NASA NTRS2002

Effect of Environment on the Stress- Rupture Behavior of a C/SiC Composite Studied

Advanced reusable launch vehicles will likely incorporate fiber-reinforced ceramic matrix composites (CMC's) in critical propulsion and airframe components. The use of CMC's is highly desirable to save weight, improve reuse capability, and increase performance. One of the candidate CMC materials is carbon-fiber-reinforced silicon carbide (C/SiC). In potential propulsion applications, such as turbopump rotors and nozzle exit ramps, C/SiC components will be subjected to a service cycle that includes mechanical loading under complex, high-pressure environments containing hydrogen, oxygen, and steam. Degradation of both the C fibers and the SiC matrix are possible in these environments. The objective of this effort was to evaluate the mechanical behavior of C/SiC in various environments relevant to reusable launch vehicle applications. Stress-rupture testing was conducted at the NASA Glenn Research Center on C/SiC specimens in air and steam-containing environments. Also, the oxidation kinetics of the carbon fibers that reinforce the composite were monitored by thermogravimetric analysis in the same environments and temperatures used for the stress-rupture tests of the C/SiC composite specimens. The stress-rupture lives obtained for C/SiC tested in air and in steam/argon mixtures are shown in the following bar chart. As is typical for most materials, lives obtained at the lower temperature (600 C) are longer than for the higher temperature (1200 C). The effect of environment was most pronounced at the lower temperature, where the average test duration in steam at 600 C was at least 30 times longer than the lives obtained in air. The 1200 C data revealed little difference between the lives of specimens tested in air and steam at atmospheric pressure.

Verrilli, Michael J.↗

NASA NTRS2002

C-Coupon Studies of SiC/SiC Composites: Microstructual Characterization - Part 2

A 'C-coupon' was used to measure the interlaminar tensile behavior of five different composite materials: Sylramic/MI (melt infiltration SiC matrix), ZMl/MI, Sylramic/S300, and ZMI and Hi-Nicalon with an S200 matrix at room temperature, 816 C, and 1204 C. Fracture behavior was characterized by field emission scanning electron microscopy, and observed cracking compared with events measured by modal acoustic emission. Both radial and matrix hoop cracking along the inner radius arising from hoop stresses were observed for all material types. In those composites in which the radial cracks were sufficiently wide to view the composite interior, fracture was observed to occur at the fiber BN or BN matrix interface.

Hurwitz, Frances I.↗

NASA NTRS2002

C-Coupon Studies of SiC/SiC Composites: Acoustic Emission Monitoring - Part 1

Modal acoustic emission (AE) was used to monitor the acoustic activity during room temperature and elevated temperature c-coupon tests for a variety of SiC/SiC systems including composites containing Sylramic (trademark), ZMI (trademark), or Hi-Nicalon (trademark) fibers with melt-infiltrated or polymer-infiltrated SiC matrices. Modal AE proved excellent at monitoring matrix cracking in the curved portion of the C-coupon specimen with increasing load. This included the load at which the first AE event occurred and the location of AE events during the test that were, presumably, caused by the formation and growth of interlaminar cracks and, at higher loads, transverse cracks. Graphical techniques were employed to estimate the load for first AE. It was determined that for this test with these material systems, the first AE could be estimated within the load range bounded by the load at which initial deviation from linearity of the load-displacement curve occurs and the load where the 98% offset of the linear regression fit intercepted the load-displacement curve. The calculation of interlaminar tensile (ILT) stress from the load for first AE was determined for all the systems. Ultimate ILT strength usually corresponded to ILT stress determined from the ultimate load to failure of the C-coupon test, which was considerably higher than the first cracking stress.

Morscher, Gregory N.↗

NASA NTRS2002

High Temperature Tensile Properties and Fatigue Behavior of a Melt-Infiltrated SiC/SiC Composite

High temperature fatigue behavior of a woven, SiC/SiC ceramic matrix composite (CMC) was investigated in air at two temperatures. The reinforcement for the CMC consisted of 5HS Sylramic(Trademark) fabric with a [0deg/90deg]4s lay-up. The SiC matrix material was infiltrated into the fiber-preform with a slurry-cast, melt-infiltration process. Tensile and fatigue test specimens were machined from the CMC plates. Initially tensile tests were conducted to obtain the average values of tensile properties at 1038 and 1204 C. Subsequently, low-cycle fatigue (LCF) tests with zero and two-hour hold-times at the maximum stress were conducted at the same two temperatures. Fatigue life data generated in the LCF tests were used to determine the geometric mean fatigue lives. In this paper, the tensile behavior and the fatigue durability of the CMC determined under different loading conditions are documented. In addition, reductions observed in the cyclic lives of the composite due to the two hour hold-time at maximum tensile stress are discussed.

Kalluri, Sreeramesh↗

NASA NTRS2001

C-Coupon Studies of CMCS: Fracture Behavior and Microstructural Characterization

A curved beam 'C-coupon' was used to assess fracture behavior in a Sylramic(tm)/melt infiltration (MI) SiC matrix composite. Failure stresses and fracture mechanisms, as determined by optical and scanning electron microstructural analysis, are compared with finite element stress calculations to analyze failure modes. Material microstructure was found to have a strong influence on mechanical behavior. Fracture occurs in interlaminar tension (ILT), provided that the ratio of ILT to tensile strength for the material is less than the ratio of radial to hoop stresses for the C-coupon geometry. Utilization of 3D architectures to improve interlaminar strength requires significant development efforts to incorporate through thickness fibers in regions with high curvatures while maintaining uniform thickness, radius, and microstructure.

Hurwitz, Frances I.↗

NASA NTRS2000

Ceramic Matrix Composites (CMC) Life Prediction Method Development

Advanced launch systems (e.g., Reusable Launch Vehicle and other Shuttle Class concepts, Rocket-Based Combine Cycle, etc.), and interplanetary vehicles will very likely incorporate fiber reinforced ceramic matrix composites (CMC) in critical propulsion components. The use of CMC is highly desirable to save weight, to improve reuse capability, and to increase performance. CMC candidate applications are mission and cycle dependent and may include turbopump rotors, housings, combustors, nozzle injectors, exit cones or ramps, and throats. For reusable and single mission uses, accurate prediction of life is critical to mission success. The tools to accomplish life prediction are very immature and not oriented toward the behavior of carbon fiber reinforced silicon carbide (C/SiC), the primary system of interest for a variety of space propulsion applications. This paper describes an approach to satisfy the need to develop an integrated life prediction system for CMC that addresses mechanical durability due to cyclic and steady thermomechanical loads, and takes into account the impact of environmental degradation.

Levine, Stanley R.↗

NASA NTRS1999

Mechanical Behavior of a Hi-Nicalon(tm)/SiC Composite Having a Polycarbosilane Derived Matrix

Polymer infiltration of a rigidized preform, followed by pyrolysis to convert the polymer to a ceramic, potentially offers a lower cost alternative to CVD. It also offers more moderate temperature requirements than melt infiltration approaches, which should minimize potential fiber damage during processing. However, polymer infiltration and pyrolysis results in a more microcracked matrix. Preliminary mechanical property characterization, including elevated temperature (1204 C) tensile, 500 h stress rupture behavior and low cycle fatigue, was conducted on Hi-Nicalon (TM)/Si-C-(O) composites having a dual layer BN/SiC interface and a matrix derived by impregnation and pyrolysis of allylhydridopolycarbosilane (AHPCS). Microstructural evaluation of failure surfaces and of polished transverse and longitudinal cross sections of the failed specimens was used to identify predominant failure mechanisms. In stress rupture testing at 1093 C, the failure was interface dominated, while at 1204 C in both stress rupture and two hour hold/fatigue tests failure was matrix dominated, resulting in specimen delamination.

Hurwitz, Frances I.↗

NASA NTRS1994

The Role of Crack Formation in Chevron-Notched Four-Point Bend Specimens

The failure sequence following crack formation in a chevron-notched four-point bend 1 specimen is examined in a parametric study using the Bluhm slice synthesis model. Premature failure resulting from crack formation forces which exceed those required to propagate a crack beyond alpha (min) is examined together with the critical crack length and critical crack front length. An energy based approach is used to establish factors which forecast the tendency of such premature failure due to crack formation for any selected chevron-notched geometry. A comparative study reveals that, for constant values of alpha (1) and alpha (0), the dimensionless beam compliance and stress intensity factor are essentially independent of specimen width and thickness. The chevron tip position, alpha (0) has its primary effect on the force required to initiate a sharp crack. Small values for alpha (0) maximize the stable region length, however, the premature failure tendency is also high for smaller alpha (0) values. Improvements in premature failure resistance can be realized for larger values of alpha (0) with only a minor reduction in the stable region length. The stable region length is also maximized for larger chevron based positions, alpha (1) but the chance for premature failure is also raised. Smaller base positions improve the premature failure resistance with only minor decreases in the stable region length. Chevron geometries having a good balance of premature failure resistance, stable region length, and crack front length are 0.20 less than or equal to alpha (0) is less than or equal to 0.30 and 0.70 is less than or equal to alpha (1) is less than or equal to 0.80.

Calomino, Anthony M.↗

NASA NTRS1993

Controlled-Crack-Growth Testing Of Brittle Materials

Simple design for fixture and specimen significantly improves crack-growth fracture testing of ceramics and other brittle materials. Makes it possible to impose crack-mouth-opening displacement that remains at or close to prescribed value even when crack extends. Important secondary advantages: geometry of specimen is simple, making specimen easy to machine; fit between pin and specimen provides self-aligning grip; contact stresses and probability of failure at or near loading spot reduced.

Calomino, Anthony M.↗

NASA NTRS1993

Analytical stress intensity solution for the Stable Poisson Loaded specimen

An analytical calibration of the Stable Poisson Loaded (SPL) specimen is presented. The specimen configuration is similar to the ASTM E-561 compact-tension specimen with displacement controlled wedge loading used for R-curve determination. The crack mouth opening displacements (CMODs) are produced by the diametral expansion of an axially compressed cylindrical pin located in the wake of a machined notch. Due to the unusual loading configuration, a three-dimensional finite element analysis was performed with gap elements simulating the contact between the pin and specimen. In this report, stress intensity factors, CMODs, and crack displacement profiles, are reported for different crack lengths and different contacting conditions. It was concluded that the computed stress intensity factor decreases sharply with increasing crack length thus making the SPL specimen configuration attractive for fracture testing of brittle, high modulus materials.

Ghosn, Louis J.↗

NASA NTRS1992

Numerical calibration of the stable poisson loaded specimen

An analytical calibration of the Stable Poisson Loaded (SPL) specimen is presented. The specimen configuration is similar to the ASTM E-561 compact-tension specimen with displacement controlled wedge loading used for R-Curve determination. The crack mouth opening displacements (CMOD's) are produced by the diametral expansion of an axially compressed cylindrical pin located in the wake of a machined notch. Due to the unusual loading configuration, a three-dimensional finite element analysis was performed with gap elements simulating the contact between the pin and specimen. In this report, stress intensity factors, CMOD's, and crack displacement profiles are reported for different crack lengths and different contacting conditions. It was concluded that the computed stress intensity factor decreases sharply with increasing crack length, thus making the SPL specimen configuration attractive for fracture testing of brittle, high modulus materials.

Ghosn, Louis J.↗

NASA NTRS1992

Controlled crack growth specimen for brittle systems

A pure Mode 1 fracture specimen and test procedure has been developed which provides extended, stable, through-thickness crack growth in ceramics and other brittle, nonmetallic materials. Fixed displacement loading, applied at the crack mouth, promotes stable crack extension by reducing the stored elastic strain energy. Extremely fine control of applied displacements is achieved by utilizing the Poisson's expansion of a compressively loaded cylindrical pin. Stable cracks were successfully grown in soda-lime glass and monolithic Al2O3 for lengths in excess of 2O mm without uncontrollable catastrophic failure.

Calomino, Anthony M.↗

NASA NTRS1991

Fully articulated four-point-bend loading fixture

A fully articulated four-point bend loading fixture for Modulus of Rupture (MOR) and fracture toughness specimens utilizes an upper loading plate in combination with a lower loading plate. The lower plate has a pair of spring loaded ball bearings which seat in V-shaped grooves located in the upper plate. The ball bearings are carried in the arms of the lower plate. A load is applied to the specimen through steel rollers, one large roller and one smaller roller each located on both the upper and lower plates. The large rollers have needle roller bearings which enable a single loading roller to rotate relative to the plate to which it is attached.

Calomino, Anthony M.↗

NASA NTRS1990

Controlled crack growth specimen for brittle systems

Calomino, Anthony M.↗

NASA NTRS1990

Ceramic Matrix Composites (CMC) Life Prediction Development

Advanced launch systems will very likely incorporate fiber reinforced ceramic matrix composites (CMC) in critical propulsion and airframe components. The use of CMC will save weight, increase operating margin, safety and performance, and improve reuse capability. For reusable and single mission use, accurate life prediction is critical to success. The tools to accomplish this are immature and not oriented toward the behavior of carbon fiber reinforced silicon carbide (C/SiC), the primary system of interest for many applications. This paper describes an approach and progress made to satisfy the need to develop an integrated life prediction system that addresses mechanical durability and environmental degradation.

Levine, Stanley R.↗