Clarke, Kester Diederik

Publications and source records attributed to Clarke, Kester Diederik.

9 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Clarifying the formation of equiaxed grains and microstructural refinement in the additive manufacturing of Ti-Cu

Controlling microstructural evolution in metallic additive manufacturing (AM) is difficult, especially in producing refined as-built grains instead of coarse, directional grains. Traditional solutions involve adding inoculants to AM feedstocks, but titanium (Ti) alloys cannot employ this approach without producing detrimental secondary phases. Ti-Cu (Ti-copper) alloys offer a solution through constitutional supercooling and/or solid state thermal cycling under AM conditions. This work analyzes a compositionally graded directed energy deposition (DED) Ti-Cu build, single-melt laser tracks, and dilatometric heat treatments to evaluate if, when, and by what mechanism(s) microstructural refinement occurs. Refinement by inoculation of unmelted powder particles was also considered. Constitutional supercooling produced no net microstructural refinement as any equiaxed dendrites which form are remelted with new deposition. This finding agreed with solidification modeling of powder bed fusion-laser beam (PBF-LB) and DED builds. Solid state thermal cycling refined microstructures only during ex-situ dilatometric heat treatments, suggesting build parameter optimization is needed to achieve refinement in-situ. Accidental heterogeneous nucleation on unmelted Ti powder, originating from the different thermophysical properties of Ti and Cu, provided the most significant microstructural refinement. This work systematically assesses the microstructural refinement mechanisms of Ti-Cu in AM builds and offers insights into microstructural control in eutectoid alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Computational thermodynamics-guided alloy design and phase stability in CoCrFeMnNi-based medium-and high-entropy alloys: An experimental-theoretical study

A computational thermodynamics approach has been employed to design CoCrFeMnNi-based medium- and high-entropy alloys (M/HEAs) with systematically varied compositions (Co(( 80-X )/ 2 )Cr(( 80-X )/ 2 )Fe X Mn 10 Ni 10 with x = 30, 40, and 50 at.%) and phase stability. Since the formation of sigma phase, usually brittle and undesirable, is a common concern, when this class of alloys is subjected to elevated temperatures (600–1000 °C), predicting its formation becomes essential. Thus, its formation and the phase equilibria were studied using the CALPHAD method, and two empirical methods, namely, valence electron concentration (VEC) and paired sigma-forming element (PSFE). Isothermal aging treatments at 900–1100 °C for 20 h were performed, since CALPHAD and VEC/PSFE predictions diverged. Both prediction methods were compared with experimental characterization by a combination of scanning electron microscopy and high-energy synchrotron X-ray diffraction. In conclusion, the predictions from the VEC/PSFE and CALPHAD calculations (depending on the database used) were shown to be quite accurate.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Tuning austenite stability through prior microstructure control in a low-alloy Q&P steel

Quenching and partitioning (Q&P) processing is a widely accepted heat treatment methodology for creating high strength steels consisting of ferrite, martensite, and austenite, while maintaining relatively low manufacturing costs. Though the research on effects of prior microstructure is limited, an understanding of the heat treatment response of different starting microstructures is critical to processing and creating steels with complex microstructures that contain retained austenite and may afford opportunities to further optimize properties. This study investigates the influence of starting microstructure (ferrite/pearlite versus martensite) and prior levels of cold work (38 verses 58 %) on the microstructural development and mechanical properties of a 0.2 C-2.0 Mn-1.5 Si (wt.%) steel exposed to Q&P processing. Samples with a starting martensitic microstructure resulted in higher retained austenite fractions and a more homogeneous microstructure after Q&P processing compared to a starting microstructure of ferrite-pearlite. Starting martensitic microstructures also displayed higher work hardening rates and higher uniform elongations. Larger cold reductions saw accelerated dissolution kinetics and austenite formation during intercritical annealing, resulting in more similar final microstructures from the ferrite-pearlite and martensitic starting microstructures. Finally, the results presented here indicate that varying prior processing can be a route to manipulate and control austenite stability in a Q&P processed steel.

36 MATERIALS SCIENCE↗
DOE OSTI2017

Annealing of (DU-10Mo)-Zr Co-Rolled Foils

Producing uranium-10wt% molybdenum (DU-10Mo) foils to clad with Al first requires initial bonding of the DU-10Mo foil to zirconium (Zr) by hot rolling, followed by cold rolling to final thickness. Rolling often produces wavy (DU-10Mo)-Zr foils that should be flattened before further processing, as any distortions could affect the final alignment and bonding of the Al cladding to the Zr co-rolled surface layer; this bonding is achieved by a hot isostatic pressing (HIP) process. Distortions in the (DU-10Mo)-Zr foil may cause the fuel foil to press against the Al cladding and thus create thinner or thicker areas in the Al cladding layer during the HIP cycle. Post machining is difficult and risky at this stage in the process since there is a chance of hitting the DU-10Mo. Therefore, it is very important to establish a process to flatten and remove any waviness. This study was conducted to determine if a simple annealing treatment could flatten wavy foils. Using the same starting material (i.e. DU-10Mo coupons of the same thickness), five different levels of hot rolling and cold rolling, combined with five different annealing treatments, were performed to determine the effect of these processing variables on flatness, bonding of layers, annealing response, microstructure, and hardness. The same final thickness was reached in all cases. Micrographs, textures, and hardness measurements were obtained for the various processing combinations. Based on these results, it was concluded that annealing at 650°C or higher is an effective treatment to appreciably reduce foil waviness.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2016

Feasibility Study for Electrical Discharge Machining of Large DU-Mo Castings

U-10 wt. % Mo (U-10Mo) alloys are being developed as low enrichment monolithic fuel for the CONVERT program. Optimization of processing for the monolithic fuel is being pursued with the use of electrical discharge machining (EDM) under CONVERT HPRR WBS 1.2.4.5 Optimization of Coupon Preparation. The process is applicable to manufacturing experimental fuel plate specimens for the Mini-Plate-1 (MP-1) irradiation campaign. The benefits of EDM are reduced machining costs, ability to achieve higher tolerances, stress-free, burr-free surfaces eliminating the need for milling, and the ability to machine complex shapes. Kerf losses are much smaller with EDM (tenths of mm) compared to conventional machining (mm). Reliable repeatability is achievable with EDM due to its computer-generated machining programs.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2015

Microstructure effects on the recrystallization of low-symmetry alpha-uranium

We employ electron backscatter diffraction (EBSD) to investigate microstructural evolution of uranium during recrystallization. To understand the relationship between microstructure and recrystallization, we use measures of intra-granular misorientation within grains and near grain boundaries in both deformed (non-recrystallized) uranium and recrystallizing uranium. The data show that the level of intra-granular misorientation depends on crystallographic orientation. However, contrary to expectation, this relationship does not significantly affect the recrystallization texture. Rather, the analysis suggests that recrystallization nucleation occurs along high angle grain boundaries in the deformed microstructure. Specifically, we show that the nucleation of recrystallized grains correlates well with the spatially heterogeneous distribution of high angle boundaries. Due to the inhomogeneous distribution of high angle boundaries, the recrystallized microstructure after long times exhibits clustered distributions of small and large grains. Twin boundaries do not appear to act as recrystallization nucleation sites.

36 MATERIALS SCIENCE↗