NASA NTRS2000

Outgassing Total Mass Loss Obtained with Micro-CVCM and other Vacuum Systems

Several instruments including the Cahn Microbalance the Knudsen Cell, the micro-CVCM, and the vacuum Thermogravimetric Analyzer (TGA) were used in the testing of a graphite epoxy (GR/EP) composite that is proposed for use as a rigidizing element of an inflatable deployment system. This GR/EP will be cured in situ. The purpose of this testing is to estimate the gaseous production resulting from the curing of the GR/EP composite, to predict the resulting pressure, and to calculate the required venting. Every test was conducted under vacuum at 125 C for 24 hours. Upon comparison of the results, the ASTM E-595 was noted to have given readings that were consistently lower than those obtained using the other instruments, which otherwise provided similar results. The GR/EP was tested using several different geometric arrangements. This paper describes the analysis evaluating the molecular and continuum flow of the outgassing products issuing from the exit port of the ASTM E-595 system. The effective flow conductance provided by the physical dimensions of the vent passage of the ASTM E-595 system and that of the material sample among other factors were investigated to explain the reduced amount of outgassing released during the 24-hour test period

Scialdone, John J.↗

NASA NTRS1996

Atomic Oxygen and Space Environment Effects on Aerospace Materials Flown with EOIM-3 Experiment

Polymer materials samples mounted on a passive carrier tray were flown aboard the STS-46 Atlantis shuttle as complement to the EOIM-3 (Evaluation of Oxygen Interaction with Materials) experiment to evaluate the effects of atomic oxygen on the materials and to measure the gaseous shuttle bay environment. The morphological changes of the samples produced by the atomic oxygen fluence of 2.07 x 10(exp 20) atoms/cm(exp 2) are being reported. The changes have been verified using Electron Spectroscopy for Chemical Analysis (ESCA), gravimetric measurement, microscopic observations and thermo-optical measurements. The samples, including Kapton, Delrin, epoxies, Beta Cloth, Chemglaze Z306, silver Teflon, silicone coatings, 3M tape and Uralane and Ultem, PEEK, Victrex (PES), Polyethersulfone and Polymethylpentene thermoplastic, have been characterized by their oxygen reaction efficiency on the basis of their erosion losses and the oxygen fluence. Those efficiencies have been compared to results from other experiments, when available. The efficiencies of the samples are all in the range of E-24 g/atom. The results indicate that the reaction efficiencies of the reported materials can be grouped in about three ranges of values. The least affected materials which have efficiencies varying from 1 to 10(exp 25) g/atom, include silicones, epoxies, Uralane and Teflon. A second group with efficiency from 10 to 45(exp 25) g/atom includes additional silicone coatings, the Chemglaze Z306 paint and Kapton. The third range from 50 to 75(exp 25) includes organic compound such as Pentene, Peek, Ultem, Sulfone and a 3M tape. A Delrin sample had the highest reaction efficiency of 179(exp 25) g/atom. Two samples, the aluminum Beta cloth X389-7 and the epoxy fiberglass G-11 nonflame retardant, showed a slight mass increase.

Scialdone, John J.↗

NASA NTRS1992

Four space application material coatings on the long-duration exposure flight (LDEF)

Four material coatings of different thickness were flown on the LDEF to determine their ability to perform in the harsh space environment. The coatings, located in the ram direction of the spacecraft, were exposed for 10 months to the low-Earth orbit (LEO) environment experienced by the LDEF at an orbit of 260 nautical miles. They consisted of indium oxide (In2O3), silicon oxide (SiO(x)), clear RTV silicone, and silicone with silicate-treated zinc oxide (ZnO). These coatings were flown to assess their behavior when exposed to atomic oxygen and to confirm their good radiative properties, stability, electrical conductivity, and resistance to UV exposure. The flown samples were checked and compared with the reference unflown samples using high-magnification optical inspection, ESCA analysis, weight changes and dimensional changes. These comparisons indicated the following: The 1000 A SiO(x) coating eroded uniformly, with minor changes in its radiative properties. The 100 A of In2O3 coating eroded completely down to the Kapton backing, with resultant losses of reflectance. The RTV-615 showed erosion, with carbon (C) content losses, while the Si remained constant, with a doubling of the oxygen (O) concentration. The RTV-615 silicone with K2SiO3-treated ZnO changed from flat to glossy white in appearance. It lost C, was etched, and increased its O content. The upper layers showed no remaining Zn or K. Losses of reflectance occurred within certain wavelength bands. It was not possible to evaluate the experimental oxygen reaction rate using the calculated atomic oxygen fluence of 2.6 x 10(exp 20) atoms/cm(exp 2) for the exposure of these coatings during the flight. The bakeout of the coatings was not carried out prior to the flight. Hence, the coating weight and dimensional losses included losses by outgassing products.

Scialdone, John J.↗

NASA NTRS1992

"Easy-on, Easy-off" Blanket Fastener

Fasteners hold flexible blanket on set of posts on supporting structure. Disk of silicone rubber cast on disk of Mylar, fastened to blanket and press-fit over post to nest securely in groove. No tools needed for installation or removal.

Kolecki, Ronald E.↗

NASA NTRS1991

A new antifoaming agent for epoxy material processing

It has been found that fluorodiepoxides are effective antifoaming agents for epoxy processing when applied at a level as low as 0.1 to 0.2 percent, and there is no adverse effect on the properties of the cured products. The novelty of the fluorodiepoxide is that it is reactive and can copolymerize with a conventional epoxy resin at the same time in the same way in forming an inter-crosslinked polymer network. However, when applied at a high level, compatibility problems may prevail.

Lee, Sheng Yen↗

NASA NTRS1990

An evaluation of two flat-black silicone paints for space application

Tests were conducted on two flat-black silicone paints suggested for space applications to determine their optical, electrical, and mechanical properties. Three different types of substrate materials were chosen for these paint tests; the application of the paints onto the primed substrates was carried out by spray coating. The adhesion properties were verified by thermal shock and sudden immersion into liquid nitrogen. A controlled thermal vacuum tests was also carried out by varying the temperature of the paint from -100 to 225 C. The measured optical properties included normal and hemispherical emittance, and solar absorption/reflectance. A simultaneous exposure to low-energy proton/UV irradiation in vacuum, and high-energy proton/electron irradiation was carried out. Additional tests of the paints are described.

Clatterbuck, Carroll H.↗