Improving the toughness of refractory compounds

Composition and processing studies were conducted on silicon nitride and silicon carbide materials. Charpy mode impact testing to 2415 F established the effectiveness of higher purity silicon nitride powder sources in reducing the scatter of measurements and in improving short time bend strengths as well as bend stress rupture properties. Stabilized zirconia additions in particular were observed to dramatically enhance low and high temperature bend strengths and stress rupture properties for all grades of silicon nitride powder. Silicon carbide samples showed relatively poor impact resistance, although the maxima in stress rupture behavior was exhibited by this material.

Vasilos, T.↗
NASA NTRS1974

High temperature compounds for turbine vanes

Fabrication and microstructure control studies were conducted on SiC, Si3N and composites based on Si3N. Charpy mode impact testing to 2400 F established that Si3N4/Mo composites have excellent potential. Attempts to fabricate composites of Si3N4 with superalloys, both by hot pressing and infiltration were largely unsuccessful in comparison to using Mo, Re, and Ta which are less reactive. Modest improvements in impact strength were realized for monolithic Si3N4; however, SiC strengths increased by a factor of six and now equal values achieved for Si3N4. Correlations of impact strength with material properties are discussed. Reduced MgO densification aid additions to Si3N4 were found to decrease densification kinetics, increase final porosity, decrease room temperature bend strength, increase high temperature bend strength, and decrease bend stress rupture properties. The decrease in bend strength at high temperature for fine grain size SiC suggested that a slightly larger grain size material with a nearly constant strength-temperature relation may prove desirable in the creep and stress rupture mode.

Rhodes, W. H.↗
NASA NTRS1972

High temperature compounds for turbine vanes

Fabrication and microstructure control studies were conducted on SiC, Si3N4, and composites based on these compounds. Charpy mode impact testing to 2400 F established that beta-spodumene, lithium aluminum silicate, coated Si3N4, Si3N4 derived from alpha-Si3N4 powder, and SiC containing 5-25 v/o chopped C fibers had the most promising strengths. Several other composite systems had excellent microstructures and could prove interesting materials in the future. Stress-rupture testing on Si3N4 established that increasing 2000 F - 100 hour strengths were obtained for increasing grain size to at least 5 micrometers, increasing density and possibly increasing phase purity. These parameters became less important at 2400 F where it is thought a grain boundary phase controls strength.