First Results from Two Nb3Sn Cavities Assembled in a CEBAF Quarter Cryomodule
Explore the source record for details and available documents.
Eremeev, G.↗
Engineering topics
Ciovati, G.
Publications and source records attributed to Ciovati, G..
First Results from Two Nb3Sn Cavities Assembled in a CEBAF Quarter Cryomodule
Two 1.5 GHz CEBAF C75-shape 5-cell accelerator cavities were coated with Nb3Sn film using the vapor diffusion technique at Fermilab and Jefferson Lab coating facilities. Both cavities were measured at 4 K and 2 K in the vertical cavity test facility (VCTF) in each lab, then assembled into a CEBAF quarter cryomodule at Jefferson Lab. The cryomodule was tested at 4 K and 2 K in the CryoModule Test Facility (CMTF) at Jefferson Lab. RF test results for both cavities in the cryomodule are similar to those in the qualification test in VTS, with one cavity reaching Eacc = 7.9 MV/m and the other - 13.3 MV/m at 4 K.
Eremeev, G.↗
First Results from two Nb3Sn Cavities Assembled in a CEBAF Quarter Cryomodule
Two 1.5 GHz CEBAF C75-shape 5-cell accelerator cavities were coated with Nb3Sn film using the vapor diffusion technique at Fermilab and Jefferson Labcoating facilities. Both cavities were measured at 4 K and 2 K in the vertical cavity test facility (VCTF) in each lab, then assembled into a CEBAF quartercryomodule at Jefferson Lab. The cryomodule was tested at 4 K and 2 K in the CryoModule Test Facility (CMTF) at Jefferson Lab. RF test results for bothcavities in the cryomodule are similar to those in the qualification test in VTS, with one cavity reaching Eacc =7.9 MV/m and the other - 13.3 MV/m at 4 K
Eremeev, G.↗
Effects of electron beam irradiation on CrMnV and CrMnTiV high entropy alloys: Nano-mechanical, structural, and thermodynamic perspectives
Beam exit windows are crucial components of any particle accelerator as they provide an interface between the beamline vacuum and target material at atmospheric media. For high beam power machines, special materials and designs are required to withstand high radiation and mechanical loads, while minimizing energy loss during transition and maximizing window lifetime. This research investigates the impact of electron beam exposure to bulk CrMnV and CrMnTiV high entropy alloys (HEAs) with the primary goal of identifying suitable candidate materials for the design of robust and durable exit window settings. The selection criteria include intrinsic characteristics, power dissipation, and mechanical responses. According to the thermodynamic calculations, both equiatomic CrMnV and the addition of 7% of Ti with equiatomic CrMnV yield solid-solutions phases. The structural and mechanical properties of CrMnV and CrMnTiV samples were tested using field emission scanning electron microscopy, atomic force microscopy, scanning electron microcopy with energy dispersive x-ray spectroscopy, x-ray diffraction, and nanoindentation before and after exposure to a dose of ~66 kGy from a 10 MeV e-beam accelerator. Despite exhibiting beam transmission characteristics comparable to Cr and V, the indentation hardness of HEAs exceeded that of the Cr and V samples by five to six times. The examination of the CrMnTiV irradiated samples revealed organized deformation patterns depicting new features, which we suspect twinning and twin boundaries due to the addition of Ti to CrMnV. Ti, a hexagonal-close-packed crystal structure, is commonly known for deformation twinning behavior.
36 MATERIALS SCIENCE↗
COMMISSIONING RESULTS OF THIRD C75 CRYOMODULE FOR CEBAF
The program to upgrade CEBAF cryomodules has been implemented to enhance the energy gain of refur-bished cryomodules up to 75 MeV. This strategy in-volves reusing the waveguide end-groups from original CEBAF cavities produced in the 1990s, and existing five elliptical cell cavities are replaced with a new optimized cell shape cavity constructed from large-grain, ingot Nb material. Following fabrication, each cavity undergoes centrifugal barrel polishing and electropolishing and is tested at 2.07 K. Eight cavities are then assembled into "cavity pairs" and tested at 2.07 K before integration into the cryomodule. This paper pre-sents the outcomes of the cavity qualification for the third C75 module, providing a detailed account of the assessment in both a vertical cryostat and the acceptance test results of the cryomodule. Furthermore, efforts have been made to address performance limitations arising from field emission and multipacting
Senevirathne, I.↗
IMPACT OF MEDIUM TEMPERATURE HEAT TREATMENT ON FLUX TRAPPING SENSITIVITY IN SRF CAVITIES
The effect of mid-T heat treatment on flux trapping sensitivity was measured on several 1.3 GHz single cell cavities subjected to medium temperature vacuum annealing at temperature of 150 - 400 ?C for a duration of 3 hours. The cavity was cooldown with residual magnetic field ?0 and ?20 mG in Dewar with cooldown condition of full flux trapped. The quality factor as a function of accelerating gradient was measured. The results show the correlation between the treatment temperature, quality factor, and sensitivity to flux trapping. Sensitivity increases with increasing heat treatment temperatures within the range of (200 - 325 ?C/3h).Moreover, variations in the effective penetration depth ofthe magnetic field and the density of quasi-particles can occur,influencing alterations in the cavity?s electromagneticresponse and resonance frequency.
Dhakal, P.↗
CHARACTERIZATION OF DISSIPATIVE REGIONS OF A N-DOPED SRF CAVITY
We report scanning tunneling microscopy measurements on N-doped cavity hot and cold spot cutouts. Analysis of the electron tunneling spectra using a proximity effect theory shows that hot spots have a reduced superconducting gap and a wider distribution of the contact resistance. Alone, these degraded superconducting properties account for a much weaker excess dissipation as compared with the vortex contribution. Based on the correlation between the quasiparticle density of states and temperature mapping, we suggest that degraded superconducting properties may facilitate vortex nucleation or settling of trapped flux during cooling the cavity through the critical temperature.
Lechner, E.M.↗
ON THE WAY TO A 10MEV, CONDUCTION-COOLED COMPACT SRF ACCELERATOR
After the success of designing a compact 1MeV, 1MW accelerator based on conduction-cooled SRF, Jefferson Lab is now pursuing a concept to provide a tenfold increase of the beam energy. The obvious challenge for SRF is to move from a single-cell to a multicell cavity while maintaining high efficiency and the ability to operate the machine without a complex cryogenic plant. This paper summarizes the current state of this effort with respect to the design of a Nb3Sn coated five-cell cavity and the corresponding RF components, especially the fundamental power coupler (FPC), as well as first thermal analysis of the cryocooler-based cooling setup.
Ciovati, G.↗
Temperature, rf field, and frequency dependence performance evaluation of superconducting niobium half-wave coaxial cavity
Recent advancement in superconducting radio frequency cavity processing techniques, with diffusion of impurities within the RF penetration depth, resulted in high quality factor with increase in quality factor with increasing accelerating gradient. The increase in quality factor is the result of a decrease in the surface resistance as a result of nonmagnetic impurities doping and change in electronic density of states. The fundamental understanding of the dependence of surface resistance on frequency and surface preparation is still an active area of research. Here, we present the result of RF measurements of the TEM modes in a coaxial half-wave niobium cavity resonating at frequencies between 0.3 ? 1.3 GHz. The temperature dependence of the surface resistance was measured between 4.2 K and 1.6 K. The field dependence of the surface resistance was measured at 2.0 K. The baseline measurements were made after standard surface preparation by buffered chemical polishing.
Dhakal, P.↗
Commissioning of the Second JLAB C75 Cryomodule & Performance Evaluation of Installed C75 Cavities
JLAB has long been a hub of SRF technology with the CEBAF accelerator as one of its first large scale adopters. As SRF technology has advanced, the C50 and C100 programs have allowed for the extension of CEBAF's total energy to 6 GeV and nearly 12 GeV respectively. Along with the increase in energy reach, rates of accelerating gradient degradation have been extracted for these cryomodule designs. A plan to mitigate these losses & maintain robust gradient headroom to deliver the 12 GeV program - the CEBAF Performance Plan - established a multi-year effort of cryomodule refurbishments and replacements. Part of this plan included a cost optimization of the C50 program with more modern processing techniques and the replacement of existing cavities with larger grain boundary cavities produced from ingot Niobium (dubbed C75 for 75 MeV gain). Reports have been made on the prototype pair of C75 cavities installed in a C50 cryomodule and the first full C75 cryomodule installed in 2017 and 2021. This paper reports on the results from the qualification of the cavities for the second C75 module in both a vertical cryostat and the commissioning results of the cryomodule in the CEBAF tunnel. This material is based upon work supported by the U.S. Department of Energy, Office of Science, Office of Nuclear Physics under contract DE-AC05-06OR23177.
McCaughan, Michael↗
Medium grain niobium SRF cavity production technology for science frontiers and accelerator applications
Herein we present the cost-effective production of superconducting radio frequency (SRF) cavities made of medium grain (MG) niobium (Nb) discs directly sliced from forged and annealed billet. This production method provides clean surface conditions and reliable mechanical characteristics with sub-millimeter average grain size resulting in stable SRF cavity production. We propose to apply this material to particle accelerator in the science and industrial applications. The science applications require high field gradients(≥ 30 MV/m) particularly in pulsed mode. The industrial applications require high $Q_0$ values with moderate gradients (~ 20 MV/m) in CW mode operation. This paper describes the MG Nb disc production recently demonstrated and discusses future prospects for application in advanced particle accelerators in the science and industrial applications.
47 OTHER INSTRUMENTATION↗
High resolution diagnostic tools for superconducting radio frequency cavities
Superconducting radio-frequency (SRF) cavities are one of the fundamental building blocks of modern particle accelerators. To achieve the highest quality factors (10 10 –10 11 ), SRF cavities are operated at liquid helium temperatures. Magnetic flux trapped on the surface of SRF cavities during cool-down below the critical temperature is one of the leading sources of residual RF losses. Instruments capable of detecting the distribution of trapped flux on the cavity surface are in high demand in order to better understand its relation to the cavity material, surface treatments and environmental conditions. We have designed, developed, and commissioned two high-resolution diagnostic tools to measure the distribution of trapped flux at the surface of SRF cavities. One is a magnetic field scanning system, which uses cryogenic Hall probes and anisotropic magnetoresistance sensors that fit the contour of a 1.3 GHz cavity. This setup has a spatial resolution of ~ 13 μm in the azimuthal direction and ~ 1 cm along the cavity contour. The second setup is a stationary, combined magnetic and temperature mapping system, which uses anisotropic magnetoresistance sensors and carbon resistor temperature sensors, covering the surface of a 3 GHz SRF cavity. This system has a spatial resolution of 5 mm close to the iris and 11 mm at the equator. Initial results show a non-uniform distribution of trapped flux on the cavities’ surfaces, dependent on the magnitude of the applied magnetic field during field-cooling below the critical temperature.
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
Evaluation of Single-Cell Cavities Made of Forged Ingot Niobium at Jefferson Lab
Currently, fine grain niobium (Nb) (grain size ~ 50 um) and large grain Nb (grain size of a few cm) are being used for the fabrication of superconducting radio frequency (SRF) cavities. Medium grain forged ingot with grain size of a few hundred um may be beneficial for cost-effectiveness as well as providing better performance for future SRF-based accelerators. Forged ingot Nb with medium grain size is a novel production method to obtain Nb discs used for the fabrication of superconducting radio frequency cavities. We have fabricated two 1.5 GHz single cell cavities made from forged Nb ingot with a residual resistivity ratio of ~100. The cavities were chemically and mechanically polished and heat-treated in the temperature range of 650-1000 C before the rf test. One of the cavities reached an accelerating gradient of 34 MV/m with a quality factor Q > 1e10, while the second cavity was limited at 14 MV/m, likely due to a weld defect at the equator.
Dhakal, P.↗
DEMONSTRATION OF TWICE REDUCED LORENTZ FORCE DETUNING IN SRF CAVITY BY COPPER COLD SPRAYING
Superconducting RF (SRF) cavities usually are made of thin-wall high RRR Niobium that is susceptible to Lorentz Force Detuning (LFD) ? cavity deformation phenomena caused by high magnitude RF fields. This type of deformation can be mitigated by using an additional copper layer deposited on the outer surface of the cavity. In this paper, we present both modeling results and experimental data of high gradient test of an SRF cavity at cryogenic temperatures. It was demonstrated that LFD can be significantly reduced (factor of two) by the copper cold spray reinforcement without sacrificing cavity flexibility for tuning. We also present a finite-element model that allows us to confirm our experimental results and optimize the cavity geometry for LFD reduction with incorporated coupled RF, structural and thermal modules.
Kostin, R.↗
USING E-BEAM IRRADIATION BEAMLINE AT JEFFERSON LAB TO REMOVE 1,4-DIOXANE AND PFAS IN WASTEWATER
The designed e-beam irradiation beamline [1] at Jefferson Lab has been commissioned and applied to study the degradation removal of 1,4-dioxane and per- and polyfluoroalkyl substances (PFAS) in wastewater by collaborating with Hampton Roads Sanitation District (HRSD), treating wastewater in southeast Virginia. The absorbed dose and dose distribution in the entire sample were achieved innovatively using Monte-Carlo simulations that were calibrated with opti-chromic dosimeter rods directly exposed to the e-beam. This research could be a stepstone to the future MW compact SRF accelerator [2] for wastewater remediation.
Li, X.↗
MAGNETIC FIELD MAPPING OF 1.3 GHz SUPERCONDUCTING RADIO FREQUENCY NIOBIUM CAVITIES
Niobium is the material of choice to build superconducting radio frequency (SRF) cavities, which are fundamental building blocks of modern particle accelerators. These cavities require a cryogenic cool-down to ~2 - 4 K for optimum performance minimizing RF losses on the inner cavity surface. However, temperature-independent residual losses in SRF cavities cannot be prevented entirely. One of the significant contributor to residual losses is trapped magnetic flux. The flux trapping mechanism depends on different factors, such as surface preparations and cool-down conditions. We have developed a diagnostic magnetic field scanning system (MFSS) using Hall probes and anisotropic magneto-resistance sensors to study the spatial distribution of trapped flux in 1.3 GHz single-cell cavities. The first result from this newly commissioned system revealed that the trapped flux on the cavity surface might redistribute with increasing RF power. The MFSS was also able to capture significant magnetic field enhancement at specific cavity locations after a quench.
Parajuli, I. P.↗
PRELIMINARY RESULTS OF MAGNETIC AND TEMPERATURE MAP SYSTEM FOR 3 GHz SUPERCONDUCTING RADIO FREQUENCY CAVITIES
Superconducting radio frequency (SRF) cavities are fundamental building blocks of modern particle accelerators. A surface resistance in the tens of nanoOhm range is achieved when cooling these cavities to liquid helium temperature, ~2 - 4 K. One of the leading sources of residual losses in SRF cavities is trapped magnetic flux. Flux trapping mechanism depends on different surface preparations and cool-down conditions. We have designed, developed and commissioned a combined magnetic and temperature mapping system using anisotropic magneto-resistance sensors and carbon resistors, respectively, to study the flux trap mechanism in 3 GHz single-cell niobium cavities. In this contribution, we will describe the experimental apparatus and present preliminary test results.
Parajuli, I. P.↗
Cavity Production and Testing of the First C75 Cryomodule for CEBAF
The CEBAF cryomodule rework program was updated over the last few years to increase the energy gain of refurbished cryomodules to 75 MeV. The concept recycles the waveguide end-groups from original CEBAF cavities fabricated in the 1990s and replaces the five elliptical cells in each with a new optimized cell shape fabricated from large-grain, ingot Nb material. Eight cavities were fabricated at Research Instruments, Germany, and two cavities were built at Jefferson Lab. Each cavity was processed by electropolishing and tested at 2.07 K. The best eight cavities were assembled into ’cavity pairs’ and re-tested at 2.07 K, before assembly into the cryomodule. All but one cavity in the cryomodule were within 10% of the target accelerating gradient of 19 MV/m with a quality factor of 8·10⁹. The performance limitations were field emission and multipacting.
Ciovati, G.↗