Real-time evolution of texture and temperature during friction stir processing of a magnesium alloy: An operando neutron diffraction study

The real-time development of texture and the evolution of temperature during friction stir processing (FSP) of a Mg alloy were investigated using an operando neutron diffraction measurement. A novel approach was applied in this study where the real-time, quasi-steady state measurements performed as a function of position during FSP are converted to a Lagrangian dataset that reveals the transient behavior as a function of time. The in-situ FSP was carried out under two different thermo-mechanical processing conditions represented by the Zener-Hollomon parameter, Z. Further, the results show that: (i) a shear texture develops from the initial strong basal texture with the peak temperature reaching about 774 K during a low-Z processing and (ii) a strong off-normal texture develops with a peak temperature of 616 K during a high-Z processing. Moreover, time-temperature-texture diagrams were established to reveal the real-time development of the texture during the processing for both the low Z and high Z processing conditions. The changes in texture will be discussed in terms of plastic deformation mechanisms active during various stages of the FSP under the two different processing conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Characterization and Rationalization of Microstructural Evolution in GRCop-84 Processed by Laser-Powder Bed Fusion (L-PBF)

In this study, prismatic geometries of GRCop-84 [Cu-8Cr-4Nb (at. pct)] were built with laser-powder bed fusion (L-PBF) process. The samples were sectioned parallel or perpendicular to the build direction and characterized in the as-built and after post-processing with a hot-isostatically pressing (HIP) treatment. The microstructure and phase evolutions were evaluated with optical microscopy, scanning electron microscopy (SEM), electron backscattered diffraction (EBSD), and high-temperature X-ray diffraction (HTXRD) up to 1223 K. The samples in the as-built conditions exhibited predominantly columnar epitaxial and misoriented Cu-FCC grains. The microstructure evolutions are discussed based on locations within the overall build geometry, the dynamics of small melt pool shape and sectioning effects. The above grain structure did not change significantly during post-process HIP treatment. The stability of this FCC grain structure is attributed to the formation of primary stable Cr 2 Nb (Laves phase) during L-PBF, even before the emergence of FCC grains from liquid. The stability of Cr 2 Nb in both as-built and HIPed samples were evaluated using high-temperature X-ray diffraction measurements and compared with that of gas-atomized powder. The significance of these results is discussed with reference to aerospace applications.

36 MATERIALS SCIENCE↗
DOE OSTI2022

In situ melt pool measurements for laser powder bed fusion using multi sensing and correlation analysis

Laser powder bed fusion is a promising technology for local deposition and microstructure control, but it suffers from defects such as delamination and porosity due to the lack of understanding of melt pool dynamics. To study the fundamental behavior of the melt pool, both geometric and thermal sensing with high spatial and temporal resolutions are necessary. This work applies and integrates three advanced sensing technologies: synchrotron X-ray imaging, high-speed IR camera, and high-spatial-resolution IR camera to characterize the evolution of the melt pool shape, keyhole, vapor plume, and thermal evolution in Ti–6Al–4V and 410 stainless steel spot melt cases. Aside from presenting the sensing capability, this paper develops an effective algorithm for high-speed X-ray imaging data to identify melt pool geometries accurately. Preprocessing methods are also implemented for the IR data to estimate the emissivity value and extrapolate the saturated pixels. Quantifications on boundary velocities, melt pool dimensions, thermal gradients, and cooling rates are performed, enabling future comprehensive melt pool dynamics and microstructure analysis. The study discovers a strong correlation between the thermal and X-ray data, demonstrating the feasibility of using relatively cheap IR cameras to predict features that currently can only be captured using costly synchrotron X-ray imaging. Such correlation can be used for future thermal-based melt pool control and model validation.

47 OTHER INSTRUMENTATION↗
DOE OSTI2021

Solidification texture, variant selection, and phase fraction in a spot-melt electron-beam powder bed fusion processed Ti-6Al-4V

The effect of a spot melt strategy on the solidification texture, variant selection, phase fraction, and their variations along the build height was investigated in comparison to a conventional linear melt strategy. Ti-6Al-4V alloy samples were manufactured by an electron-beam powder bed fusion process using two different melt strategies and characterized using high-energy synchrotron x-ray diffraction. The linear and spot melt cases resulted in β<100> cube and fiber textures, respectively, with the cube/fiber axis nearly parallel to the build direction. The α phase exhibited Burgers orientation relationship (BOR) with the parent β phase for both melt strategies. Although all of the key texture components and the BOR between the α and β phases were consistently observed in both cases along the build height, there were several measurable differences between the two. At the top of the build height, the β<100> build texture intensity was stronger in the linear case. However, the texture intensity in the linear case decreased gradually from the top to near the substrate, whereas the spot melt case did not show this trend. Moreover, the BOR was examined along the build height and the results showed that there is a distinct variant selection in the spot melt case, unlike the linear case. Specifically, the planar variants sharing ($\bar101$) β || (0002) α with [$\bar2\bar2\bar2$]β and [$2\bar22$]β were the most prominent in the spot melt, but no preference was identified in the directional variants. The β phase fraction was slightly lower in the spot melt case compared to the linear case. In both the cases, the β phase fraction decreased moving towards the substrate but remained significantly higher than that of the powder feedstock. Overall, the novel spot melt strategy produced a more homogeneous microstructure in terms of both the phase fraction and texture across the build height.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Deformation and fracture behavior of a laser powder bed fusion processed stainless steel: In situ synchrotron x-ray computed microtomography study

Tensile plastic deformation and fracture behavior of a laser powder bed fusion processed 316L stainless steel alloy was investigated in situ using high-resolution synchrotron x-ray computed microtomography (sXCT). Three different cases were studied: (1) specimen A1, near full-density with initial porosity of 0.04%, (2) specimen B1, initial lack-of-fusion (LOF) porosity of about 3% with the major axis of defects aligned nearly perpendicular to the tensile loading direction (LD), and (3) specimen B, similar to B1 but with the major axis of LOF defects aligned nearly parallel to LD. The effects of type, density, and orientation of defects in as-printed samples on plastic deformation and failure modes were studied by analyzing sXCT image sequences and quantitative defect properties. Specifically, the evolutions of porosity, size, aspect ratio, and angle of gas pores and LOF defects were characterized as a function of applied strain. Moreover, interactions between as-printed defects and deformation-induced crack propagation were investigated. The tensile behavior of specimen A1 was comparable to that of a commercial wrought plate. Furthermore, the quantitative in-situ sXCT results showed a void-growth phenomenon in A1 but without noticeable coalescence, resulting in a ductile cup-cone failure. Specimen B1 showed damage-driven brittle failure with limited plasticity due to early and rapid propagation of open voids. On the other hand, specimen B, with a similar amount of LOF defects as B1, showed deceivingly strong and ductile tensile behavior similar to A1 without any major crack propagations due to the favorable orientation relationship between LOF defects and the LD.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Dynamic recrystallization of a wrought magnesium alloy: Grain size and texture maps and their application for mechanical behavior predictions

Effect of dynamic recrystallization (DRX) on the grain refinement and texture modification was studied by conducting a series of hot compression on AZ31B Mg alloy. Processing-grain size-texture maps were established as a function of temperature, strain rate, strain, and the Zener-Hollomon parameter (Z). Moreover, influence of simultaneous changes in the grain size and texture on tensile yield strength and ductility of the hot-worked Mg alloy was studied using the grain size and texture maps established. The processing-grain size map showed that the DRX grain size decreased with the increase in Z, also revealing various characteristics ranging from a grain growth, grain refinement, to a bimodal distribution of ultrafine grains and partially recrystallized grains. The effect of twinning on the grain refinement was also evident at high Z conditions. The processing-texture map revealed that the initial fiber texture was altered significantly to a shear, off-normal, or extension-twin texture with the increase in Z. The Schmid-factor maps were calculated to identify a dominant deformation mode during a subsequent tensile deformation of the hot-worked samples. Finally, a corresponding Hall-Petch relationship for each dominant deformation mode was used to establish tensile yield-strength maps, which agree well with the measured data.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Influence of defect characteristics on tensile deformation of an additively manufactured stainless steel: Evolutions of texture and intergranular strain

The micromechanics of plastic deformation behavior of a selective laser melt processed austenitic stainless steel were studied by investigating the evolutions of texture and intergranular strain using in situ high-energy synchrotron x-ray diffraction (sXRD). The effects of defect characteristics on tensile behavior were studied using three different samples: a near full-density sample with elliptical closed voids and two samples with lack-of-fusion (LOF) defects tensile loaded either perpendicular or parallel to their major axes. The evolutions of pole figures and inverse pole figures show that the full-density specimen develops a strong (111)/(200) fiber texture along the loading direction. For both LOF specimens, the evolution of texture is qualitatively similar to the full-density counterpart, but the development of the fiber texture was much slower, indicating a limited plasticity at a given macroscopic strain. The intergranular strain evolution in the full-density specimen is similar to that of a wrought 316L stainless steel. Conversely, a significantly different intergranular strain development was observed in a LOF specimen, where tensile strain development was observed in both the axial and transverse directions. Finally, the influence of defect type, density, and orientation on the local stress states in the steel matrix and the evolutions of intergranular strains is discussed.

36 MATERIALS SCIENCE↗
NASA NTRS2006

Non-Contact Measurements of Creep Properties of Refractory Materials

State-of-the-art technologies for hypersonic aircraft, nuclear electric/thermal propulsion for spacecraft, and more efficient jet engines are driving ever more demanding needs for high-temperature (>2000 C) materials. At such high temperatures, creep rises as one of the most important design factors to be considered. Since conventional measurement techniques for creep resistance are limited to about 17OO0C, a new technique is in demand for higher temperatures. This paper presents a non-contact method using electrostatic levitation (ESL) which is applicable to both metallic and non-metallic materials. The samples were rotated quickly enough to cause creep deformation by centrifugal acceleration. The deformation of the samples was captured with a high speed camera and then the images were analyzed to estimate creep resistance. Finite element analyses were performed and compared to the experiments to verify the new method. Results are presented for niobium and tungsten, representative refractory materials at 2300 C and 2700 C respectively.

Lee, Jonghyun↗
NASA NTRS2006

Analytical, Numerical, and Experimental Investigation on a Non-Contact Method for the Measurements of Creep Properties of Ultra-High-Temperature Materials

Responsive access to space requires re-use of components such as rocket nozzles that operate at extremely high temperatures. For such applications, new ultra-hightemperature materials that can operate over 2,000 C are required. At the temperatures higher than the fifty percent of the melting temperature, the characterization of creep properties is indispensable. Since conventional methods for the measurement of creep is limited below 1,700 C, a new technique that can be applied at higher temperatures is strongly demanded. This research develops a non-contact method for the measurement of creep at the temperatures over 2,300 C. Using the electrostatic levitator in NASA MSFC, a spherical sample was rotated to cause creep deformation by centrifugal acceleration. The deforming sample was captured with a digital camera and analyzed to measure creep deformation. Numerical and analytical analyses have also been conducted to compare the experimental results. Analytical, numerical, and experimental results showed a good agreement with one another.

Lee, Jonghyun↗
NASA NTRS2005

Non-contact Creep Resistance Measurement for Ultra-high temperature Materials

Continuing pressures for higher performance and efficiency in propulsion are driving ever more demanding needs for high-temperature materials. Some immediate applications in spaceflight include combustion chambers for advanced chemical rockets and turbomachinery for jet engines and power conversion in nuclear-electric propulsion. In the case of rockets, the combination of high stresses and high temperatures make the characterization of creep properties very important. Creep is even more important in the turbomachinery, where a long service life is an additional constraint. Some very high-temperature materials are being developed, including platinum group metals, carbides, borides, and silicides. But the measurement of creep properties at very high temperatures is itself problematic, because the testing instrument must operate at such high temperatures. Conventional techniques are limited to about 1700 C. A new, containerless technique for measuring creep deformation has been developed. This technique is based on electrostatic levitation (ESL) of a spherical sample, which is heated to the measurement temperature and rotated at a rate such that the centrifugal acceleration causes creep deformation. Creep of samples has been demonstrated at up to 2300 C in the ESL facility at NASA MSFC, while ESL itself has been applied at over 3000 C, and has no theoretical maximum temperature. The preliminary results and future directions of this NASA-funded research collaboration will be presented.

Hyers, Robert W.↗