DOE OSTI2022

Suppressing Chemical Corrosions of Lithium Metal Anodes

In this study, the lithium metal anode is essential for next-generation high-energy-density rechargeable Li-metal batteries. Although extensive studies have been performed to prolong the cycle life of Li-metal batteries, the calendar life, which associates with the chemical corrosion of Li metal in liquid electrolytes, has not been quantitatively understood. Here, by combing the titration gas chromatography method and cryogenic focused ion beam, a quantitative relationship between the chemical corrosion rate and electrochemically deposited Li morphology in various liquid electrolyte systems is established. It has been identified that the corrosion rate is dominated by the porosity of the deposited Li. The larger the porosity of deposited Li has, the faster the corrosion rate will be. Strategies to mitigate the chemical corrosion on Li thus to extend the calendar life of Li-metal batteries are further proposed. By strictly controlling the stacking pressure during Li plating, Li deposits with ultra-low porosity can be achieved, suppressing the corrosion rate to 0.08 ± 0.16%/day compared with 1.71 ± 0.19%/day of the high-porosity Li.

25 ENERGY STORAGE↗
DOE OSTI2021

Pressure-tailored lithium deposition and dissolution in lithium metal batteries

Unregulated lithium (Li) growth is the major cause of low Coulombic efficiency, short cycle life and safety hazards for rechargeable Li metal batteries. Strategies that aim to achieve large granular Li deposits have been extensively explored, and yet it remains a challenge to achieve the ideal Li deposits, which consist of large Li particles that are seamlessly packed on the electrode and can be reversibly deposited and stripped. In this work, we report a dense Li deposition (99.49% electrode density) with an ideal columnar structure that is achieved by controlling the uniaxial stack pressure during battery operation. Using multiscale characterization and simulation, we elucidate the critical role of stack pressure on Li nucleation, growth and dissolution processes and propose a Li-reservoir-testing protocol to maintain the ideal Li morphology during extended cycling. The precise manipulation of Li deposition and dissolution is a critical step to enable fast charging and a low-temperature operation for Li metal batteries.

25 ENERGY STORAGE↗
DOE OSTI2019

Quantifying inactive lithium in lithium metal batteries

Lithium metal anodes offer high theoretical capacities (3,860 milliampere-hours per gram)1, but rechargeable batteries built with such anodes suffer from dendrite growth and low Coulombic efficiency (the ratio of charge output to charge input), preventing their commercial adoption. The formation of inactive (‘dead’) lithium— which consists of both (electro)chemically formed Li + compounds in the solid electrolyte interphase and electrically isolated unreacted metallic Li 0 —causes capacity loss and safety hazards. Quantitatively distinguishing between Li + in components of the solid electrolyte interphase and unreacted metallic Li 0 has not been possible, owing to the lack of effective diagnostic tools. Optical microscopy, in situ environmental transmission electron microscopy, X-ray microtomography and magnetic resonance imaging provide a morphological perspective with little chemical information. Nuclear magnetic resonance, X-ray photoelectron spectroscopy and cryogenic transmission electron microscopy can distinguish between Li + in the solid electrolyte interphase and metallic Li 0 , but their detection ranges are limited to surfaces or local regions. Here we establish the analytical method of titration gas chromatography to quantify the contribution of unreacted metallic Li 0 to the total amount of inactive lithium. We identify the unreacted metallic Li 0 , not the (electro)chemically formed Li + in the solid electrolyte interphase, as the dominant source of inactive lithium and capacity loss. By coupling the unreacted metallic Li 0 content to observations of its local microstructure and nanostructure by cryogenic electron microscopy (both scanning and transmission), we also establish the formation mechanism of inactive lithium in different types of electrolytes and determine the underlying cause of low Coulombic efficiency in plating and stripping (the charge and discharge processes, respectively, in a full cell) of lithium metal anodes. Here we propose strategies for making lithium plating and stripping more efficient so that lithium metal anodes can be used for next-generation high-energy batteries.

25 ENERGY STORAGE↗