NASA NTRS2014

Properties of Desert Sand and CMAS Glass

As-received desert sand from a Middle East country has been characterized for its phase composition and thermal stability. X-ray diffraction analysis showed the presence of quartz (SiO2), calcite (CaCO3), gypsum (CaSO4.2H2O), and NaAlSi3O8 phases in as-received desert sand and showed weight loss of approx. 35 percent due to decomposition of CaCO3 and CaSO4.2H2O when heated to 1400 C. A batch of as-received desert sand was melted into calcium magnesium aluminosilicate (CMAS) glass at approx. 1500 C. From inductively coupled plasma-atomic emission spectrometry, chemical composition of the CMAS glass was analyzed to be 27.8CaO-4MgO-5Al2O3-61.6SiO2-0.6Fe2O3-1K2O (mole percent). Various physical, thermal and mechanical properties of the glass have been evaluated. Bulk density of CMAS glass was 2.69 g/cc, Young's modulus 92 GPa, Shear modulus 36 GPa, Poisson's ratio 0.28, dilatometric glass transition temperature (T (sub g)) 706 C, softening point (T (sub d)) 764 C, Vickers microhardness 6.3 +/- 0.4 GPa, indentation fracture toughness 0.75 +/- 0.15 MPa.m (sup 1/2), and coefficient of thermal expansion (CTE) 9.8 x 10 (exp -6)/degC in the temperature range 25 to 700 C. Temperature dependence of viscosity has also been estimated from various reference points of the CMAS glass using the Vogel-Fulcher-Tamman (VFT) equation. The glass remained amorphous after heat treating at 850 C for 10 hr but crystallized into CaSiO3 and Ca-Mg-Al silicate phases at 900 C or higher temperatures. Crystallization kinetics of the CMAS glass has also been investigated by differential thermal analysis (DTA). Activation energies for the crystallization of two different phases in the glass were calculated to be 403 and 483 kJ/mol, respectively.

Desert sand↗

NASA NTRS2008

Mixed Mode Fracture of Plasma Sprayed Thermal Barrier Coatings: Effects of Anisotropy and Heterogeneity

The combined mode I-mode II fracture behavior of anisotropic ZrO2-8wt%Y2O3 thermal barrier coatings was determined in asymmetric flexure loading at both ambient and elevated temperatures. A fracture envelope of KI versus KII was determined for the coating material at ambient and elevated temperatures. Propagation angles of fracture as a function of KI/KII were also determined. The mixed-mode fracture behavior of the microsplat coating material was modeled using Finite Element approach to account for anisotropy and micro cracked structures, and predicted in terms of fracture envelope and propagation angle using mixed-mode fracture theories.

Zhu, Dongming↗

NASA NTRS2008

Impact Resistance of EBC Coated SiC/SiC Composites

Impact performance of 2-D woven SiC/SiC composites coated with 225 and 525 m thick environmental barrier coating (EBC) was investigated. The composites were fabricated by melt infiltration and the EBC was deposited by plasma spray. Impact tests were conducted at room temperature and at 1316 C in air using 1.59-mm diameter steel-balls at projectile velocities ranging from 110 to 375 m/s. Both microscopy and nondestructive evaluation (NDE) methods were used to determine the extent of damage in the substrate and coating with increasing projectile velocity. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. At projectile velocities less than 125 m/s, no detectable damage was noticed in the MI SiC/SiC composites coated with 525 m EBC. With increase in projectile velocity beyond this value, spallation of EBC layers, delamination of fiber plies, and fiber fracture were detected. At a fixed projectile velocity, the composites coated with 525 m EBC showed less damage than the composite coated with 225 m EBC. Both types of EBC coated composites retained a large fraction of the baseline properties of as-fabricated composites and exhibited non-brittle failure after impact testing at projectile velocities up to 375 m/s. Exposure of impact tested specimens in a moisture environment at 1316 C for 500 hr indicated that the through-the-thickness cracks in the EBC coating and delamination cracks in the substrate generated after impact testing acted as conduits for internal oxidation.

Fox, Dennis S.↗

NASA NTRS2008

Impact Resistance of Environmental Barrier Coated SiC/SiC Composites

Impact performance of 2D woven SiC/SiC composites coated with 225 and 525 microns thick environmental barrier coating (EBC) was investigated. The composites were fabricated by melt infiltration and the EBC was deposited by plasma spray. Impact tests were conducted at room temperature and at 1316 C in air using 1.59 mm diameter steel-balls at projectile velocities ranging from 110 to 375 m/s . Both microscopy and non-destructive evaluation (NDE) methods were used to determine the extent of damage in the substrate and coating with increasing projectile velocity. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. At projectile velocities less than 125 m/s , no detectable internal damage was noticed in the MI SiC/SiC composites coated with 525 microns EBC. With increase in projectile velocity beyond this value, spallation of EBC layers, delamination of fiber plies, and fiber fracture were detected. At a fixed projectile velocity, the composites coated with 525 microns EBC showed less damage than those coated with 225 microns EBC. Both types of coated composites retained a large fraction of the baseline properties of the as-fabricated composites and exhibited non-brittle failure after impact testing. Furnace exposure of impacted specimens in a moisture environment at 1316 C for 500 h indicated that the through-the-thickness cracks in the coating and delamination cracks in the substrate generated after impact testing acted as conduits for internal oxidation.

Bhatt, Ramakrishna T.↗

NASA NTRS2008

Impact Resistance of Uncoated SiC/SiC Composites

Two-dimensional woven SiC/SiC composites fabricated by melt infiltration method were impact tested at room temperature and at 1316 C in air using 1.59-mm diameter steel-ball projectiles at velocities ranging from 115 to 400 m/s. The extent of substrate damage with increasing projectile velocity was imaged and analyzed using optical and scanning electron microscopy, and non-destructive evaluation (NDE) methods such as pulsed thermography, and computed tomography. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. Results indicate that at 115 m/s projectile velocity, the composite showed no noticeable surface or internal damage and retained its as-fabricated mechanical properties. As the projectile velocity increased above this value, the internal damage increased and mechanical properties degraded: At velocities >300 m/s, the projectile penetrated through the composite, but the composite retained approx.50% of the ultimate tensile strength of the as-fabricated composite and exhibited non-brittle failure. Predominant internal damages are delamination of fiber plies, fiber fracture and matrix shearing.

Bhatt, Ramakrishna T.↗

NASA NTRS2007

Glass/BNNT Composite for Sealing Solid Oxide Fuel Cells

A material consisting of a barium calcium aluminosilicate glass reinforced with 4 weight percent of boron nitride nanotubes (BNNTs) has shown promise for use as a sealant in planar solid oxide fuel cells (SOFCs).

Bansal, Narottam P.↗

NASA NTRS2007

Glass/Ceramic Composites for Sealing Solid Oxide Fuel Cells

A family of glass/ceramic composite materials has been investigated for use as sealants in planar solid oxide fuel cells. These materials are modified versions of a barium calcium aluminosilicate glass developed previously for the same purpose. The composition of the glass in mole percentages is 35BaO + 15CaO + 5Al2O3 + 10B2O3 + 35SiO2. The glass seal was found to be susceptible to cracking during thermal cycling of the fuel cells. The goal in formulating the glass/ ceramic composite materials was to (1) retain the physical and chemical advantages that led to the prior selection of the barium calcium aluminosilicate glass as the sealant while (2) increasing strength and fracture toughness so as to reduce the tendency toward cracking. Each of the composite formulations consists of the glass plus either of two ceramic reinforcements in a proportion between 0 and 30 mole percent. One of the ceramic reinforcements consists of alumina platelets; the other one consists of particles of yttria-stabilized zirconia wherein the yttria content is 3 mole percent (3YSZ). In preparation for experiments, panels of the glass/ceramic composites were hot-pressed and machined into test bars.

Bansal, Narottam P.↗

NASA NTRS2006

Apparatus for Hot Impact Testing of Material Specimens

An apparatus for positioning and holding material specimens is a major subsystem of a system for impact testing of the specimens at temperatures up to 1,500 C. This apparatus and the rest of the system are designed especially for hot impact testing of advanced ceramics, composites, and coating materials. The apparatus includes a retaining fixture on a rotating stage on a vertically movable cross support driven by a linear actuator. These components are located below a furnace wherein the hot impact tests are performed (see Figure 1). In preparation for a test, a specimen is mounted on the retaining fixture, then the cross support is moved upward to raise the specimen, through an opening in the bottom of the furnace, to the test position inside the furnace. On one side of the furnace there is another, relatively small opening on a direct line to the specimen. Once the specimen has become heated to the test temperature, the test is performed by using an instrumented external pressurized-gas-driven gun to shoot a projectile through the side opening at the specimen.

Pawlik, Ralph J.↗

NASA NTRS2006

Foreign Object Damage in a Gas-Turbine Grade Silicon Nitride by Spherical Projectiles of Various Materials

Assessments of foreign object damage (FOD) of a commercial, gas-turbine grade, in situ toughened silicon nitride ceramic (AS800, Honeywell Ceramics Components) were made using four different projectile materials at ambient temperature. AS800 flexure target specimens rigidly supported were impacted at their centers in a velocity range from 50 to 450 m/s by spherical projectiles with a diameter of 1.59 mm. Four different projectile materials were used including hardened steel, annealed steel, silicon nitride ceramic, and brass. Post-impact strength of each target specimen impacted was determined as a function of impact velocity to appraise the severity of local impact damage. For a given impact velocity, the degree of strength degradation was greatest for ceramic balls, least for brass balls, and intermediate for annealed and hardened steel balls. For steel balls, hardened projectiles yielded more significant impact damage than annealed counterparts. The most important material parameter affecting FOD was identified as hardness of projectiles. Impact load as a function of impact velocity was quasi-statically estimated based on both impact and static indentation associated data.

Choi, Sung R.↗

NASA NTRS2006

Assessments of Fracture Toughness of Monolithic Ceramics-SEPB Versus SEVNB Methods

Fracture toughness of a total of 13 advanced monolithic ceramics including silicon nitrides, silicon carbide, aluminas, and glass ceramic was determined at ambient temperature by using both single edge precracked beam (SEPB) and single edge v-notched beam (SEVNB) methods. Relatively good agreement in fracture toughness between the two methods was observed for advanced ceramics with flat R-curves; whereas, poor agreement in fracture toughness was seen for materials with rising R-curves. The discrepancy in fracture toughness between the two methods was due to stable crack growth with crack closure forces acting in the wake region of cracks even in SEVNB test specimens. The effect of discrepancy in fracture toughness was analyzed in terms of microstructural feature (grain size and shape), toughening exponent in R-curve, and stable crack growth determined using back-face strain gaging.

Choi, Sung R.↗

NASA NTRS2006

Life Limiting Behavior in Interlaminar Shear of Continuous Fiber-Reinforced Ceramic Matrix Composites at Elevated Temperatures

Interlaminar shear strength of four different fiber-reinforced ceramic matrix composites was determined with doublenotch shear test specimens as a function of test rate at elevated temperatures ranging from 1100 to 1316 C in air. Life limiting behavior, represented as interlaminar shear strength degradation with decreasing test rate, was significant for 2-D crossplied SiC/MAS-5 and 2-D plain-woven C/SiC composites, but insignificant for 2-D plain-woven SiC/SiC and 2-D woven Sylramic (Dow Corning, Midland, Michigan) SiC/SiC composites. A phenomenological, power-law delayed failure model was proposed to account for and to quantify the rate dependency of interlaminar shear strength of the composites. Additional stress rupture testing in interlaminar shear was conducted at elevated temperatures to validate the proposed model. The model was in good agreement with SiC/MAS-5 and C/SiC composites, but in poor to reasonable agreement with Sylramic SiC/SiC. Constant shear stress-rate testing was proposed as a possible means of life prediction testing methodology for ceramic matrix composites subjected to interlaminar shear at elevated temperatures when short lifetimes are expected.

Choi, Sung R.↗

NASA NTRS2006

Assessments of Mechanical and Life Limiting Properties of Two Candidate Silicon Nitrides for Stirling Convertor Heater Head Applications

NASA Glenn Research Center is developing advanced technology for Stirling convertors with a target of significantly improving the specific power and efficiency of the convertor and overall generator for Mars rovers and deep space missions. One specific approach to the target has been recognized as the use of appropriate high-temperature materials. As a series of ceramic material approaches in Advanced Stirling Convertor Development Program in fiscal year 2005, two commercial, structural silicon nitrides AS800 (Honeywell, Torrence, California) and SN282 (Kyocera, Vancouver, Washington) were selected and their mechanical and life limiting properties were characterized at 1050 C in air. AS800 exhibited both strength and Weibull modulus greater than SN282. A life limiting phenomenon was apparent in AS800 with a low slow crack growth parameter n = 15; whereas, a much increased resistance to slow crack growth was found in SN282 with n greater than 100. Difference in elastic modulus and thermal conductivity was negligible up to 1200 C between the two silicon nitrides. The same was true for the coefficient of thermal expansion up to 1400 C.

Choi, Sung R.↗

NASA NTRS2005

Solid Oxide Fuel Cell Seal Glass - BN Nanotubes Composites

Solid oxide fuel cell seal glass G18 composites reinforced with approx.4 weight percent of BN nanotubes were fabricated via hot pressing. Room temperature strength and fracture toughness of the composite were determined by four-point flexure and single edge V-notch beam methods, respectively. The strength and fracture toughness of the composite were higher by as much as 90% and 35%, respectively, than those of the glass G18. Microscopic examination of the composite fracture surfaces using SEM and TEM showed pullout of the BN nanotubes, similar in feature to fiber-reinforced ceramic matrix composites with weak interfaces. Other mechanical and physical properties of the composite will also be presented.

Bansal, Narottam P.↗

NASA NTRS2005

Boron Nitride Nanotubes-Reinforced Glass Composites

Boron nitride nanotubes of significant lengths were synthesized by reaction of boron with nitrogen. Barium calcium aluminosilicate glass composites reinforced with ~4 weight percent of BN nanotubes were fabricated by hot pressing. Ambient-temperature flexure strength and fracture toughness of the glass-BN nanotube composites were determined. The strength and fracture toughness of the composite were higher by as much as 90 and 35 percent, respectively, than those of the unreinforced glass. Microscopic examination of the composite fracture surfaces showed pullout of the BN nanotubes. The preliminary results on the processing and improvement in mechanical properties of BN nanotube reinforced glass matrix composites are being reported here for the first time.

Bansal, Narottam↗

NASA NTRS2005

Strong, Tough Glass Composites Developed for Solid Oxide Fuel Cell Seals

A fuel cell is an electrochemical device that continuously converts the chemical energy of a fuel directly into electrical energy. It consists of an electrolyte, an anode, and a cathode. Various types of fuel cells are available, such as direct methanol fuel cells, alkaline fuel cells, proton-exchange-membrane fuel cells, phosphoric acid fuel cells, molten carbonate fuel cells, and solid oxide fuel cells (SOFCs). The salient features of an SOFC are all solid construction and high-temperature electrochemical-reaction-based operation, resulting in clean, efficient power generation from a variety of fuels. SOFCs are being developed for a broad range of applications, such as portable electronic devices, automobiles, power generation, and aeronautics.

Bansal, Narottam P.↗

NASA NTRS2005

Thermographic Characterization of Impact Damage in SiC/SiC Composite Materials

SiC/SiC composite materials targeted as turbine components for next-generation aero-engines are being investigated at NASA Glenn Research Center. In order to examine damage mechanisms in these materials, SiC/SiC coupons were impacted with 1.59 mm diameter steel spheres at increasing velocities from 115 m/s to 400 m/s. Pulsed thermography, a nondestructive evaluation technique that monitors the thermal response of a sample over time, was utilized to characterize the impact damage. A thermal standard of similar material was fabricated to aid in the interpretation of the thermographic data and to provide information regarding thermography system detection capabilities in 2.4 mm thick SiC/SiC composite materials. Flat bottom holes at various depths with aspect ratios greater than 2.5 were detectable in the thermal images. In addition, the edges of holes at depths of 1.93 mm into the sample were not as resolvable as flat bottom holes closer to the surface. Finally, cooling behavior was characterized in SiC/SiC materials and used to determine impact damage depth within an 8.5% error of a known depth.

Fox, Dennis S.↗

NASA NTRS2005

Damage Accumulation and Failure of Plasma-Sprayed Thermal Barrier Coatings under Thermal Gradient Cyclic Conditions

Thermal barrier coatings will be more aggressively designed to protect gas turbine engine hot-section components in order to meet future engine higher fuel efficiency and lower emission goals. A fundamental understanding of the sintering and thermal cycling induced delamination of thermal barrier coating systems under engine-like heat flux conditions will potentially help to improve the coating temperature capability. In this study, a test approach is established to emphasize the real-time monitoring and assessment of the coating thermal conductivity, which can initially increase under the steady-state high temperature thermal gradient test due to coating sintering, and later decrease under the thermal gradient cyclic test due to coating cracking and delamination. Thermal conductivity prediction models have been established for a ZrO2-(7- 8wt%)Y2O3 model coating system in terms of heat flux, time, and testing temperatures. The coating delamination accumulation is then assessed based on the observed thermal conductivity response under the combined steady-state and cyclic thermal gradient tests. The coating thermal gradient cycling associated delaminations and failure mechanisms under simulated engine heat-flux conditions will be discussed in conjunction with the coating sintering and fracture testing results.

Zhu, Dongming↗

NASA NTRS2005

Effect of Projectile Materials on Foreign Object Damage of a Gas-Turbine Grade Silicon Nitride

Foreign object damage (FOD) behavior of AS800 silicon nitride was determined using four different projectile materials at ambient temperature. The target test specimens rigidly supported were impacted at their centers by spherical projectiles with a diameter of 1.59 mm. Four different types of projectiles were used including hardened steel balls, annealed steel balls, silicon nitride balls, and brass balls. Post-impact strength of each target specimen impacted was determined as a function of impact velocity to better understand the severity of local impact damage. The critical impact velocity where target specimens fail upon impact was highest with brass balls, lowest with ceramic ball, and intermediate with annealed and hardened steel balls. Degree of strength degradation upon impact followed the same order as in the critical impact velocity with respect to projectile materials. For steel balls, hardened projectiles yielded more significant impact damage than annealed counterparts. The most important material parameter affecting FOD was identified as hardness of projectiles and was correlated in terms of critical impact velocity, impact deformation, and impact load.

Choi, Sung R.↗