DOE OSTI2024

Mechanical Milling – Induced Microstructure Changes in Argyrodite LPSCl Solid-State Electrolyte Critically Affect Electrochemical Stability

Microstructure of argyrodite solid-state electrolyte (SSE) critically affects lithium metal electrodeposition/dissolution. While the stability of unmodified SSE is mediocre, once optimized state-of-the-art electrochemical performance is achieved (symmetric cells, full cells with NMC811) without secondary interlayers or functionalized current collectors. Planetary mechanical milling in wet media (m-xylene) is employed to alter commercial Li 6 PS 5 Cl (LPSCl) powder. Quantitative stereology demonstrates how milling progressively refines grain and pore size/distribution in the SSE compact, increases its density, and geometrically smoothens the SSE-Li interface. Mechanical indentation demonstrates that these changes lead to reduced site-to-site variation in the compact's hardness. Milled microstructures promote uniform early-stage electrodeposition on foil collectors and stabilize solid electrolyte interphase (SEI) reactivity. Analysis of half-cells with bilayer electrolytes demonstrates the importance of microstructure directly contacting current collector, with interface roughness due to pore and grain size distribution being key. For the first time, short-circuiting Li metal dendrite is directly identified, employing 1.5 mm diameter “mini” symmetrical cell and cryogenic focused ion beam (cryo-FIB) electron microscopy. The branching sheet-like dendrite traverses intergranularly, filling the interparticle voids and forming an SEI around it. Importantly, mesoscale modeling reveals the relationship between Li-SSE interface morphology and the onset of electrochemical instability, based on underlying reaction current distribution.

25 ENERGY STORAGE↗
DOE OSTI2023

Roles of Mn and Co in the Air Synthesizability of Layered Oxide Cathodes for Lithium-Based Batteries

High-nickel layered oxides (LiNi 1-x-y Mn x Co y O 2 ) are the prevailing cathode materials for high-energy-density lithium-based batteries, but they are plagued with deleterious surface air instabilities stemming from residual lithium formation. These issues severely hinder mass production as cathode calcination is limited to a flowing oxygen atmosphere, which entails high manufacturing costs as opposed to simpler and more economical air calcination. Here, while higher Ni contents are known to worsen air instabilities, the influence of Mn and Co contents on impacting these phenomena are less elucidated. We herein present the synthesis in ambient air and flowing oxygen atmospheres of three cathode variants with the same Ni contents, but varying Mn and Co contents: LiNi 0.7 Mn 0.3 O 2 , LiNi 0.7 Mn 0.15 Co 0.15 O 2 , and LiNi 0.7 Co 0.3 O 2 . It is found that the critical parameter influencing the air stability of the cathodes is the average Ni oxidation state, which is greatly dependent on the Mn and Co contents. Substitution of Mn for Ni drives down the Ni oxidation state as Mn exists as Mn4 + and reduces surface residual lithium formation, which vastly improves the overall air stability and, therefore, the synthesizability in air, but with a penalty of lowered capacity. In contrast, substitution of Co for Ni maintains Ni 3+ as Co exists as Co 3+ , offering increased initial capacity, but worsens the air stability and cyclability as the driving force for residual lithium formation and surface reactivity is increased.

25 ENERGY STORAGE↗
DOE OSTI2023

Tuned Reactivity at the Lithium Metal–Argyrodite Solid State Electrolyte Interphase

Thin intermetallic Li 2 Te–LiTe 3 bilayer (0.75 µm) derived from 2D tellurene stabilizes the solid electrolyte interphase (SEI) of lithium metal and argyrodite (LPSCl, Li 6 PS 5 Cl) solid-state electrolyte (SSE). Tellurene is loaded onto a standard battery separator and reacted with lithium through single-pass mechanical rolling or transferred directly to SSE surface by pressing. State-of-the-art electrochemical performance is achieved, e.g., symmetric cell stable for 300 cycles (1800 h) at 1 mA cm -2 and 3 mAh cm -2 (25% DOD, 60 µm foil). Cryo-stage focused ion beam (Cryo-FIB) sectioning and Raman mapping demonstrate that the Li 2 Te–LiTe 3 bilayer impedes SSE decomposition. The unmodified Li–LPSCl interphase is electrochemically unstable with a geometrically heterogeneous reduction decomposition reaction front that extends deep into the SSE. Decomposition drives voiding in Li metal due to its high flux to the reaction front, as well as voiding in the SSE due to the associated volume changes. Analysis of cycled SSE found no evidence for pristine (unreacted) lithium metal filaments/dendrites, implying failure driven by decomposition phases with sufficient electrical conductivity that span electrolyte thickness. In conclusion, DFT calculations clarify thermodynamic stability, interfacial adhesion, and electronic transport properties of interphases, while mesoscale modeling examines interrelations between reaction front heterogeneity (SEI heterogeneity), current distribution, and localized chemo-mechanical stresses.

25 ENERGY STORAGE↗
DOE OSTI2022

Uncovering the Solvation Structure of LiPF 6 –Based Localized Saturated Electrolytes and Their Effect on LiNiO 2 –Based Lithium–Metal Batteries

Electrolytes play a critical role in stabilizing highly reactive lithium-metal anodes (LMAs) and high-voltage cathodes for rechargeable lithium-metal batteries (LMBs). Localized high concentration electrolytes (LHCEs) have achieved remarkable success in the context of LMBs. However, the state-of-the-art LHCEs are based on LiFSI salt, which is prohibitively expensive. Here, the utility of low-cost LiPF 6 salt in localized saturated electrolytes (LSEs) with a series of solvents and diluents in LMBs with cobalt-free LiNiO 2 cathode is systematically explored. Experimental and theoretical analyses reveal that the unique solvation structure formed not only changes the distribution of solvents and anions but also alters the atom–atom distances within them, leading to different reduction and oxidation stabilities compared to low-concentration electrolytes. In addition, LSEs help form LiF-rich interphase layers on the LMA and LiNiO 2 cathode, protecting the electrodes from degradation during cycling. Different LSEs also lead to differences in lithium plating morphology and impedance buildup during cycling, impacting the performance of LMBs. Finally, the solvent and diluent must be carefully selected for compatibility with a lithium salt when developing LHCEs and LSEs for LMBs.

25 ENERGY STORAGE↗
DOE OSTI2022

Paving Pathways Toward Long–Life Graphite/LiNi 0.5 Mn 1.5 O 4 Full Cells: Electrochemical and Interphasial Points of View

The high-voltage spinel cathode LiNi 0.5 Mn 1.5 O 4 (LNMO) with no cobalt and low nickel content is promising for lithium-ion batteries due to its high energy and power densities, good thermal stability, and low cost. However, its high operating voltage (≈4.7 V) results in a decomposition of the electrolyte, severe chemical crossover, and deterioration of electrode-electrolyte interphases (EEIs), hindering its practical viability. It is demonstrated here that by electrochemically pre-cycling the graphite in an electrolyte containing 30 wt.% fluoroethylene carbonate, a robust LiF-rich artificial solid electrolyte interphase can be constructed for surface protection; on the other hand, an electrochemical pre-lithiation of Fe-doped LNMO serves as a lithium source for graphite at a full-cell voltage of 2.6 V. As a result, the full cells with the as-modified electrodes deliver a high capacity of 129 mA h g –1 with an excellent capacity retention of 93% after 200 cycles, vastly outperforming the full cells with fresh electrodes (120 mA h g –1 initial capacity with 78% retention). Lastly, pathways toward long-life graphite||LNMO full cells are pictured based on the inspirations from the electrochemical modifications and in-depth analyses of the EEIs in this study.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Surface Stabilization with Fluorine of Layered Ultrahigh-Nickel Oxide Cathodes for Lithium-Ion Batteries

High-nickel layered oxide cathodes are key to meet the demands of the electric vehicle industry because of their high specific capacity. However, commercialization of these materials is hindered by critical challenges, such as phase transitions, particle cracking, aggressive surface reactivity, and thermal instability. Cation doping along with surface coating has proven to be an effective way to circumvent some of these issues to a large extent. Herein, fluorine coating is employed on a high-nickel Li[Ni 0.95 Mn 0.015 Co 0.02 Al 0.01 Mg 0.005 ]O 2 (NMCAM) cathode via a solution route. Detailed structural and electrochemical analyses indicate fluorine largely decorates the surface at low enough calcination temperatures. The cathode with 1 mol % fluorine coating exhibits a capacity retention of 71% after 500 cycles as compared to 59% for the control sample when cycled to a high cutoff voltage of 4.3 V in a full cell configuration with graphite anode. Post-mortem analysis of cycled electrodes reveals that surface reactivity is a major contributor to capacity fade as compared to particle cracking. Fluorine coating reduces surface reactivity and the depth to which rock-salt phase is formed on the surface during cycling. The thermal stability is also enhanced after fluorine coating as the material shows less heat release at high states of charge. Furthermore, this work demonstrates an effective, economical, and scalable way to stabilize the surface with fluorine and enhance the electrochemical performance of high-nickel cathodes.

25 ENERGY STORAGE↗
DOE OSTI2021

Multifunctional Separator Allows Stable Cycling of Potassium Metal Anodes and of Potassium Metal Batteries

Here, this is the first report of a multifunctional separator for potassium-metal batteries (KMBs). Here, double-coated tape-cast microscale AlF 3 on polypropylene (AlF 3 @PP) yields state-of-the-art electrochemical performance: symmetric cells are stable after 1000 cycles (2000 h) at 0.5 mA cm –2 and 0.5 mAh cm –2 , with 0.042 V overpotential. Stability is maintained at 5.0 mA cm –2 for 600 cycles (240 h), with 0.138 V overpotential. Postcycled plated surface is dendrite-free, while stripped surface contains smooth solid electrolyte interphase (SEI). Conventional PP cells fail rapidly, with dendrites at plating, and “dead metal” and SEI clumps at stripping. Potassium hexacyanoferrate(III) cathode KMBs with AlF 3 @PP display enhanced capacity retention (91% at 100 cycles vs 58%). AlF 3 partially reacts with K to form an artificial SEI containing KF, AlF 3 , and Al 2 O 3 phases. The AlF 3 @PP promotes complete electrolyte wetting and enhances uptake, improves ion conductivity, and increases ion transference number. The higher of K + transference number is ascribed to the strong interaction between AlF 3 and FSI – anions, as revealed through 19 F NMR. The enhancement in wetting and performance is general, being demonstrated with ester- and ether-based solvents, with K-, Na-, or Li- salts, and with different commercial separators. In full batteries, AlF 3 prevents Fe crossover and cycling-induced cathode pulverization.

NMB↗
DOE OSTI2021

A Sodium–Antimony–Telluride Intermetallic Allows Sodium-Metal Cycling at 100% Depth of Discharge and as an Anode-Free Metal Battery

In this work, repeated cold rolling and folding is employed to fabricate a metallurgical composite of sodium–antimony–telluride Na 2 (Sb 2/6 Te 3/6 Vac 1/6 ) dispersed in electrochemically active sodium metal, termed “NST-Na.” This new intermetallic has a vacancy-rich thermodynamically stable face-centered-cubic structure and enables state-of-the-art electrochemical performance in widely employed carbonate and ether electrolytes. NST-Na achieves 100% depth-of-discharge (DOD) in 1 m NaPF 6 in G2, with 15 mAh cm –2 at 1 mA cm –2 and Coulombic efficiency (CE) of 99.4%, for 1000 h of plating/stripping. Sodium-metal batteries (SMBs) with NST-Na and Na 3 V 2 (PO 4 ) 3 (NVP) or sulfur cathodes give significantly improved energy, cycling, and CE (>99%). An anode-free battery with NST collector and NVP obtains 0.23% capacity decay per cycle. Imaging and tomography using conventional and cryogenic microscopy (Cryo-EM) indicate that the sodium metal fills the open space inside the self-supporting sodiophilic NST skeleton, resulting in dense (pore-free and solid electrolyte interphase (SEI)-free) metal deposits with flat surfaces. The baseline Na deposit consists of filament-like dendrites and “dead metal”, intermixed with pores and SEI. Density functional theory calculations show that the uniqueness of NST lies in the thermodynamic stability of the Na atoms (rather than clusters) on its surface that leads to planar wetting, and in its own stability that prevents decomposition during cycling.

36 MATERIALS SCIENCE↗
DOE OSTI2021

In–Depth Analysis of the Degradation Mechanisms of High–Nickel, Low/No–Cobalt Layered Oxide Cathodes for Lithium–Ion Batteries

A rational compositional design of high-nickel, cobalt-free layered oxide materials for high-energy and low-cost lithium-ion batteries would be expected to further propel the widespread adoption of electric vehicles (EVs), yet a composition with satisfactory electrochemical properties has yet to emerge. The previous work has demonstrated a promising LiNi 0.883 Mn 0.056 Al 0.061 O 2 (NMA-89) composition that outperformed high-nickel, cobalt-containing analogs in cycling stability and maintained a comparable rate performance and thermal stability. Herein, the capacity fading mechanism of NMA-89 in a pouch full cell with a 4.2 V cutoff is compared to that of its cobalt-containing analogs. The results reveal that particle cracking in LiNi 0.89 Mn 0.055 Co 0.055 O 2 (NMC-89) and LiNi 0.883 Co 0.053 Al 0.064 O 2 (NCA-89) leads to a loss of active material and an increase in surface area, thereby exacerbating structural and surface instabilities, accelerating impedance and polarization growth, and ultimately reducing their capacity retentions. LiNi 0.89 Mn 0.044 Co 0.042 Al 0.013 Mg 0.011 O 2 (NMCAM-89) and NMA-89 experience subdued surface reactions and maintain spherical particle structures, both of which are conducive to their capacity retentions during long-term cycling. Furthermore, this investigation offers insights into how specific transition-metal ions dictate the electrochemical stability of high-Ni layered oxide cathode materials, highlights the benefit of Mn-Al combination in NMA-89, and presents potential strategies to further enhance the performance of this novel class of cathode materials.

degradation mechanisms↗