DOE OSTI2024

Tuning crosslinking of hybrid preceramic polymers in vat photopolymerization toward controlled ceramic yields

Control of preceramic polymer crosslinking for UV-curable processing is essential for fine 3D printing with high ceramic conversion for sustainable polymer-derived ceramics (PDC) engineering. While various factors influencing ceramic yield have been studied, the systematic exploration of the relationship between crosslinking and ceramic yield, especially when crosslinking increases volatile elements, remains open for further investigation. This study addresses this gap by utilizing vat photopolymerization (VP) additive manufacturing (AM) as a versatile platform for controlling preceramic crosslinking and ceramic yield. By rationally designing and tuning the photochemical crosslinking through digital light processing (DLP), we demonstrate that the ceramic yield can be enhanced from 64% to over 86%, even with added volatile elements. We reveal that the post-pyrolysis ceramic yield can be closely correlated with the pre-pyrolysis crosslinking of the preceramic network represented by its stiffness. This correlation thereby suggests a fast, energy-efficient, non-destructive methodology to predict and improve ceramic yield. Combined with these findings, our one-pot thiol-ene hybridization of polycarbosilane and polycarbosiloxane via DLP offers an exemplary method to generate hybrid preceramic polymers with tailored material properties toward target applications, and potentially even higher ceramic yields. This study thus contributes to achieving better resource- and energy-efficient preceramic polymer and PDC processing routes toward sustainable, advanced organic–inorganic materials manufacturing.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2024

Material selection and manufacturing for high‐temperature heat exchangers: Review of state‐of‐the‐art development, opportunities, and challenges

Abstract Many energy systems demand heat transfer at high temperatures to keep up with high demand for power, so high‐temperature material that can perform and last under these harsh conditions is needed for heat exchangers. The engineering requirements for these high‐temperature heat exchanger material call for high thermal conductivity, high resistance to fracture, high resistance to creep deformation, environmental stability in environments associated with the application, and high modulus of elasticity while maintaining low cost to make and maintain. Naturally, ceramics are a good solution for this endeavor. In the past, high‐temperature heat exchangers made from ceramics have been used. We provide examples of ceramics in relevant heat exchange applications and provide motivation where additive manufacturing (AM) can improve efficiency. AM for the relevant material is under development, and we provide insight on the AM of ceramic materials and examples of AM heat exchangers keeping cost in mind. The motivation of the review paper is to provide a framework for material and manufacturing selection for high‐temperature heat exchangers for AM to keep up with the demand for better efficiency, better material, better manufacturing, and cost moving forward with AM technology in high‐temperature ceramic heat exchangers.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Ability of x‐ray computed tomography to resolve critical flaw size in laser‐based, paste stereolithography ceramic printing of alumina

Abstract Complex alumina parts were printed using vat photopolymerization (VPP), which is a stereolithography‐based additive manufacturing (AM) technique used to shape ceramic preforms, or green parts. The critical flaw size was determined using classical fracture mechanics techniques. The strength and fracture toughness were measured and compared to flaws detected in x‐ray computed tomography (XCT or CT) distributions as well as the fracture surfaces. The strength was lower compared traditionally made alumina, and that is due to layering effects, slurry defects, and printing defects. The critical flaw size from fracture mechanics was 206 µm. XCT has high enough resolution to detect the critical flaw size and much smaller features, where the average flaw size observed in CT scans was around 80–100 µm. The fracture surfaces indicate that flaws causing failure are larger than that of the critical flaw size (∼300 µm), but fracture surfaces do not show definitive features compared to traditionally made ceramics. Since XCT can observe flaws smaller than the critical flaw size, this method can be used as a screening technique.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Indirect additive manufacturing process for fabricating bonded soft magnets

A bonded soft magnet object comprising bonded soft magnetic particles of an iron-containing alloy having a soft magnet characteristic, wherein the bonded soft magnetic particles have a particle size of at least 200 nm and up to 100 microns. Also described herein is a method for producing the bonded soft magnet by indirect additive manufacturing (IAM), such as by: (i) producing a soft magnet preform by bonding soft magnetic particles with an organic binder, wherein the magnetic particles have an iron-containing alloy composition with a soft magnet characteristic, and wherein the particles of the soft magnet material have a particle size of at least 200 nm and up to 100 microns; (ii) subjecting the preform to an elevated temperature sufficient to remove the organic binder to produce a binder-free preform; and (iii) sintering the binder-free preform at a further elevated temperature to produce the bonded soft magnet.

Paranthaman, Mariappan Parans↗

DOE OSTI2024

Additive manufacturing process for producing aluminum-boron carbide metal matrix composites

A method for additive manufacturing of a composite object containing a bonded network of boron carbide particles and aluminum occupying spaces between boron carbide particles, the method comprising: (i) producing a porous preform constructed of boron carbide by an additive manufacturing process in which particles of boron carbide are bonded together; and (ii) infiltrating molten aluminum, at a temperature of 1000-1400° C., into pores of said porous preform to produce said composite object constructed of boron carbide particles within an aluminum matrix, wherein the boron carbide is present in the composite object in an amount of 30-70 wt. %. The resulting composite material is also herein described.

Cramer, Corson L.↗

DOE OSTI2023

Oxidation performance and limitations of additively manufactured SiC/Si-O-C composites at elevated temperatures

Here, SiC preforms were infiltrated with polycarbosiloxane preceramic polymer to create low-cost SiC—Si x O y C z matrix composites for possible high temperature application. The effect of specimen annealing conditions on the steam and air oxidation resistance was analyzed. Air exposures from 900–1500°C showed stability of the Si x O y C z matrix phase with moderate oxidation resistance. After 900°C exposures, oxidation of the composite is primarily limited to the matrix phase, and only at 1200 and 1500°C was SiC consumption visualized. Steam cycle exposures at 1200°C resulted in rapid linear oxidation of the composites with induced specimen swelling from volume expansion associated with internal oxidation. Specimens annealed in argon were found to be the most oxidation resistant due to increased matrix crystallinity and carbon retention. The results of this work were used to develop clear strategies for improving the high-temperature properties of SiC—Si x O y C z composites.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Environmental stability of additively manufactured siliconized silicon carbide for applications in hybrid energy systems

A key consideration for the successful operation of hybrid energy systems will be the environmental stability of materials used for their construction, particularly when experiencing service environments containing water vapor at high temperatures. Here, we report results from the characterization of siliconized silicon carbide (Si-SiC) prepared via binder jet additive manufacturing and reactive silicon melt infiltration after being exposed to environments representative of those in solid oxide fuel cell (SOFC) anodes, and to exhaust gases inside a microturbine operating on natural gas. In both cases, it was found that oxide scales formed on the surface and that these scales were dense, continuous, and well-bonded to the substrates, although there was evidence of transverse and longitudinal cracking most likely as a result of mismatches in the thermal expansion of the scale and the substrate. Measured values of the thickness of the oxide scale were compared to those predicted by parabolic oxidation kinetics of silicon, but the potential effects of silica volatilization induced by water vapor, and silica reduction when exposed to hydrogen are discussed. The overall results showed that the oxide scale is expected to be protective under the conditions of hybrid power generation systems.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Compliant heat exchangers, heat pipes and methods for making same

A method for fabricating heat exchangers using additive manufacturing technologies. Additive manufacturing enables the manufacture of heat exchangers with complex geometries and/or with internal and external integral surface features. Additive manufacture also facilitates the manufacture of heat exchangers with regional variations, such as changes in size, shape and surface features. In one embodiment, the present invention provides a heat exchanger with a helicoidal shape that provides axial elastic compliance. In one embodiment, the internal channel of the heat exchanger varies along its length. The internal channel may have a cross-sectional area that increases progressively from one end to the other. In one embodiment, the external shape of the tubular structure may be non-circular to optimize heat transfer with an external heat transfer fluid. In one embodiment, the present invention provides a heat pipe with an internal wicking structure formed as an integral part of the additive manufacturing process.

Lara-Curzio, Edgar↗

DOE OSTI2023

Hardness Measurements and Interface Behavior of SiC-B 4 C-Si Multiple Phase Particulate Composites Made with Melt Infiltration and Additive Manufacturing

Reaction-bonded SiC-B 4 C-Si ceramic composites were binder jet 3D-printed and subsequently pressureless-melt-infiltrated with molten Si. The addition of B 4 C aided the Si infiltration to produce a highly dense composite. The microstructures and phases of these composites were examined. The measured hardness values of each constituent with Vickers and nanoindentation matched the bulk values, and the macro-hardness values with Knoop and spherical indentation represented the bulk, composite hardness values of all three phases together, which was close to a rule of mixtures value. For particulate-based composites, this is a significant finding. The interfacial bonds of SiC and Si were imaged using scanning transmission electron microscopy to view intimacy, whereas the crack propagation was examined with carefully placed indents. This work demonstrated that pressureless melt infiltration with a reactive particle provides a method to shape non-wetting reaction-bonded ceramic composites with limited shrinkage and high density and provides insights into the mechanical behavior with numerous indentation techniques.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Additive Manufacturing of C/C-SiC Ceramic Matrix Composites by Automated Fiber Placement of Continuous Fiber Tow in Polymer with Pyrolysis and Reactive Silicon Melt Infiltration

An additive manufacturing process for fabricating ceramic matrix composites has been developed based on the C/C-SiC system. Automated fiber placement of the continuous carbon fibers in a polyether ether ketone matrix was performed to consolidate the carbon fibers into a printed preform. Pyrolysis was performed to convert the polymer matrix to porous carbon, and then Si was introduced by reactive melt infiltration to convert a portion of the carbon matrix to silicon carbide. The densities and microstructures were characterized after each step during the processing, and the mechanical properties were measured. The C/C-SiC composites exhibited a porosity of 10–20%, characteristic flexural strength of 234.91 MPa, and Weibull modulus of 3.21. The composites displayed toughness via a significant displacement to failure.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Indirect additive manufacturing process for producing SiC—B4C—Si composites

A method for indirect additive manufacturing of an object constructed of boron carbide, silicon carbide, and free silicon, comprising: (i) producing a porous preform constructed of boron carbide and silicon carbide by an indirect ceramic additive manufacturing (ICAM) process in which particles of a powder mixture become bonded together with an organic binder, wherein the powder mixture comprises: a) boron carbide particles, and b) silicon carbide particles, wherein at least 80 vol % of the silicon carbide particles are larger than the boron carbide particles; and wherein the boron carbide and silicon carbide particles are each included in an amount of 40-60 wt. % of the powder mixture, provided that the foregoing amounts sum to at least 95 wt. %; (ii) subjecting the porous preform to a temperature of 500-900° C. to volatilize the organic binder; and (iii) infiltrating molten silicon into pores of the porous preform to produce the object.

Cramer, Corson L.↗

DOE OSTI2022

Additive manufacturing of ceramic materials for energy applications: Road map and opportunities

Among engineering materials, ceramics are indispensable in energy applications such as batteries, capacitors, solar cells, smart glass, fuel cells and electrolyzers, nuclear power plants, thermoelectrics, thermoionics, carbon capture and storage, control of harmful emission from combustion engines, piezoelectrics, turbines and heat exchangers, among others. Advances in additive manufacturing (AM) offer new opportunities to fabricate these devices in geometries unachievable previously and may provide higher efficiencies and performance, all at lower costs. This article reviews the state of the art in ceramic materials for various energy applications. The focus of the review is on material selections, processing, and opportunities for AM technologies in energy related ceramic materials manufacturing. The aim of the article is to provide a roadmap for stakeholders such as industry, academia and funding agencies on research and development in additive manufacturing of ceramic materials toward more efficient, cost-effective, and reliable energy systems.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Zirconium-diboride silicon-carbide composites: A review

Zirconium diboride (ZrB 2 ) and silicon carbide (SiC) composites have long been of interest since it was observed that ZrB 2 improved the thermal shock resistance of SiC. However, processing of these materials can be difficult due to high and different sintering temperatures and differences in the thermodynamic stability of each material. ZrB 2 –SiC composites have been processed in a variety of ways including hot-pressing, spark-plasma sintering, reactive melt infiltration, pack cementation, chemical vapor deposition, chemical vapor infiltration, stereolithography, direct ink writing, selective laser sintering, electron beam melting, and binder jet additive manufacturing. Each manufacturing method has its own pros and cons. This review serves to summarize more than 60 years of research and provide a coherent resource for the variety of methods and advancements in development of ZrB 2 –SiC composites.

36 MATERIALS SCIENCE↗