Operando X-ray scattering reveals ordering-mediated solidification in additive manufacturing
Explore the source record for details and available documents.
36 MATERIALS SCIENCE↗
Engineering topics
Chuang, Chihpin Andrew
Publications and source records attributed to Chuang, Chihpin Andrew.
Martensite decomposition during rapid heating of Ti-6Al-4V studied via in situ synchrotron X-ray diffraction
Martensite, α‘, commonly appears in Ti-6Al-4V upon rapid cooling from above the β-transus temperature. It is known that α‘ decomposes into α and β at high temperatures but well below the β-transus temperature. Here, we study the decomposition of martensitic Ti-6Al-4V under rapid laser heating, employing in situ synchrotron X-ray diffraction. A comparison is made with post-annealed Ti-6Al-4V under heating to elucidate changes without martensite decomposition. The fast acquisition of X-ray diffraction data at 250 Hz temporally resolves the decomposition process initiated by annihilating dislocations in α‘. The recovery process is accompanied by structural changes in martensite, followed by the phase transformation to β. Thermal profiles estimated from the lattice parameter data reveal the influence of heating rates and dislocation densities on the decomposition process. Throughout the analysis of the diffraction profiles with respect to estimated temperature, we propose a straightforward method for approximating the initiation temperature of martensite decomposition.
42 ENGINEERING↗
Melting and solidification dynamics during laser melting of reaction-based metal matrix composites uncovered by in-situ synchrotron X-ray diffraction
Laser additive manufacturing (AM) of reaction-based metal matrix composites (MMCs) involves highly complex and non-equilibrium material transformation behavior, including melting, dissolution, precipitation, and solidification. Yet, the dynamics and interplay of these phase transformation processes remain poorly understood, posing substantial challenges in identifying the microstructure formation mechanism, and predicting and controlling the microstructure in the printed parts. Here, in this study, we performed the in-situ X-ray diffraction experiment to characterize the phase evolution dynamics of the 316L + 10 vol.%TiC system during laser melting, which provides direct and quantitative insights of the complex phase reaction and evolution dynamics under rapid heating and cooling conditions relevant to additive manufacturing of reaction-based MMCs. Further in-depth thermodynamic and kinetic calculations revealed that most of the phase evolution behavior observed in the in-situ X-ray diffraction experiment cannot be solely explained by widely used equilibrium thermodynamic models, and diffusion-controlled nonequilibrium dissolution and precipitation kinetics must be considered to elucidate the complex phase evolution behavior, including incomplete TiC dissolution, and three-step TiC precipitation. The three distinct types of precipitates generate unique hierarchical TiC micro- and nanostructures, which enhances the yield strength from 513 MPa to 877 MPa by 71 %, tensile strength from 628 MPa to 1054 MPa by 68 %, and Young's modulus from 193 GPa to 221 GPa by 14 %. The findings of our research provide the knowledge foundation for the design of unique microstructures and advanced MMC materials through laser AM.
36 MATERIALS SCIENCE↗
Phase transformation dynamics guided alloy development for additive manufacturing
Fusion-based additive manufacturing technologies enable the fabrication of geometrically and compositionally complex parts unachievable by conventional manufacturing methods. However, the non-uniform and far-from-equilibrium heating/cooling conditions pose a significant challenge to consistently obtaining desirable phases in the as-printed parts. Here, in this study, we report a martensite stainless steel development guided by phase transformation dynamics revealed by in-situ high-speed, high-energy, high-resolution X-ray diffraction. This developed stainless steel consistently forms desired fully martensitic structure across a wide range of cooling rates (10 2 –10 7 °C/s), which enables direct printing of parts with fully martensitic structure. The as-printed material exhibits a yield strength of 1157 ± 23 MPa, comparable to its wrought counterpart after precipitation-hardening heat-treatment. The as-printed property is attributed to the fully martensitic structure and the fine precipitates formed during the intrinsic heat treatment in additive manufacturing. The phase transformation dynamics guided alloy development strategy demonstrated here opens the path for developing reliable, high-performance alloys specific for additive manufacturing.
17–4 PH stainless steel↗
Solid-State Joining of Magnesium Sheet to High-Strength Steel
Increasing the use of lightweight materials and implementing enabling manufacturing technologies are the two primary paths toward automotive weight reduction. In many situations, the ability to substitute light weight material requires a need to attach and join light weight material to existing steel substructures requiring dissimilar joining technologies. Dissimilar joining methods currently available in cost range for high volume automotive manufacturing face multiple challenges. The problem is exacerbated in the case of Magnesium alloy to steel joints because of their highly dissimilar nature and lack of mutual miscibility. Additionally, Magnesium’s poor room temperature ductility complicates the use of point fastening technologies. Two emerging solid-state joining technologies Friction Stir assisted Scribe welding (FaST) and Ultrasonic Welding (USW) that employ large amount of plastic deformation at the interface were used to investigate, develop, and understand dissimilar joints between Magnesium Alloy to DP590 Steel. Various process responses including interface temperatures, process forces, strain fields were captured during the development of the welding process. Variety of welded samples were tested and characterized to understand the relationship between welding conditions and joints microstructure and mechanical properties.
36 MATERIALS SCIENCE↗
High-Energy X-ray Tomographic Analysis of Precursor Metal Powders (Ti-6Al-4V) Used for Additive Manufacturing
We utilized high-energy x-ray tomography to characterize Ti-6Al-4V metal powders (both as-received and recycled) used in powder-bed additive manufacturing process. The image processing workflow was developed to process and analyze large amount of data objectively by computer program. The distribution of size and shape of the metal particles as well as defect (mainly porosity) inside the particles was analyzed with the statistical representation and resolution in micrometer. The result revealed that circular-shaped porosity with various sizes could be embedded in the powder particles. These porosities could potentially be transferred to the 3D printed part and critically affect the mechanical performance of the component. The present study shows the effectiveness of characterizing metal powders using x-ray imaging techniques where sufficient number of particles can be sampled within tens of minutes with a minimum sample preparation and high accuracy. Clear structural differences in the as-received and recycled powders were delineated that helps in determining the feasibility of using the recycled powders.