Engineering topics
Publications and source records attributed to Choi, Wookjin.
The overall objective of this program is to achieve ≥ 22.5 % bifacial p-type cell efficiencies by developing and implementing optimized homogeneous phosphorus (P) emitter on the front and tunnel oxide passivated boron (B) doped poly-Si contact (p-TOPCon) on the rear side, in combination with advanced fine-line screen-printing metallization and high bulk lifetime in the base material.
The overall objective of this program is to achieve ~23% bifacial n-type cell efficiencies by developing and implementing optimized homogeneous or selective boron (B) emitter on front and tunnel oxide passivated contact (TOPCon) on rear side, in combination with advanced fine-line screen-printing metallization with floating busbars. During this research project, first we developed a technology roadmap to drive the 21% n-PERT cell efficiency from 21% to 23% by transforming the cell design to n-TOPCon and establishing the requirements for each layer, including B emitter, rear n-TOPCon, n-base Si and screen-printed contacts. Next, consistent with our roadmap, we developed advanced homogeneous implanted B emitter (150-180 Ω/⌫) passivated with ALD Al 2 O 3 layer capped with PECVD SiN x /SiO x double-layer antireflection coating This gave a very low recombination current density of 10-15 fA/cm 2 prior to metallization. In addition, we demonstrated metallized recombination current density of ~31 fA/cm 2 for this advanced homogeneous B emitter with industrial screen-printed, fire-through contacts with 40 μm wide grid lines, floating busbars and implementation of an advanced Ag-Al paste which resulted in local or reduced area metal-Si contact under the grid lines with virtually no emitter surface etching. This paste reduced the full area metallized J oe,metal from >1100 fA/cm 2 to ~700 fA/cm 2 . We also developed novel processes for the formation of p + /p ++ selective B emitter by a) single B diffusion with selective etch back and b) two-steps diffusion with implanted B in field region and APCVD B diffusion under the metal grid. We achieved very low un-metallized recombination current density (J 0 ) of ~18 fA/cm 2 for the selective p ++ p + emitters (30/150 Ω/⌫) and metallized J 0 of ~28 fA/cm 2 with ~3% screen-printed metal contact to p ++ regions. Next, we developed the technology for n-TOPCon by growing phosphorus-doped LPCVD and PECVD poly-Si on top of ~ 15Å chemically grown (NAO) tunnel oxide. After an optimized anneal at 875 °C for 30 min, passivated n-TOPCon have unmetallized J 0 of ~ 5 fA/cm 2 which went down further to ~ 1 fA/cm 2 after a 700 Å SiN x capping layer and simulated contact firing cycle at 770 °C. After screen-printed fire-through metallization on this n-TOPCon with ~13% metal coverage, metallized J 0 value increased to only ~5 fA/cm 2 which is among the lowest reported value to the best of our knowledge for screen-printed metallization. Finally, we integrated all the above technology innovations and enhancements and demonstrated low-cost manufacturable screen-printed n-TOPCon bifacial Si solar cell with ~23% efficiencies. Based on the experimental and theoretical understanding developed in this project, we have developed a new technology roadmap that shows that implementation of busbarless contacts, 10-20 ms bulk lifetime Si, and selective B emitter or selective TOPCon on the front can drive ~23% efficient cells achieved in this research to ~25% at low-cost.
The plasma charge injection technology reported earlier can be a low-cost alternative to the Al 2 O 3 passivation technology. The charge stability under sunlight exposure is a key concern. We investigated the light-induced loss of injected charge for different nitrogen-to-silicon atomic ratios (x=N/Si) of SiN x , and found drastic improvements in charge loss with increasing x-value and logarithmic time dependent charge decays. The best result indicated a sufficient charge amount can sustain over the module lifetime (25 years). Here, the charge loss is likely related to photo-generated free carriers and atomic hydrogens in SiN x .