Hydrogen transport in yttrium hydride under asymmetric heat
Metal hydrides are a promising moderator material for high temperature fission reactors. Yttrium hydride can be loaded to a high hydrogen density with relatively high hydrogen stability at temperatures up to 800°C. This makes yttrium hydride a potential moderator material for microreactors as foreseen in the fission surface power program. However, during the operation of such advanced reactors temperature gradients are expected which can change the local hydrogen density in the moderator. Hydrogen diffusion in metals is driven by a concentration gradient (Fick’s law) and thermal diffusion (Soret diffusion). Thermal diffusion is the transport of hydrogen, or other species, due to a temperature gradient. For example, hydrogen might migrate from the hot side of a sample to the cold side of a sample. Measuring Fickian diffusion is achieved through various permeation or absorption experiments, however measuring thermal diffusion is challenging and has rarely been performed. The Hydrogen Experimental Apparatus for Thermal Diffusion (HEATD) experiment is designed to induce thermal diffusion in samples and quench those samples so that the hydrogen distribution can be analyzed using hot vacuum extraction (HVE). One side of the sample was heated to a high temperature e.g., 800°C, while the other side of the sample is at a lower temperature. The sample was held under the applied temperature gradient for a given time until the anticipated hydrogen diffusion has occurred. The actual time depends depend on the sample composition and hydrogen concentration. The results from HVE showed that thermal diffusion took place in the specimen and the Soret coefficient was calculated.