Investigation of the structure, filler interaction and degradation of disulfide elastomers made by Reversible Radical Recombination Polymerization (R3P)

In this paper we report the synthesis and analysis of cyclic polydisulfides, their redox depolymerization as well as their interaction with carbon black. Cyclic poly(3,6-dioxa-1,8-octanedithiol)s (pDODT) were synthesized by Reversible Radical Recombination Polymerization (R3P). R3P is a scalable “green” polymerization process using triethylamine (TEA), H 2 O 2 and air for the polymerization of dithiol monomers. pDODTs were synthesized in 5 and 20 g batches. The effect of peroxide concentration (3, 5, 10, 20, 30%) was investigated. It was found that the molecular weights increased exponentially with increasing peroxide concentrations. At 30% peroxide concentration pDODTs with M n up to 400,000 g/mol and polydispersity of 2 were obtained. 700 and 800 MHz NMR were used for investigating the chemical structure of the polymers. The absence of thiol end group signals in polymers made with > 10wt % H 2 O 2 and M n < 100,000 g/mol, including a sample of a fractionated polymer with starting Mn = 600,000 g/mol, verified cyclic structures. Dithiothreitol reduced the polymers to monomer and a small percentage of oligomers. Carbon black was shown to increase the moduli of high molecular weight pDODTs. Swelling tests in chloroform showed that polymers made with 20 and 30w% peroxide swelled 14 and 10 times of their starting weight without dissolving, indicating chemical interaction between the polymers and carbon black. In conclusion, further analysis of these interesting elastomers, available at the 20 g scale, is in progress.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Linear Viscoelastic Properties of Putative Cyclic Polymers Synthesized by Reversible Radical Recombination Polymerization (R3P)

Linear viscoelastic properties in both melt and solution states are reported for a series of poly(3,6-dioxa-1,8-octanedithiol) (polyDODT) made by reversible radical recombination polymerization (R 3 P) under conditions designed to produce linear (LDODT), cyclic (RDODT) and linear-cyclic mixtures (LRDODT). PolyDODT is amorphous (T g < -50 °C) and highly flexible (entanglement molecular weight M e,lin ≈ 1850 g/mol for LDODT). PolyDODT’s low T g and low M e,lin enable characterization over a wide dynamic range and a wide range of dimensionless weight-average molecular weight Z w = M w /M e,lin . Measurements at temperatures from -57 °C to 100 °C provide up to 18 deades of reduced frequency, which is necessary to characterize RDODT melts with Z w from 23 to 300. The two highest molecular weight polymers in the present RDODT series have such high M w (406k and 556k g/mol) that mass spectrometry, NMR spectroscopy, and even chemical assays for chain ends are unable to rule out up to 2 mol% linear contaminant. By studying the samples in solution (using dilution to reduce Z w ) we could compare their dynamics with those of previously established high-purity polystyrene (PS) rings (limited to Z w ≤ 13.6). RDODT solutions with Z w < 15 (concentrations <5wt% for RDODT-406k and 556k) have dynamic moduli G^* that accord with LCCC-purified PS rings in terms of the frequency dependence (including the absence of a plateau), the progression of shapes of G* as a function of Z w , and the linear scaling of their zero-shear viscosity η0 with M w . The shape of G* as a function of Z w for solutions of RDODT-406k and -556k also accord with lower M w RDODT melts (which have ≤ 1.3mol% linear contaminant). Thus, measurement of the linear viscoelastic properties of appropriate concentrations of high M w (>200k g/mol) putative cyclic polymers, in which linear chains evade spectroscopic detection, may provide an alternative means (though not fully proven) of validation of sample purity. When Z w > 15 (including all seven RDODT melts and eight of their solutions), G* has a rubbery plateau. This suggests that the onset of entanglement-like behavior in rings requires 4-5-fold greater Z w than is required for linear chains. Further, the plateau moduli of RDODT samples are indistinguishable from G N o of the corresponding LDODT (melt or matched-concentration solutions). In entangled linear polymers, the observation that G N o is independent of Z w follows from limitations on lateral fluctuations due to neighboring chains becoming independent of position along a given chain. The present results for RDODT suggest that this holds for sufficiently long endless chains, too. While the RDODT have the same G N o as entangled LDODT, when Z w > 60 the terminal relaxation, if reached at all, of RDODT extends to orders of magnitude lower frequency than an entangled linear polymer of the same Z w . Consequently, the viscosity of RDODT with Z w > 60 increases with Z w much more strongly than the 3.4-power observed for entangled linear polymers. Lastly, these novel polymers, with disulfide-linked backbone and broad relaxation time distribution may prove important in relation to biodegradable elastomers and materials with exceptional low-frequency dissipation, extending at least 12 decades below the onset of the rubbery plateau.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗
DOE OSTI2022

PolyDODT: a macrocyclic elastomer with unusual properties

The effect of reaction conditions on the structure of poly(3,6-dioxa-1,8-octanedithiol) (polyDODT) made by Reversible Radical Recombination Polymerization (R3P) using triethylamine (TEA), H 2 O 2 and air was investigated. 800 MHz (1 and 2D) NMR was used to investigate the polymer structures. Sensitivity analysis provided direct evidence for high purity cyclic polyDODT up to M n ~ 100 000 g mol –1 . Here, comparative analysis by High Resolution Multidetector Size Exclusion Chromatography (SEC) using integrated data showed that the cycles had lower viscosity and were more compact (both for R g and R h ) than linear samples of similar molecular weight. However, differential data revealed unusual behavior. While lower molecular weight cyclic polymers eluted later and had lower intrinsic viscosity than their linear counterparts at the same molecular weight, at higher molecular weights the polymers showed strange behavior: both the diffusion coefficient measured by Quasielastic Light Scattering (QELS) and Mark–Houwink–Sakurada plots of intrinsic viscosity for linear and cyclic polyDODT were found to converge. R3P, an aqueous based “green” method is capable of producing polymers at the 10–100 g scale in the lab, which will allow more detailed studies of this new class of biodegradable elastomers so further experimentation can be performed to elucidate the reasons for the unusual findings.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Deep glassy state dynamic data challenge glass models: Elastic models

The idea of an “ideal” glass transition temperature has persisted at least since the work from Kauzmann when it was observed that the entropy of glass-forming liquids extrapolated to below that of the crystal, thus suggesting the need for a phase transition at a finite or non-zero absolute temperature. This thermodynamic paradox was also found to be related to the observations of a diverging of the extrapolated viscosity or relaxation times at a temperature near to this ideal glass transition. Recently, however, we have carried out experiments using both an ancient amber material and an ultra-stable amorphous fluoropolymer that challenge the ideas of the divergence of the viscosity or relaxation times at this ideal glass transition. In the present manuscript we have evaluated two theories of the glass transition that are based on ideas related to elasticity of the amorphous glass-forming material. We find that the models from both J. Dyre and his group and of K.S. Schweizer and his group not only show non-diverging behavior but are also in some agreement with the new data, though still showing somewhat slower dynamics than those observed in the experiments. The work shows that the data are good enough to distinguish between theories and it is suggested that other mechanisms may be needed to fully describe the non-diverging responses of the ultra-stable glasses.