Resumption of SFR Overpower Testing and Post-Transient Examination of the THOR-C-2 Irradiation Test

Transient overpower testing for fuel safety research and development has resumed at Idaho National Laboratory. The THOR-C-2 commissioning test has been performed and post-transient examination has been performed revealing the intended creep rupture failure near the top of the fuel zone. This paves the way for future testing on previously irradiated fuels that will support fuel development and qualification.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Resumption of SFR Overpower Testing and Post-Transient Examination of the THOR-C-2 Irradiation Test

Transient overpower testing for fuel safety research and development has resumed at Idaho National Laboratory. The THOR-C-2 commissioning test has been performed and post-transient examination has been performed revealing the intended failure near the top of the fuel zone. This paves the way for future testing on previously irradiated fuels that will support fuel development and qualification.

advanced reactors↗
DOE OSTI2024

Understanding a novel form of intergranular corrosion of stainless steel 316L exposed to molten LiCl-Li 2 O-Li

We report stainless steel 316 L exposed to LiCl-Li2O molten salt containing Li metal for 500 and 1000 h experiences deep intergranular attack and bulk void formation. This degradation is due to a synergistic corrosion mechanism, different than other forms of molten salt corrosion, where Cr and Mn oxides and carbides form along grain boundaries and are dissolved by Li metal. Synchrotron transmission X-ray microscopy 3D imaging is used to show corrosion morphology and Cr enrichment and depletion in a novel format that has not previously been used for bulk corrosion samples.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗