NASA NTRS1999

Waterproof Silicone Coatings of Thermal Insulation and Vaporization Method

Thermal insulation composed of porous ceramic material can be waterproofed by producing a thin silicone film on the surface of the insulation by exposing it to volatile silicone precursors at ambient conditions. When the silicone precursor reactants are multi-functional siloxanes or silanes containing alkenes or alkynes carbon groups higher molecular weight films can be produced. Catalyst are usually required for the silicone precursors to react at room temperature to form the films. The catalyst are particularly useful in the single component system e.g. dimethylethoxysilane (DNMS) to accelerate the reaction and decrease the time to waterproof and protect the insulation. In comparison to other methods, the chemical vapor technique assures better control over the quantity and location of the film being deposited on the ceramic insulation to improve the waterproof coating.

Cagliostro, Domenick E.↗

NASA NTRS1998

Method for Waterproofing Ceramic Materials

Hygroscopic ceramic materials which are difficult to waterproof with a silane, substituted silane or silazane waterproofing agent, such as an alumina containing fibrous, flexible and porous, fibrous ceramic insulation used on a reentry space vehicle, are rendered easy to waterproof if the interior porous surface of the ceramic is first coated with a thin coating of silica. The silica coating is achieved by coating the interior surface of the ceramic with a silica precursor converting the precursor to silica either in-situ or by oxidative pyrolysis and then applying the waterproofing agent to the silica coated ceramic. The silica precursor comprises almost any suitable silicon containing material such as a silane, silicone, siloxane, silazane and the like applied by solution, vapor deposition and the like. If the waterproofing is removed by e.g., burning, the silica remains and the ceramic is easily rewaterproofed. An alumina containing TABI insulation which absorbs more that five times its weight of water, absorbs less than 10 wt. % water after being waterproofed according to the method of the invention.

Cagliostro, Domenick E.↗

NASA NTRS1998

Organopolysiloxane Waterproofing Treatment for Porous Ceramics

Rigid and flexible porous ceramics, including thermal insulation of a type used on space vehicles, are waterproofed by a treatment which comprises applying an aqueous solution of an organopolysiloxane water-proofing agent having reactive silanol groups to the surface of the ceramic and then heating the treated ceramic to form a waterproofed ceramic. The organopolysiloxane is formed by the hydrolysis and partial condensation of di- and trialkoxyfunctional alkylalkoxysilanes having 1-10 carbon atom hydrocarbyl groups.

Leiser, Daniel B.↗

NASA NTRS1993

Model for the formation of silicon carbide from the pyrolysis of dichlorodimethylsilane in hydrogen. I - Silicon formation from chlorosilanes. II - Silicon carbide formation from silicon and methane

In the first part of this work, a model is developed for the deposition of silicon from the reduction of silicon tetrachloride with hydrogen in a tubular reactor at 700-1100 C, at atmospheric pressure. The model is based on gas chromatography of the volatile products of the reaction, followed by gravimetric analysis of total Si deposition on the tube. In the second part of this work, a model is developed for the case of SiC deposition from the pyrolysis of dichlorodimethylsilane in hydrogen under the same reactor conditions. The rate constants derived from a nonlinear regression analysis are reported.

Cagliostro, Domenick E.↗

NASA NTRS1990

Analysis of the pyrolysis products of dimethyldichlorosilane in the chemical vapor deposition of silicon carbide in argon

A study of the products and reactions occurring during the chemical vapor deposition of silicon carbide from dimethyldichlorosilane in argon is presented. Reaction conditions were as follows: 700 to 1100 C, a contact time of about 1 min, and a pressure of 1 atm. At these conditions, the gases that formed were mainly methane, hydrogen, silicon tetrachloride, trichlorosilane, and methyltrichlorosilane. The silicon carbide solid that formed showed the presence of hydrogen and chloride as impurities, which might degrade the silicon carbide properties. These impurities were eliminated slowly, even at 1100 C, forming hydrogen, trichlorosilane, and silicon tetrachloride.

Cagliostro, Domenick E.↗

NASA NTRS1989

Ceramic Honeycomb Structures and Method Thereof

The present invention relates to a method for producing ceramic articles and the articles, the process comprising the chemical vapor deposition (CVD) and/or chemical vapor infiltration (CVI) of a honeycomb structure. Specifically the present invention relates to a method for the production of a ceramic honeycomb structure, including: (a) obtaining a loosely woven fabric/binder wherein the fabric consists essentially of metallic, ceramic or organic fiber and the binder consists essentially of an organic or inorganic material wherein the fabric/binder has and retains a honeycomb shape, with the proviso that when the fabric is metallic or ceramic the binder is organic only; (b) substantially evenly depositing at least one layer of a ceramic on the fabric/binder of step (a); and (c) recovering the ceramic coated fiber honeycomb structure. In another aspect, the present invention relates to a method for the manufacture of a lightweight ceramic-ceramic composite honeycomb structure, which process comprises: (d) pyrolyzing a loosely woven fabric a honeycomb shaped and having a high char yield and geometric integrity after pyrolysis at between about 700 degrees and 1,100 degrees Centigrade; (e) substantially evenly depositing at least one layer of ceramic material on the pyrolyzed fabric of step (a); and (f) recovering the coated ceramic honeycomb structure. The ceramic articles produced have enhanced physical properties and are useful in aircraft and aerospace uses.

Cagliostro, Domenick E.↗

NASA NTRS1989

Ceramic Honeycomb Panels

Ceramic honeycomb panels serve as lightweight, heat-resistant structural members. Depending on choice of ceramic materials, panels expected to withstand temperatures as high as 1,800 degree C. Honeycomb structure made by vapor-depositing ceramic on fabric substrate woven in honeycomb pattern, then eliminating substrate by oxidizing it. Fabric made of loosely woven polymer such as polyacrylonitrile. Impregnated with organic binder such as phenolic resin for stiffness.

Cagliostro, Domenick E.↗

NASA NTRS1987

Ceramic honeycomb structures and the method thereof

The subject invention pertains to a method of producing an improved composite-composite honeycomb structure for aircraft or aerospace use. Specifically, the subject invention relates to a method for the production of a lightweight ceramic-ceramic composite honeycomb structure, which method comprises: (1) pyrolyzing a loosely woven fabric/binder having a honeycomb shape and having a high char yield and geometric integrity after pyrolysis at between about 700 and 1,100 C; (2) substantially evenly depositing at least one layer of ceramic material on the pyrolyzed fabric/binder of step (1); (3) recovering the coated ceramic honeycomb structure; (4) removing the pyrolyzed fabric/binder of the structure of step (3) by slow pyrolysis at between 700 and 1000 C in between about a 2 to 5% by volume oxygen atmosphere for between about 0.5 and 5 hr.; and (5) substantially evenly depositing on and within the rigid hollow honeycomb structure at least one additional layer of the same or a different ceramic material by chemical vapor deposition and chemical vapor infiltration. The honeycomb shaped ceramic articles have enhanced physical properties and are useful in aircraft and aerospace uses.

Riccitiello, Salvatore R.↗