Calderoni, Pattrick

Publications and source records attributed to Calderoni, Pattrick.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Sensor Qualification for the Development of Advanced Reactors

A temperature sensor qualification device is undergoing development and testing in order to qualify temperature sensors for advanced reactor metrology applications. This device will provide National Institute of Standards and Technology (NIST) traceable performance testing of temperature sensors while under the high radiation environments experienced while in-core. This is completed by utilizing retractable sensors which transfer the measurements from ex-core to in-core sensors. A detailed discussion of the uncertainty propagation associated with this comparative process is provided. Experimental testing of the temperature distribution occurring in the device has begun and is reported on. It is pertinent to minimize this temperature distribution to prevent variation in sensor measurements. This variation will be indistinguishable from sensor drift for in-pile applications and would result in unnecessarily conservative uncertainty bounds.

46 - INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AN↗
DOE OSTI2024

Methods for making high-temperature thermocouples

Methods of manufacturing thermocouples having a first thermoelement wire comprises a molybdenum-lanthanum based material and a second thermoelement wire comprises a phosphorus-doped niobium, may involve exposing a first thermoelement wire and a second thermoelement wire to a temperature in a range extending from about 50° C. to about 60° C. above an intended operational temperature of the first and second thermoelement wires and until a rate of change of a normalized voltage output of the first thermoelement wire and the second thermoelement wire is about 0.001 normalized Volts per hour or less.

Skifton, Richard S.↗
DOE OSTI2024

INSTRUMENTATION FOR IN-CORE REAL-TIME MECHANICAL TESTING OF STRUCTURAL MATERIALS (INCREASE) PROJECT

Idaho National Laboratory (INL), in collaboration with the Electric Power Research Institute (EPRI), Nuclear Regulatory Commission, French Atomic and Alternative Energies Commission (CEA), Joint Research Centre, Nuclear Research and Consultancy Group, and Research Center Rez, is the operating agent of the In-Core Real-Time Mechanical Testing of Structural Materials (INCREASE) joint experimental program (JEEP) project that operates within the Nuclear Energy Agency (NEA)’s Framework for Irradiation Experiments (FIDES-II) program. The first objective of the INCREASE project is to design a shared capsule that can house a variety of in-core mechanical testing instrumentation for enabling smart irradiation experiments. The second objective is to collect in core stress relaxation data pertaining to high priority stainless steel (SS) materials under light water reactor conditions with target temperature of 340°C +/-20°C and a minimum neutron damage of 2 displacement per atom (dpa). The INCREASE project will be demonstrated in the Massachusetts Institute of Technology Nuclear Research Reactor (MITR).

36 MATERIALS SCIENCE↗
DOE OSTI2022

Assessment of thermodynamic stability of sapphire in eutectic molten chloride environment

The continued development of molten salt reactors requires highly efficient and stable instruments that can efficiently track monitor conditions of the molten salt during long-term application operation in both the fuel and coolant/heat transfer fluid loops. Sapphire (Al 2 O 3 ) fibers have shown tremendous potential by enabling radiation resistance and a broader operational range of temperature . Thermodynamic modeling using the ThermoCalc and the SGTE Molten Salts (SALT1) and Pure Substances (Pure5) database is done performed to understand the compatibility of Al 2 O 3 fibers with NaCl-MgCl 2 eutectic molten salt in the temperature range of 600 to 1000°C. The thermodynamic calculations show that sapphire fibers are not expected to be compatible with long term exposure to molten chloride salts within this temperature range. Furthermore, various pure metallic elements were evaluated as potential cladding materials for part of the Al 2 O 3 fibers. Based on the thermodynamic analysis, molybdenum (Mo) and nickel (Ni) could be effective cladding materials to enhance the stability of Al 2 O 3 in NaCl and MgCl 2 chloride salt molten bath in the desired temperature range. The presence of a metallic cladding leads to the suppression of aluminum dissolution from Al 2 O 3 , thus improving its stability in chloride salts. Additionally, it is also shown that Al 2 O 3 remains stable up to 2300 K in the presence of pre-existing Al 2 MgO 4 and Al 2 NiO 4 in the eutectic molten chloride bath environment.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2021

Out-of-Pile Test of LVDT-Based Creep Test Rig at PWR Prototypical Conditions

New and improved materials are being considered to support the existing nuclear reactors and future next-generation reactors. The materials can significantly degrade and limit their properties in harsh reactor environments. To accurately understand the material’s degradation, real-time data is required under prototypic-irradiation conditions. Additionally, understanding the creep behavior of materials under harsh environments is essential for an evaluation of safety concerns. To provide these capabilities, the Idaho National Laboratory’s (INL’s) High Temperature Test Laboratory (HTTL) has developed several instrumented test rigs to obtain real-time data from specimens in well-controlled pressurized water reactor (PWR) coolant conditions in the Materials and Test Reactors (MTRs). This technical report focuses on INL’s efforts to evaluate and enhance the former prototype creep test rig that relied on linear variable differential transformers in laboratory settings. Specifically, the test rig is capable of detecting changes in the length of tensile specimen, which is useful for measuring thermal expansion and creep loading.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2020

Active Irradiation Testing of Temperature Sensing Capability of Clad Sapphire Optical Fibers with Type 2 Bragg Gratings using Optical Backscatter Reflectometry

This work investigated the temperature-sensing capabilities of Type II fiber Bragg gratings (FBGs) inscribed in sapphire optical fiber in the Ohio State University Research Reactor (OSURR). A Luna Innovations 4600 optical backscatter reflectometer (OBR) was used to interrogate FBGs in three sapphire optical fibers with an internal cladding that was developed by Ohio State. The sapphire fibers were fusion-spliced to silica lead fibers. In addition to the sapphire fibers, two silica fibers with the same Type II FBGs were included in the experiment as a reference. The fiber-based sensors were irradiated in the Central Irradiation Facility (CIF) of the OSURR for a total of 40 hours over 5 days at a reactor power of 450 kW, resulting in a total neutron fluence of approximately 2.5 × 10 18 n/cm 2 and a gamma dose of approximately 3.48 Grad. Two K-type thermocouples were included within the rig: one at the core centerline and the other 12 inches above the top of the core. The temperature was not actively controlled, but the thermocouples were used to provide a reference to which the fiber-based temperature measurements could be compared.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Evaluation of Low Dose Silicon Carbide Temperature Monitors

Thermocouples are generally used to provide real-time temperature indications in instrumented tests performed at materials and test reactors. Melt wires or paint spots are often included in such tests as an independent technique of detecting peak temperatures incurred during irradiation. In addition, less expensive static capsule tests, which have no leads attached for real-time data transmission, often rely on melt wires and paint spots as a post-irradiation technique for peak temperature indication. Unfortunately, these techniques are limited in that they can only detect whether a single temperature is or is not exceeded. Silicon carbide (SiC) monitors are advantageous because a single monitor can be used to determine the peak temperature reached within a relatively broad range (200 – 800°C). Although the use of SiC monitors was proposed more than five decades ago, the ultimate performance limits of this technique are not fully understood. The Nuclear Science User Facilities (NSUF) is the United States Department of Energy Office of Nuclear Energy's only designated nuclear energy user facility. Its mission is to provide nuclear energy researchers access to world-class capabilities and to facilitate the advancement of nuclear science and technology. This mission is supported by providing access to state-of-the-art experimental irradiation testing, post irradiation examination facilities, and high performance computing capabilities as well as technical and scientific assistance for the design and execution of projects. As part of an NSUF project, low dose silicon carbide monitors were irradiated in the Belgian Reactor 2 and were then evaluated both at the SCK•CEN and at Idaho National Laboratory's High Temperature Test Laboratory to determine their peak temperature achieved during irradiation. The technical significance of this work was that the monitors were irradiated to a dose that was significantly less than recommended in published literature. This paper will discuss the evaluation process, the irradiation test, and the performance of the low dose silicon carbide temperature monitors.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Advanced Sensors and Instrumentation (ASI) Program Plan. Nuclear Energy Enabling Technologies (NEET)

The U.S. Department of Energy Office of Nuclear Energy (DOE-NE) sponsors a crosscutting technology development (CTD) program addressing common instrumentation & controls (I&C) needs in all DOE-NE sponsored programs. In 2012, DOE-NE initiated the Nuclear Energy Enabling Technology (NEET) Program to conduct research, development, and demonstration (RD&D) in crosscutting technologies that directly support and enable the development of existing, new and advanced reactor designs, and fuel cycle technologies. These technologies will advance the state of nuclear technology, improve its competitiveness, and promote continued contribution to meeting our Nation’s energy and environmental challenges. The NEET Program has spurred innovation in the field of sensors and instrumentation, advanced methods for manufacturing, and cyber security. The Advanced Sensors and Instrumentation (ASI) program is one element of the NEET CTD that has spurred innovation in the measurement science field by funding research on sensors, instrumentation and controls, communication, and advanced analytics that measure system parameters, gauge component control input, and provide power plant owners and operators critical awareness so they can plan and safely manage operational evolutions. The NEET ASI Program has carried out research and development (R&D) required to develop and deploy innovative and advanced sensors, and instrumentation and control capabilities for current and future nuclear energy systems, and to enable the advanced technologies essential to NE’s R&D efforts needed to realize mission goals. The concept of technology readiness assessment is helpful for the classification of instrumentation technology as part of the program strategy. A technology readiness assessment evaluates technology maturity using the Technology Readiness Level (TRL) scale and was pioneered by the National Aeronautics and Space Administration in the 1980s for space technology. It has recently been adopted to advance fuels and materials. The NEET ASI program objective is to mature instruments technology to TRL 6, which is “demonstration of the technology in relevant environment.” While there may be instances in which a different strategy is justified, the aim of the program is to respond to DOE program and stakeholder needs for nuclear instrumentation then hand off the technology after demonstration for integration in a more complex system, for example an irradiation test, experimental loop or a plant component such as the core, primary system or heat exchanger. A mechanism to continue some level of support from NEET ASI during and after the adoption (for example, to maintain fabrication and calibration capabilities) will be defined as the first example of technology hand off comes to fruition. In addition, several paths exist within DOE to complement NEET ASI activities to extend the maturity beyond TRL, for example through GAIN, technology commercialization funding, and small-business programs. Role of NEET ASI CINR projects in the TRL space, and integration with direct funded demonstration.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2019

An impedance-based diameter gauge for in-pile fuel deformation measurements

During irradiation, the fuel-cladding interface of a nuclear fuel rod can experience significant mechanical and chemical interaction. In-situ measurement of the radial deformation of the cladding can quantify the extent of this interaction and the state of the cladding. Existing capabilities to perform in-pile diameter measurements are limited by required contact and an intrusive presence of a device near to a specimen. To overcome these limitations, researchers have developed and evaluated an electrical impedance based diameter gauge using a benchtop system. The sensor consists of an electrically conductive concentric ring around the fuel cladding such that the electrical impedance between the ring and cladding is measured. Additionally, the cladding diameter is determined through a measurement of the electrical impedance between the electrodes with a known ring electrode diameter. Analytic and 3-D finite element analyses (FEA) were used to quantify the measurement sensitivity, uncertainty, and off-design conditions. The experimental sensor measured diameters with <20 µm of error, and had a measurement resolution of <1 µm for diameters ranging from 9.5 to 9.6 mm. Lastly, the uncertainty analysis for the experimental setup estimated an uncertainty of 20 µm, consistent with the experimentally measured results.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2019

Innovative sensing technologies for nuclear instrumentation

The Idaho National Laboratory (INL) is engaged in research and development activities for the development of nuclear instrumentation that contribute to advances in measurement methodologies, measurement systems, instrumentation, and sensors in the area of nuclear engineering. The activities described in this paper are centered on the INL Measurement Science Department, which was formed in 2018. Their mission is to develop instrumentation that provides real time, accurate, spatially resolved information regarding test conditions and the performance of fuels and materials during irradiation. This paper describes the integration of innovative optical fiber, acoustic and electrical impedance sensing technologies and measurement techniques as part of the activities.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2019

Evaluation of a Versatile Experimental Salt Irradiation Loop (VESIL) inside the Advanced Test Reactor

A Versatile Experimental Salt Irradiation Loop (VESIL) is under investigation at Idaho National Laboratory. An initial feasibility study was conducted for potential deployment inside the Advanced Test Reactor (ATR). Historical salt-irradiation tests are reviewed and summarized in this report. The study also surveys available instrumentation for this type of application and identifies key design and testing requirements. Neutronic analysis was performed in different ATR position for various salt candidates using MCNP6 and ORIGEN-6.2. The results indicate that both the B and I-positions are suitable for VESIL. The B-position allows for accelerated testing in light of its higher flux, but its smaller volume may be detrimental for a flowing loop. The O-position flux level was found to be insufficient for the purposes of this experiment; it is not recommended. In all the different salt candidates investigated, both the B and I-positions are found to able to reach adequate burnup conditions that are representative of the operating conditions inside proposed molten-salt reactor concepts.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2019

Summary of High Temperature Irradiation Resistant Thermocouple Standarization Tests

Over the preceding ten years, continual research and development has been performed on the high temperature irradiation resistant thermocouple (HTIR-TC) by the team at Idaho National Laboratories (INL) High Temperature Test Laboratory (HTTL). The HTIR-TC has the capability of achieving high temperatures up to 1600°C or more. Further, the HTIR-TC has gone through many longevity tests both in and out of pile to show the amount of drift is minimal compared standard thermocouples. Key considerations for properties and materials of the HTIR-TC have been final diameter, ductility after heat treatment, and minimizing transmutation of materials during operation. Further, heat treatment and calibration processes have been established in order to consistently produce repeatable and reliable temperature readings. The current work provides further background for the standardization process of the HTIR-TC.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2018

In-Pile Instrumentation Initiative –Focused Sensor Development for Test Reactors

The In-Pile Instrumentation Initiative (I3) is a recently established program that focuses on the in-core instrumentation needs of test reactors and advanced technology reactors. The goal is to deploy high-quality instrumentation to support irradiation experiments today and, in parallel, develop and deploy the next generation of in-pile instrumentation to support advanced reactor technologies.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗