SAMIS, the Solar Array Manufacturing Industry Simulation computer program was developed by Jet Propulsion Laboratories (JPL) to provide a method whereby manufacturers or potential manufacturers of photovoltaics could simulate a solar industry using their own particular approach. This paper analyzes the usefulness of SAMIS to a growing photovoltaic industry and clearly illustrates its limitations as viewed by an industrial user.
Several specific processing steps as part of a total process sequence for manufacturing silicon solar cells were studied. Ion implantation was identified as the preferred process step for impurity doping. Unanalyzed beam ion implantation was shown to have major cost advantages over analyzed beam implantation. Further, high quality cells were fabricated using a high current unanalyzed beam. Mechanically masked plasma patterning of silicon nitride was shown to be capable of forming fine lines on silicon surfaces with spacings between mask and substrate as great as 250 micrometers. Extensive work was performed on advances in plated metallization. The need for the thick electroless palladium layer was eliminated. Further, copper was successfully utilized as a conductor layer utilizing nickel as a barrier to copper diffusion into the silicon. Plasma etching of silicon for texturing and saw damage removal was shown technically feasible but not cost effective compared to wet chemical etching techniques.
The choice of which photovoltaic system (flat plate or concentrator) to use for utilizing solar cells to generate electricity depends mainly on the cost. A detailed, comparative manufacturing cost analysis of the two types of systems is presented. Several common assumptions, i.e., cell thickness, interest rate, power rate, factory production life, polysilicon cost, and direct labor rate are utilized in this analysis. Process sequences, cost variables, and sensitivity analyses have been studied, and results of the latter show that the most important parameters which determine manufacturing costs are concentration ratio, manufacturing volume, and cell efficiency. The total cost per watt of the flat plate solar cell is $1.45, and that of the concentrator solar cell is $1.85, the higher cost being due to the increased process complexity and material costs.
Solder, copper, and silver are evaluated as conductor layer metals for silicon solar cell metallization on the basis of metal price stability and reliability under operating conditions. Due to its properties and cost, copper becomes an attractive candidate for the conductor layer. It is shown that nickel operates as an excellent diffusion barrier between copper and silicon while simultaneously serving as an electrical contact and mechanical contact to silicon. The nickel-copper system may be applied to the silicon by plating techniques utilizing a variety of plating bath compositions. Solar cells having excellent current-voltage characteristics are fabricated to demonstrate the nickel-copper metallization system.
An advanced process sequence for manufacturing high efficiency solar cells and modules in a cost-effective manner is discussed. Emphasis is on process simplicity and minimizing consumed materials. The process sequence incorporates texture etching, plasma processes for damage removal and patterning, ion implantation, low pressure silicon nitride deposition, and plated metal. A reliable module design is presented. Specific process step developments are given. A detailed cost analysis was performed to indicate future areas of fruitful cost reduction effort. Recommendations for advanced investigations are included.
Processes for producing antireflection films on glass are concentrated in three areas: acid etching of glass, plasma etching of glass, and acid development of sodium silicate films on glass. The best transmission was achieved through the acid etching technique, while the most durable films were produced from development of sodium silicate films. Control of the acid etching technique is presently inadequate for production implementation. While films having excellent antireflective properties were fabricated by plasma etching techniques, all were water soluble.
The results of a study of process variables and solar cell variables are presented. Interactions between variables and their effects upon control ranges of the variables are identified. The results of a cost analysis for manufacturing solar cells are discussed. The cost analysis includes a sensitivity analysis of a number of cost factors.
A detailed cost analysis of solar cell module manufacturing, utilizing process sequences incorporating near-term technology, has been performed. The entire structuring of a factory to manufacture solar cell modules, starting from supplied polycrystalline silicon and other raw materials, was specified. This analysis then formed the basis for a sensitivity analysis of the major cost factors. The results of the cost and sensitivity analyses are presented here.
The rationale and application of a plated metal system, Pd2Si Pd - Ni - solder, is presented. This metallization system is particularly useful on shallow p-n junction solar cells. The advantages of such plated solar cell contacts are discussed. A process sequence for applying the metallization system is outlined. A specific example is presented, including chemical plating solution formulations and detailed process step descriptions. Electrical test data for solar cells metallized with the palladium-nickel-solder system are provided.
The state of technology readiness for the automated production of solar cells and modules is reviewed. Individual process steps and process sequences for making solar cells and modules were evaluated both technically and economically. High efficiency with a suggested cell goal of 15% was stressed. It is concluded that the technology exists to manufacture solar cells which will meet program goals.