3 records

DOE OSTI2022

The impact of infill percentage and layer height in small-scale material extrusion on porosity and tensile properties

We report material extrusion additive manufacturing is prone to introducing porosity within the structure due to the layer-by-layer construction using elliptical beads of material. This open porosity ultimately plays a role in determining the mechanical properties of printed parts. The shape, size, and amount of porosity within a printed part is influenced by a variety of factors, including nozzle diameter, infill percentage, layer height, raster orientation, and print speed. While several studies have investigated these and other parameters’ effects on mechanical performance and porosity, better understanding the interconnected relationships is crucial in balancing the various input parameters to achieve maximum strength. This work initially examined the influence of key print parameters (infill percentage and layer height) on the internal porosity of a printed Acrylonitrile Butadiene Styrene (ABS) part. Then, the print parameters and internal porosity were statistically correlated to final mechanical properties. Porosity was further classified as either open or closed to differentiate between connected voids in the mesostructure from isolated voids within the material itself. Mechanical performance increased with an increasing density and infill percentage, displaying a 224 % increase in elastic modulus and a 150 % increase in ultimate tensile strength. The contribution of layer height was found to be conditional upon the infill percentage.

3D Printing↗

DOE OSTI2020

Characterizing material transitions in large-scale Additive Manufacturing

Integrating Multiple Materials (MM) into large-scale Additive Manufacturing (AM) is a key for various industrial applications wishing to incorporate site-specific properties into geometrically complex designs that are difficult to manufacture with traditional techniques. Printing with multiple materials is typically accomplished by using layers as natural material boundaries, but having the capability to switch between materials within a single layer without pausing would further expand MM possibilities. This study used Cincinnati Incorporated’s Big Area Additive Manufacturing (BAAM) system to explore material transitions with a novel dual-hopper that enables in-situ material blending of a pelletized feedstock. Constructing MM and functionally graded material (FGM) structures requires depositing a specific material composition at a specific geometric location to achieve a desired performance. Furthermore, accurately implementing this with the BAAM’s blended extrusion system requires a thorough understanding of the transition between distinct material compositions. This study characterizes a step-change transition between neat acrylonitrile butadiene styrene (ABS) and carbon fiber-reinforced ABS. Three distinct techniques were compared for analyzing the fiber content, and the transition zone between materials was characterized as a function of transition direction. The transition process was consistent to within 0.7 wt% carbon fiber variation between different layers and prints. The transition between materials was found to be directionally dependent, with ABS to CF/ABS having a transition length of 3.5 m compared to 3.2 m for CF/ABS to ABS. Furthermore, the transition from Material A to Material B was found to be repeatable with a possible variance in transition length of 0.3 m.

36 MATERIALS SCIENCE↗

DOE OSTI2020

The Influence of Processing Parameters on the Transition Zone for Blended Material 3D Printing

The use of Multiple Materials (MM) in Additive Manufacturing (AM) is increasingly important for expanding the range of applications in the manufacturing industry, particularly for large-format processes. Typically, polymer-based AM incorporates MM transitions through discrete interfaces between layers. This arrangement significantly increases the occurrence of layer delamination failures due to decreased bonding between dissimilar polymers. Elimination of discrete material interfaces by continuously transitioning from Material A to B provides a possible solution. Such continuous gradients could be used to create functionally graded structures that take full advantage of AM’s capability to deliberately impart site-specific properties. Cincinnati’s Big Area Additive Manufacturing (BAAM) system at Oak Ridge National Lab has been equipped with a dual-hopper system that enables in-situ material switching specifically intended for functionally graded and MM printing. The resulting material transition exhibits varied behavior based on printing conditions, which can have an impact on part design and resulting mechanical properties. In this work, the transition zone is characterized as a function of the printing screw speed (related to volumetric flow) and the screw geometry.