Titanium in silicon as a deep level impurity

Titanium inserted in silicon by diffusion or during Czochralski ingot growth is electrically active to a concentration level of about 4 x 10 to the 14th per cu cm. It is reported that Hall measurements after diffusion show conversion of lightly doped p-type Si to n-type due to a Ti donor level at E sub c -0.22 eV. In addition, in DLTS measurements of n(+)p structures this level shows as an electron (minority carrier) trap at E sub c -0.26 eV with an electron capture cross section of about 3 x 10 to the -15th per sq cm at 300 K. Finally, a Ti electrically active concentration of about 1.35 x 10 to the 13th per cu cm in p type Si results in a minority carrier (electron) lifetime of 50 nsec at 300 K.