceability data are collected into comprehensive spreadsheets. Data sets are composed of single billets of graphite for any given grade, organized by mechanical test-specimen type, and further subdivided into individual spreadsheet tabs according to the specific test or evaluation being performed. A direct analysis of properties was not conducted, and this report does not provide information on the validity or performance characteristics of the graphite itself. Rather, this report is intended as a verification of the completeness of actual data collected in accordance with PLN-3467, “Baseline Graphite Characterization Plan: Electromechanical Testing,” [1] and PLN-3348 “Graphite Mechanical Testing” [2] and their representation of the measurement and test results with sole regard to the graphite billets under evaluation.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Baseline Graphite Characterization

Presentation will include baseline graphite characterization information, such as purpose and results, baseline property measurements, baseline graphite characterization method, baseline progress, split disc tensile strength: ASTM Tensile Strength Alternative, Identification of proper split disk fracture, baseline graphite ASTM D8289, horizontal orientation, digital image correlation, and DIC Analyzation.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

A Study of a Surrogate Nuclear Thermal Propulsion Fuel Element

We report a surrogate fuel, Zirconium Carbide/Titanium Nitride has been prepared using a simple method to obtain a more uniform distribution of titanium nitride in the zirconium carbide matrix. Powders were sintered using Spark Plasma Sintering at 1750oC and 1850oC using a modified sintering profile. This resulted in a fairly uniform distribution of titanium nitride in the zirconium carbide matrix with a density of 95% of theoretical at 1850oC. Scanning electron microscopy, indentation hardness and x-ray diffraction results are given.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Creating Hydride Rim Structures in Zircaloy 4 Cladding Tubes to Mimic High Burnup

During their long service in commercial light water reactors, zirconium alloy cladding tubes are subject to oxidation and subsequent hydrogen pickup which can degrade the materials mechanical properties [1]. These degradations can lead to premature cladding ruptures during reactor power transients [2] as well as negatively impact the claddings post quench ductility following high temperature steam oxidation in thermal hydraulic transients [3]. Hydrogen has low solid solubility in zirconium and usually precipitates as brittle zirconium hydride platelets in the cladding metal matrix. Due to temperature driven diffusion (Soret effect) and the grain texture of stress relieved zirconium metal tubes, these hydrides precipitate with a circumferential orientation near the outer surface of the cladding tubes forming a hydride rim which can serve as a site for crack initiation during circumferential ‘hoop’ loading of the cladding [4rim formation][5]. In order to better understand the effect of hydride rims on the fracture behavior of stress relieved zirconium alloy cladding tubes a procedure to produce these rim-like structures is being developed at Idaho National Laboratory (INL).

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗