Mechanism of Lithium Ion Exchange Into Spinel Manganese Oxide
Lithium manganese oxide (LMO) is an effective absorbent for lithium recovery from brines, characterized by its high adsorption capacity, excellent regeneration performance, and selectivity. Here, this study investigates the mechanisms of material degradation during lithium loading and unloading in LMO, employing a combination of time‐resolved Raman spectroscopy, X‐ray diffraction, and X‐ray photoelectron spectroscopy. Key findings reveal that the A 1g vibrational mode wavenumber shifts from 635 cm −1 at the onset of lithium ion exchange to 656 cm −1 after 12 min, indicating local symmetry loss and manganese (Mn) loss during lithium intercalation. The proposed lithium exchange mechanism involves initial occupation of tetrahedral interstitial voids, followed by migration into interstitial sites between Mn octahedral sites. Computational modeling suggests that the loss of symmetry in MnO cubane‐like groups occurs as lithium migrates, significantly affecting the Raman spectra. Importantly, the study demonstrates that after 100 cycles of lithium/hydrogen loading, a 24% loss in Mn is observed, which correlates with decreased structural stability; however, the structural integrity of LMO is enhanced when subjected to multiple cycles without complete loading. Here, these insights contribute to the understanding of LMO's performance in lithium recovery applications and highlight potential strategies to optimize its use in future technologies.