Options, Initial Design Requirements, Estimated Costs, Reactor Commitments, and Potential Uses of a Graphite Leadout Type Experiment Supporting Various Commercial HTR Vendors

Multiple commercial High Temperature Reactor (HTR) vendors and nuclear graphite suppliers would benefit by collaborating on a new irradiation capsule(s) that would include graphite grades not included within the AGC Experiment. This new irradiation capsule(s) would provide data to answer vendor graphite licensing issues. Rather than spending money (and especially) time in designing separate irradiation capsules for each designer, the capsule(s) would be used for multiple graphite and composite designs to maximize efficiency and promote multiple HTR designs. However, the primary motivation for assisting vendors with this new irradiation capsule(s) is lack of availability in the existing Material Test Reactors (MTRs). Cost reduction is a secondary goal. A common, collaborative, capsule design can be achieved for graphite and composites due to the similarity of different grades. Irradiation, disassembly, shipping, and PIE costs would be cost-shared by all users. It is anticipated that interest would extend across all DOE campaigns (micro-Rx, SMR, GCR, MSR, etc.) due to the similar requirements for all graphite grades.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Volume 6: Experiment Facility Spectrum Tailoring (HFIR Futures – Enhanced Capabilities Series)

In-core irradiation experiment research, such as materials and fuels irradiation research and radioisotope production, is one of the primary missions of Oak Ridge National Laboratory’s (ORNL) versatile High Flux Isotope Reactor (HFIR). In support of the HFIR-Sustaining and Enhancing Neutron Science (SENSe) Initiative, a technically diverse group of ORNL irradiation research subject matter experts formed the Spectrum Tailoring Working Group, with the goal of developing a compendium of experiment facility concepts to enhance irradiation experiment conditions via neutron spectrum tailoring capabilities. The purpose of this report is to document the concepts developed in FY22 and the associated scientific justifications, identify potential facility sponsors, and estimate costs and schedules for each concept. This report documents the efforts performed in FY22, which may continue in FY23 or later pending the direction of the HFIR-SENSe Initiative and the interested sponsors.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2022

Equibiaxial Flexure Strength of a Superfine-Grained Nuclear Graphite

The strength of advanced graphite is reported in accordance with ASTM D7846-16 using a two-parameter Weibull distribution for uniaxial strength testing. The rule of thumb for Weibull distributions is to use a minimum of 30 strength measurements to have a high level of confidence in the Weibull characteristic strength and the Weibull modulus. These large sample sets for statistical confidence are easily obtained for as-manufactured graphite, but determination of the Weibull two-factor parameters on graphite that has been exposed to neutron irradiation is nearly impossible due to irradiation testing restraints on specimen size and space limitations in test reactors for the accommodation of specimens. These restrictions have resulted in irradiation programs that use sub-sized specimens to measure uniaxial strength change, but the specimen geometries still hinder the number of replicate specimens for each irradiation condition. In contrast, this work used an advanced ceramic standard, ASTM C1499-05, as the foundation for equibiaxial strength testing of a superfine-grained nuclear graphite to investigate the irradiation-induced strength change and any changes to the two-parameter Weibull distribution. The goal was to investigate the effect of specimen size on the two-parameter Weibull distribution parameters in support of the small specimens and geometry desired for irradiation. A study of the effect of a reduced sample population was also undertaken to investigate the reliability of using the two-parameter Weibull distribution to study changes to the materials properties caused by neutron irradiation damage. The results of this work suggest that these equibiaxial specimens would be ideal for statistically significant studies of the effects of irradiation on the Weibull characteristic strength (but not the modulus) and for providing a method for surveillance specimen campaigns for future operating commercial reactors.

Campbell, Anne↗
DOE OSTI2022

Texture analysis of AGR program matrix materials

We report the fuel form for high-temperature gas-cooled reactors consists of tristructural isotropic (TRISO) particles embedded in a matrix of graphite flake and carbonized resin. The process of overcoating particles prior to compacting yields a circumferential orientation of the graphite flake surrounding the TRISO particles, which is modified to varied extents when overcoated particles are pressed into the final fuel form. As graphite is highly anisotropic, the texture may impact the properties and performance of the fuel. Ellipsometry was used to measure the texture of the matrix for fueled compacts and unfueled “matrix-only” samples. Results indicated local texture related to the spherical particles in compacts associated with overcoating versus a more linear layered structure in “matrix-only” samples.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗