Oxide nucleation via threshold-driven volume instability in Ni oxidation

Oxide nucleation dictates the onset of metal oxidation, yet the atomistic pathways bridging initial oxygen adsorption to bulk phase transformation remain elusive. Here, we utilize in-situ atomic-resolution imaging to directly capture the nucleation of nickel oxide, revealing a threshold-driven, cooperative transformation of Ni into NiO. Our observations identify a distinct incubation period during which oxygen progressively accumulates in subsurface layers. Once a critical concentration and penetration depth are reached, a collective lattice reconfiguration is triggered, abruptly converting multiple Ni layers into NiO. Atomistic simulations corroborate this mechanism, identifying a cooperative lattice instability induced by subsurface oxygen saturation. These results establish subsurface oxygen incorporation as the missing mechanistic link between surface adsorption and three-dimensional oxide formation, providing an atomistic framework to understand and control reactive phase transformations in materials synthesis, catalysis, and degradation.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Surface Self-Diffusion Induced Sintering of Nanoparticles

Despite the critical role of sintering phenomena in constraining the long-term durability of nanosized particles, a clear understanding of nanoparticle sintering has remained elusive due to the challenges in atomically tracking the neck initiation and discerning different mechanisms. Through the integration of in situ transmission electron microscopy and atomistic modeling, this study uncovers the atomic dynamics governing the neck initiation of Pt–Fe nanoparticles via a surface self-diffusion process, allowing for coalescence without significant particle movement. Real-time imaging reveals that thermally activated surface morphology changes in individual nanoparticles induce significant surface self-diffusion. Further, the kinetic entrapment of self-diffusing atoms in the gaps between closely spaced nanoparticles leads to the nucleation and growth of atomic layers for neck formation. This surface self-diffusion-driven sintering process is activated at a relatively lower temperature compared to the classic Ostwald ripening and particle migration and coalescence processes. The fundamental insights have practical implications for manipulating the morphology, size distribution, and stability of nanostructures by leveraging surface self-diffusion processes.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Atomic-Scale Visualization of Surface Segregation and Ordering of Pt in a Dilute Cu(Pt) Alloy under a Hydrogen Atmosphere

Surface segregation is a common phenomenon in alloys exposed to reactive atmospheres, yet the atomic mechanisms underlying surface structure and composition dynamics remain largely unexplored. Using a combination of environmental transmission electron microscopy observations and atomistic modeling, here we report the surface segregation process of Pt atoms in a dilute Pt(Cu) alloy and determine the distribution of Pt atoms at both atomically flat and stepped surfaces of the Pt(Cu) alloy at elevated temperatures and in a hydrogen gas atmosphere. Through directly probing Pt segregation, we find that Pt atoms segregated on the (100) surface exhibit a p(2 × 2) ordering, with ~25% Pt occupancy. In contrast, on the stepped (410) surface, hydrogen adsorption induces Pt segregation, initially occurring at the step edges, which then expands to the terrace sites upon increased hydrogen coverage, resulting in an ordered distribution of segregated Pt atoms with ~22% occupancy. Finally, these observations offer mechanistic insights into the structure and composition dynamics of the topmost atomic layer of the alloy in response to environmental stimuli and hold practical implications for the design and optimization of catalysts based on Pt group metals.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Enhancing Stability of Surface Au under Oxidizing Conditions through Reduced Bulk Au Content

Contrary to the common assumption that a higher bulk content of precious metals facilitates the preservation of more surface noble metal by serving as a reservoir for surface enrichment, we demonstrate that a lower bulk content of Au results in a more stable arrangement of Au atoms at the surface of Cu–Au nanoparticles when exposed to an O 2 atmosphere. Using ambient pressure X-ray photoelectron spectroscopy, we investigate the surface segregation and oxidation behavior of Cu–Au nanoparticles across various compositions. Here, our results reveal that in Au-rich nanoparticles exposed to an H 2 atmosphere, surface segregation prompts the formation of a continuous Au-enriched shell, which subsequently oxidizes into a complete CuO x shell upon transitioning to an O 2 atmosphere. Conversely, in Au-poor nanoparticles during H 2 treatment, segregation results in the emergence of Au clusters embedded within the surface layer, persisting upon exposure to O 2 . This unexpected phenomenon shows that reducing the bulk content of precious metals can enhance the surface stability of noble atoms under oxidizing conditions, as further demonstrated by comparing the catalytic performance of Cu–Au nanoparticles with varying Au bulk contents in CO oxidation.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Morphology‐controlled synthesis of multi‐metal‐based spinel oxide nanocatalysts and their performance for oxygen reduction

Abstract We present a one‐pot colloidal synthesis method for producing monodisperse multi‐metal (Co, Mn, and Fe) spinel nanocrystals (NCs), including nanocubes, nano‐octahedra, and concave nanocubes. This study explores the mechanism of morphology control, showcasing the pivotal roles of metal precursors and capping ligands in determining the exposed crystal planes on the NC surface. The cubic spinel NCs, terminated with exclusive {100}‐facets, demonstrate superior electrocatalytic activity for the oxygen reduction reaction (ORR) in alkaline media compared to their octahedral and concave cubic counterparts. Specifically, at 0.85 V, (CoMn)Fe 2 O 4 spinel oxide nanocubes achieve a high mass activity of 23.9 A/g and exhibit excellent stability, highlighting the promising ORR performance associated with {100}‐facets of multi‐metal spinel oxides over other low‐index and high‐index facets. Motivated by exploring the correlation between ORR performance and surface atom arrangement (active sites), surface element composition, as well as other factors, this study introduces a prospective approach for shape‐controlled synthesis of advanced spinel oxide NCs. It underscores the significance of catalyst shape control and suggests potential applications as nonprecious metal ORR electrocatalysts.

Li, Can↗
DOE OSTI2024

Observing Chemical and Morphological Changes in a Cu@TiO x Core@Shell Catalyst: Impact of Reversible Metal-Oxide Interactions on CO 2 Activation and Hydrogenation

A combination of several in-situ techniques (XRD, XAS, AP-XPS, E-TEM) was used to explore links between the structural and chemical properties of a Cu@TiO x catalyst under CO 2 hydrogenation conditions. The active phase of the catalyst involved an inverse oxide/metal configuration, but the initial core@shell motif was disrupted during the pre-treatment in H 2 . As a consequence of strong metal-support interactions, the titania shell cracked and Cu particles migrated from the core to on top of the oxide with the simultaneous formation of a Cu-Ti-O x phase. The generated Cu particles had a diameter of 20-40 nm and were decorated by small clusters of TiO x (< 5 nm in size). Results of in-situ XAS and XRD and images of E-TEM showed a very dynamic system, where the inverse oxide/metal configuration promoted the reactivity of the system towards CO 2 and H 2 . At room temperature, CO 2 oxidized the Cu nanoparticles (CO 2,gas → CO gas + O oxide ) inducing a redistribution of the TiO x clusters and big modifications in catalyst surface morphology. The generated oxide overlayer disappeared at elevated temperatures (> 180 °C) upon exposure to H 2 , producing a transient surface that was very active for the reverse water-gas shift reaction (CO 2 + H 2 → CO + H 2 O) but was not stable at 250 °C. When oxidation and reduction occurred at the same time, under a mixture of CO 2 and H 2 , the surface structure evolved toward a dynamic equilibrium that strongly depended on the temperature. Neither CO 2 nor H 2 can be considered as passive reactants. In the Cu@TiO x system, morphological changes were linked to variations in the composition of metal-oxide interfaces which were reversible with temperature or chemical environment and affected the catalytic activity of the system. Finally, the present study illustrates the dynamic nature of phenomena associated with the trapping and conversion of CO 2 .

36 MATERIALS SCIENCE↗